Exploring the functional properties of PVP/PVA blend incorporated with non-stoichiometric SnS for optoelectronic devices

Impact of Mn-Ni spinal ferrite nanoparticles on the structural, morphological, surface roughness, and optical parameters of polyvinyl alcohol for optoelectronic applications

Herein, polyvinyl alcohol (PVA) acts as a host matrix for manganese-nickel ferrite (Mn0.4Ni0.6Fe2O4) nanoparticles (NPs). Oxalate precursors and a solution-cast method were used to produce a Mn0.4Ni0.6Fe2O4 spinel structure and PVA-Mn0.4Ni0.6Fe2O4 films, respectively. X-ray diffraction (XRD), scanning electron microscopy, optical microscopy (OM), a surface roughness tester, and FT-IR spectroscopy were used to identify the structure and morphology of the PVA-Mn0.4Ni0.6Fe2O4 films. XRD confirmed the formation of Mn0.4Ni0.6Fe2O4 spinel, and its additive into the PVA matrix causes an increase in the PVA amorphousity. The PVA-Mn0.4Ni0.6Fe2O4 film's transmission and absorption spectra were recorded with the help of a UV-visible spectrophotometer. The addition of 4%Mn0.4Ni0.6Fe2O4 to PVA resulted in a decrease in the optical bandgap from 5.53 eV to 4.83 eV. The Urbach energy increases from 0.46 eV for pure PVA to 2.14 eV for PVA-4%Mn0.4Ni0.6Fe2O4, indicating a rise in the defect density. In addition, the refractive index and extinction coefficient were calculated theoretically and were found to increase as the Mn0.4Ni0.6Fe2O4 content increases in the PVA matrix.

Modification of the Structure and Linear/Nonlinear Optical Characteristics of PVA/Chitosan Blend through CuO Doping for Eco-Friendly Applications

The solution casting technique is utilized to fabricate blank and CuO-doped polyvinyl alcohol/chitosan (PVA/CS) blends for eco-friendly applications. The structure and surface morphologies of prepared samples were explored by Fourier transform infrared (FT-IR) spectrophotometry and scanning electron microscopy (SEM), respectively. FT-IR analysis reveals the incorporation of CuO particles within the PVA/CS structure. SEM analysis exposes the well-dispersion of CuO particles in the host medium. The linear/nonlinear optical characteristics were found on the basis of UV-visible-NIR measurements. The transmittance of the PVA/CS decreases upon CuO increasing to 20.0 wt%. The optical bandgap (E_{g dir.}/E_{g ind.}) decreases from 5.38/4.67 eV (blank PVA/CS) to 3.72/3.12 eV (20.0 wt% CuO-PVA/CS). An obvious improvement in the optical constants of the PVA/CS blend is achieved by CuO doping. The Wemple-DiDomenico (WDD) and Sellmeier oscillator models were utilized to examine the CuO role dispersion behavior of the PVA/CS blend. The optical analysis shows clear enrichment of the optical parameters of the PVA/CS host. The novel findings in the current study nominate CuO-doped PVA/CS films for applications in linear/nonlinear optical devices.