The effectiveness of functionalized nano-hydroxyapatite filler on the physical and mechanical properties of novel dental restorative composite

Deep margin elevation in class II cavities: A comparative evaluation of microleakage and interface integrity using confocal laser microscopy and scanning electron microscopy

Aim

This study aims to evaluate the microleakage between the gingival seat and base material and to assess the interface integrity between the base material and overlying composite in class II cavities restored using deep margin elevation.

Materials and Methods

Thirty maxillary molars (n = 30) were taken, and class II cavities were prepared with a gingival seat extending below the cementoenamel junction. These teeth were divided into three groups for subgingival margin elevation using different materials: Group A (n = 10) - flowable composite, Group B (n = 10) - glass ionomer cement (GIC), and Group C (n = 10) - GIC with nanohydroxyapatite (GIC n-HAp). The remaining cavities were restored with bulk-fill composite. After undergoing 1000 thermocycling cycles, half of the samples were examined for microleakage using confocal laser microscopy, and the other half were assessed for interface integrity using scanning electron microscopy. Microleakage was statistically analyzed by one-way ANOVA, and interface integrity was analyzed by Kruskal-Wallis tests.

Results

The study found that GIC n-HAp exhibited significantly lower microleakage between the base material and gingival seat than flowable composite and GIC. However, regarding interface integrity between the base material and bulk-fill composite, flowable composite, and GIC outperformed GIC n-HAp.

Conclusions

Incorporating n-HAp into GIC effectively reduced microleakage at the dentin-base material interface. However, the interface integrity between GIC n-HAp and the composite poses a challenge.

Characterization of PLA/PCL/Nano-Hydroxyapatite (nHA) Biocomposites Prepared via Cold Isostatic Pressing

Hydroxyapatite has the closest chemical composition to human bone. Despite this, the use of nano-hydroxyapatite (nHA) to produce biocomposite scaffolds from a mixture of polylactic acid (PLA) and polycaprolactone (PCL) using cold isostatic pressing has not been studied intensively. In this study, biocomposites were created employing nHA as an osteoconductive filler and a polymeric blend of PLA and PCL as a polymer matrix for prospective usage in the medical field. Cold isostatic pressing and subsequent sintering were used to create composites with different nHA concentrations that ranged from 0 to 30 weight percent. Using physical and mechanical characterization techniques such as Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and density, porosity, tensile, and flexural standard tests, it was determined how the nHA concentrations affected the biocomposite's general properties. In this study, the presence of PLA, PCL, and nHA was well identified using FTIR, XRD, and SEM methods. The biocomposites with high nHA content showed intense bands for symmetric stretching and the asymmetric bending vibration of PO₄^3-. The incorporation of nHA into the polymeric blend matrix resulted in a rather irregular structure and the crystallization became more difficult. The addition of nHA improved the density and tensile and flexural strength of the PLA/PCL matrix (0% nHA). However, with increasing nHA content, the PLA/PCL/nHA biocomposites became more porous. In addition, the density, flexural strength, and tensile strength of the PLA/PCL/nHA biocomposites decreased with increasing nHA concentration. The PLA/PCL/nHA biocomposites with 10% nHA had the highest mechanical properties with a density of 1.39 g/cm³, a porosity of 1.93%, a flexural strength of 55.35 MPa, and a tensile strength of 30.68 MPa.

Functionalized calcium orthophosphates (CaPO4) and their biomedical applications

Due to the chemical similarity to natural calcified tissues (bones and teeth) of mammals, calcium orthophosphates (abbreviated as CaPO4) appear to be good biomaterials for creation of artificial bone grafts. However, CaPO4 alone have some restrictions, which limit their biomedical applications. Various ways have been developed to improve the properties of CaPO4 and their functionalization is one of them. Namely, since surfaces always form the interfaces between implanted grafts and surrounding tissues, the state of CaPO4 surfaces plays a crucial role in the survival of bone grafts. Although the biomedically relevant CaPO4 possess the required biocompatible properties, some of their properties could be better. For example, functionalization of CaPO4 to enhance cell attachment and cell material interactions has been developed. In addition, to prepare stable formulations from nanodimensional CaPO4 particles and prevent them from agglomerating, the surfaces of CaPO4 particles are often functionalized by sorption of special chemicals. Furthermore, there are functionalizations in which CaPO4 are exposed to various types of physical treatments. This review summarizes the available knowledge on CaPO4 functionalizations and their biomedical applications.