Influence of α-Tocopherol Load and Annealing Treatment on the Wear Resistance of Biomedical UHMWPE Irradiated with Electron Beam

Wear Assessment of Tibial Inserts Made of Highly Cross-Linked Polyethylene Supplemented with Dodecyl Gallate in the Total Knee Arthroplasty

Background: the wear of tibial insert is still one of primary factors leading to failure of total knee arthroplasty (TKA). Dodecyl gallate (DG) has shown improvements in the oxidation stability of highly cross-linked polyethylene (HXLPE). This study aimed to assess the application of HXLPE supplemented with DG (HXLPE-DG) on the tibial insert in TKA concerning the wear resistance and the potential impact on implant fixation; Methods: tibial inserts made of HXLPE-DG were subjected to a 3 million loading-cycle wear test following ISO 14243-1:2009. The loss of mass and wear rate of the tibial inserts were calculated. The quantity, size,- and shape of wear particles were recorded; Results: the test specimens lost an average mass of 16.00 mg ± 0.94 mg, and were on an average wear rate of 3.92 mg/million cycles ± 0.19 mg/million cycles. The content of wear particles in the calf serum medium was 3.94 × 10⁸ particles/mL ± 3.93 × 10⁷ particles/mL, 96.66% ± 0.77% of the particles had an equivalent circular diameter less than 0.5 μm. The aspect ratio of wear particles was 1.40 (min: 1.01; max: 6.42). Conclusions: HXLPE-DG displayed advantages over the commonly used materials for tibial inserts and presented the potential of application in TKA.

Wear Resistant Nanocomposites Based on Biomedical Grade UHMWPE Paraffin Oil and Carbon Nano-Filler: Preliminary Biocompatibility and Antibacterial Activity Investigation

In the present paper, we investigate the effectiveness of nanocomposites (composed of ultra-high molecular weight polyethylene (UHMWPE) mixed with carbon nano-filler (CNF) and medical grade paraffin oil (PO), from the biological point of view. Wear measurements were carried out without (air) and with lubricant (distilled water, natural, and artificial lubricant), and antibacterial activity and cytotoxicity were evaluated. The results highlighted that the presence of CNF is important in the nanocomposite formulation because it reduces the wear rate and prevents oxidative degradation during its processing. An amount of 1.0 wt % of CNF is best because it reaches the optimal distribution within the polymeric matrix, resulting in the best wear resistant, bio-active, and anti-bacterial nanocomposite among all investigated samples.

Wear behaviour of UHMWPE reinforced by carbon nanofiller and paraffin oil for joint replacement

The majority of artificial joints incorporate biomedical grade Ultra High Molecular Weight Poly Ethylene (UHMWPE), whose wear is considered most important in controlling service time of the whole joint. The aim of this work was to improve wear resistance of UHMWPE through the addition of 0.5-2.0wt% of Carbon Nano Filler (CNF) and 2% wt of Paraffin Oil (PO) using ball milling (BM) and extrusion techniques (EX). The wear tests on these nanocomposites were conducted by a pin on disc in dry (air) and wet media (simulated synovial fluid or artificial lubricant, and bovine synovial fluid or natural lubricant). Mechanical tests (tensile and hardness), physical analysis (calorimetric, density, wet ability, roughness) and morphological observations were also performed. The experimental results showed that natural lubricant provides the greatest reduction in wear rate while the largest one occurred in air. Furthermore, the BM mixed nanocomposites with a filler load of 1.0% exhibited the best wear resistance among all the samples with an improvement of 42%, 64% and 83% in air, artificial and natural lubricant, respectively. This is due to its higher ductility and thermal features, and lower wet ability in the two lubricants.