High-pressure polymorphism of BaFe2Se3

Pressure-Induced Superconductivity in Iron-Based Spin-Ladder Compound BaFe2+δ(S1-xSex)3

The iron-based superconductors had a significant impact on condensed matter physics. They have a common structural motif of a two-dimensional square iron lattice and exhibit fruitful physical properties as a strongly correlated electron system. During the extensive investigations, quasi-one-dimensional iron-based spin-ladder compounds attracted much attention as a platform for studying the interplay between magnetic and orbital ordering. In these compounds, BaFe₂S₃ and BaFe₂Se₃ were found to exhibit superconductivity under high pressure, having a different crystal and magnetic structure at low temperature. We report a brief review of the iron-based spin-ladder compound and recent studies for BaFe_2+δ(S_1−xSe_x)₃. BaFe₂(S_0.75 Se_0.25)₃ is in the vicinity of the boundary of two different magnetic phases and it is intriguing to perform high pressure experiments for studying superconductivity, since effects of large magnetic fluctuations on superconductivity are expected. The effect of iron stoichiometry on the interplay between magnetism and superconductivity is also studied by changing the iron concentration in BaFe_2+δSe₃.

Structural, magnetic, and electronic evolution of the spin-ladder system BaFe2S3-x Se x with isoelectronic substitution

We report experimental studies of a series of BaFe2S3-x Se x (0 ⩽ x ⩽ 3) single crystals and powder specimens using x-ray diffraction, neutron-diffraction, muon-spin-relaxation, and electrical transport measurements. A structural transformation from Cmcm (BaFe2S3) to Pnma (BaFe2Se3) was identified around x = 0.7 - 1. Neutron-diffraction measurements on the samples with x = 0.2, 0.4, and 0.7 reveal that the Néel temperature of the stripe antiferromagnetic order is gradually suppressed from ~120 to 85 K, while the magnitude of the ordered Fe2+ moments shows very little variation. Similarly, the block antiferromagnetic order in BaFe2Se3 remains robust for 1.5 ⩽ x ⩽ 3 with negligible variation in the ordered moment and a slight decrease of the Néel temperature from 250 K (x = 3) to 225 K (x = 1.5). The sample with x = 1 near the Cmcm and Pnma border shows coexisting, two-dimensional, short-range stripe- and block-type antiferromagnetic correlations. The system remains insulating for all x, but the thermal activation gap shows an abrupt increase when traversing the boundary from the Cmcm stripe phase to the Pnma block phase. The results demonstrate that the crystal structure, magnetic order, and electronic properties are strongly coupled in the BaFe2S3-x Se x system.