Leakage associated with intermediate restorative material and glass-ionomer cement retrograde fillings: a human and sheep teeth comparison with 2 different aging procedures

In-vitro evaluation of microleakage of bioceramic root-end filling materials: A spectrophotometric study

Aim

To evaluate the microleakage of newer bioceramic root-end filling materials.

Material and method

Sixty freshly extracted human single-rooted mandibular premolar teeth were selected for the study. Teeth with fractured root, cracks, anddilacerations were rejected. All teeth were cleaned with ultrasonic scalers. Standard access opening was done and root canal treatment was performed with rotary files followed by obturation. After storing in saline for a week apical 3 ​mm of the root was resected at 900 angles to the long axis of the root. Retro cavity preparation was done with ultrasonic tips. The teeth were divided into four groups of 15 specimens each. Group I - Biodentin, GroupII-Bioaggregate, Group III - MTA Plus, and Group IV - MTA. After the restoration of retro cavities of all the teeth as per manufacture instructions, two coats of nail varnish were applied to leave apical 3 ​mm. All teeth were stored in 2% methylene blue for 72 ​h followed by emersion in 65% nitric acid for the next 72 ​h for Dye extraction. The obtained supernatant solution was then centrifuged and optical density or absorbance was measured with a UV spectrophotometer.

Result

Microleakage was found to be increasing in this order: Biodentin ​< ​Bioaggregate ​< ​MTA Plus ​< ​MTA. No significant difference was found in the microleakage of Biodentin compared to that of Bioaggregate(p ​> ​0.01).

Conclusion

All materials exhibit some amount of microleakage. Biodentin shows the least microleakage among all the bioceramic material groups. Hence, Biodentin and bioaggregate are better material of choice for the retrograde filling to prevent microleakage.

Microleakage evaluation around retrograde filling materials prepared using conventional and ultrasonic techniques

INTRODUCTION

The importance of the retrograde cavity preparation and the material used to restore is of utmost importance to achieve successful surgical endodontics.

AIM

The aim of the present study is to evaluate the apical micro-leakage of root end cavities filled with Mineral trioxide aggregate, Biodentine and light cure GIC using two different cavity preparation techniques that is conventional bur preparation and ultrasonic tip preparation.

MATERIALS AND METHODS

Eighty extracted single rooted human teeth (except mandibular incisors) with one canal, fully developed apices and without any major carious lesion are collected for the study. The teeth were sectioned at CEJ to standardize the length. Roots are instrumented upto master apical file 40 K size and obturated with gutta percha and AH plus sealer in lateral condensation technique. The teeth were then resected apically at 90° angle axis to the long axis of the root removing 3 mm of the apex. The teeth were divided in to four groups of 20 each- • Group I- samples restored with MTA. • Group II- samples restored with Biodentine. • Group III- (Positive control group)- samples restored with Light activated GIC. • Group IV - (negative control group)- no filling material. Each group is divided into two subgroups (a, b) of ten teeth each 1. Retropreparation done with ultrasonic retrotip. 2. Retropreparation done with conventional bur. The teeth were then immersed in 0.5% Rhodamine B dye for 48 h. The teeth were split longitudinally and the interface between the restored material and the canal wall is observed under Confocal laser scanning microscope. Depth of dye penetration was examined under stereomicroscope.

RESULTS

The statistical analysis was performed by One way ANOVA, t test. Pair wise comparision was done by Newman - Keuls multiple post hoc test. The mean values of Dye penetration for Group Ia (321.23), Group Ib (490.11), Group IIa (1065.14), Group IIb (1170.96), Group IIIa (1888.90), Group IIIb (2025.35). The samples prepared with ultrasonic retrotip showed less microleakage but it is statistically not significant.

CONCLUSION

MTA showed significantly less microleakage when compared to Biodentine and light cure GIC and there is no statistical difference between the ultrasonic retrotip preparation and conventional bur preparation.

Sealing ability of castor oil polymer as a root-end filling material

OBJECTIVE

The purpose of this study was to evaluate the sealing ability of castor oil polymer (COP), mineral trioxide aggregate (MTA) and glass ionomer cement (GIC) as root-end filling materials. Forty-five single-rooted human teeth were cleaned and prepared using a step-back technique. The apical third of each root was resected perpendicularly to the long axis direction. All teeth were obturated with gutta-percha and an endodontic sealer. After, a root-end cavity with 1.25-mm depth was prepared using a diamond bur. The specimens were randomly divided into three experimental groups (n=15), according to the root-end filling material used: G1) COP; G2) MTA; G3) GIC. The external surfaces of the specimens were covered with epoxy adhesive, except the root-end filling. The teeth were immersed in rhodamine B dye for 24 hours. Then, the roots were sectioned longitudinally and the linear dye penetration at the dentin/material interface was determined using a stereomicroscope. ANOVA and Tukey's tests were used to compare the three groups. The G1 group (COP) presented smaller dye penetration, statistically different than the G2 (MTA) and G3 (GIC) groups (p<0.05). No statistically significant difference in microleakage was observed between G2 and G3 groups (p>0.05). The results of this study indicate that the COP presented efficient sealing ability when used as a root-end filling material showing results significantly better than MTA and GIC.