Electronically- and crystal-structure-driven magnetic structures and physical properties of RScSb (R = rare earth) compounds: a neutron diffraction, magnetization and heat capacity study

Hydrogen Insertion in the Intermetallic GdScGe: A Drastic Reduction of the Dimensionality of the Magnetic and Transport Properties

Intermetallic phases have been investigated with respect to their ability to accept small atoms in interstitial sites without changing the host structure. Among those, the intermetallic compounds crystallizing in the tetragonal CeScSi-type structure are able to absorb hydrogen atoms. These compounds are of particular interest because they can show electride-like character and, therefore, can be exploited as new catalysts. Here we report the case of GdScGe which uptakes hydrogen at 623 K and under a H₂ gas pressure between 0.5 and 4 MPa. The formation of the hydride GdScGeH, with H atoms entering into the [Gd₄] tetrahedra, preserves the host structure but induces an anisotropic volume expansion with a strong increase of the c-parameter and a slight decrease of the a-parameter. Interestingly, we show for the first time for this family of materials that hydrogen insertion reduces the dimensionality of the magnetic and transport properties from 3D to quasi-2D which results in a vanishing of the ferromagnetic order ( T_C = 350 K for GdScGe) and a change of the metallic conduction behavior to a nonmetallic one. As evidenced by density functional theory calculations, such drastic effects are accounted for through the Gd-H chemical bonding effect and the oxidizing effect of H whereas the volume expansion plays only a minor role.

Crystal, magnetic, calorimetric and electronic structure investigation of GdScGe1-x Sb x compounds

Experimental investigations of crystal structure, magnetism and heat capacity of compounds in the pseudoternary GdScGe-GdScSb system combined with density functional theory projections have been employed to clarify the interplay between the crystal structure and magnetism in this series of RTX materials (R  =  rare-earth, [Formula: see text]  =  transition metal and X  =  p-block element). We demonstrate that the CeScSi-type structure adopted by GdScGe and CeFeSi-type structure adopted by GdScSb coexist over a limited range of compositions [Formula: see text]. Antimony for Ge substitutions in GdScGe result in an anisotropic expansion of the unit cell of the parent that is most pronounced along the c axis. We believe that such expansion acts as the driving force for the instability of the double layer CeScSi-type structure of the parent germanide. Extensive, yet limited Sb substitutions [Formula: see text] lead to a strong reduction of the Curie temperature compared to the GdScGe parent, but without affecting the saturation magnetization. With a further increase in Sb content, the first compositions showing the presence of the CeFeSi-type structure of the antimonide, [Formula: see text], coincide with the appearance of an antiferromagnetic phase. The application of a finite magnetic field reveals a jump in magnetization toward a fully saturated ferromagnetic state. This antiferro-ferromagnetic transformation is not associated with a sizeable latent heat, as confirmed by heat capacity measurements. The electronic structure calculations for [Formula: see text] indicate that the key factor in the conversion from the ferromagnetic CeScSi-type to the antiferromagnetic CeFeSi-type structure is the disappearance of the induced magnetic moments on Sc. For the parent antimonide, heat capacity measurements indicate an additional transition below the main antiferromagnetic transition.

Tetragonal to triclinic structural transition in the prototypical CeScSi induced by a two-step magnetic ordering: a temperature-dependent neutron diffraction study of CeScSi, CeScGe and LaScSi

An investigation on the ground state magnetism of CeScSi, CeScGe (tetragonal CeScSi-type, tI12, space group I4/mmm) by temperature-dependent powder neutron diffraction has been carried out, as debated and controversial data regarding the low temperature magnetic behaviours of these two compounds were reported. Our studies reveal that, while cooling, long-range magnetic ordering in CeScSi and CeScGe takes place by a two-step process. A first transition leads to a magnetic structure with the Ce moments aligned ferromagnetically onto two neighbouring tetragonal basal a-b planes of the CeScSi-type structure; the double layers are then antiferromagnetically coupled to each other along the c-axis. The transition temperature associated with the first ordering is T _N ~ 26 K and T _N ~ 48 K for the silicide and the germanide, respectively. Here the spin directions are rigorously confined to the basal plane, with values of the Ce magnetic moments of μ _Ce  =  0.8-1.0 μ _B. A second magnetic transition, which takes place at slightly lower temperatures, results in a canting of the ordered magnetic moments out of the basal plane which is accompanied by an increase of the magnetic moment value of Ce to μ _Ce  =  1.4-1.5 μ _B. Interestingly, the second magnetic transition leads to a structural distortion in both compounds from the higher-symmetry tetragonal space group I4/mmm to the lower-symmetry and triclinic I-1 (non-standard triclinic). Magnetic symmetry analysis shows that the canted structure would not be allowed in the I4/mmm space group; this result further confirms the structural transition. The transition temperatures T _S from I4/mmm to I-1 are about 22 K in CeScSi and 36 K in CeScGe, i.e. well below the temperature of the first onset of antiferromagnetic order observed in this work (or below the ordering temperature, previously reported as either T _C or T _N). This result, along with the synchronism of the magnetic and structural transitions, suggests a magnetostructural origin of this structural distortion. We have also carried out powder neutron diffraction for LaScSi as a non-magnetically-ordering reference compound and compared the results with those of CeScSi and CeScGe compounds.

Cerium intermetallics CeTX – review III

The structure–property relationships of CeTX intermetallics with structures other than the ZrNiAl and TiNiSi type are systematically reviewed. These CeTX phases form with electron-poor and electron-rich transition metals (T) and X = Mg, Zn, Cd, Hg, Al, Ga, In, Tl, Si, Ge, Sn, Pb, P, As, Sb, and Bi. The review focusses on the crystal chemistry, the chemical bonding peculiarities, and the magnetic and transport properties. Furthermore 119Sn Mössbauer spectroscopic data, high-pressure studies, hydrogenation reactions and the formation of solid solutions are reviewed. This paper is the third of a series of four reviews on equiatomic intermetallic cerium compounds [Part I: R. Pöttgen, B. Chevalier, Z. Naturforsch. 2015, 70b, 289; Part II: R. Pöttgen, B. Chevalier, Z. Naturforsch. 2015, 70b, 695].