Three-Dimensional Printing of Calcium Carbonate/Hydroxyapatite Scaffolds at Low Temperature for Bone Tissue Engineering

Determination of the Optimum Architecture of Additively Manufactured Magnetic Bioactive Glass Scaffolds for Bone Tissue Engineering and Drug-Delivery Applications

For better bone regeneration, precise control over the architecture of the scaffolds is necessary. Because the shape of the pore may affect the bone regeneration, therefore, additive manufacturing has been used in this study to fabricate magnetic bioactive glass (MBG) scaffolds with three different architectures, namely, grid, gyroid, and Schwarz D surface with 15 × 15 × 15 mm3 dimensions and 70% porosity. These scaffolds have been fabricated using an in-house-developed material-extrusion-based additive manufacturing system. The composition of bioactive glass was selected as 45% SiO2, 20% Na2O, 23% CaO, 6% P2O5, 2.5% B2O3, 1% ZnO, 2% MgO, and 0.5% CaF2 (wt %), and additionally 0.4 wt % of iron carbide nanoparticles were incorporated. Afterward, MBG powder was mixed with a 25% (w/v) Pluronic F-127 solution to prepare a slurry for fabricating scaffolds at 23% relative humidity. The morphological characterization using microcomputed tomography revealed the appropriate pore size distribution and interconnectivity of the scaffolds. The compressive strengths of the fabricated grid, gyroid, and Schwarz D scaffolds were found to be 14.01 ± 1.01, 10.78 ± 1.5, and 12.57 ± 1.2 MPa, respectively. The in vitro study was done by immersing the MBG scaffolds in simulated body fluid for 1, 3, 7, and 14 days. Darcy's law, which describes the flow through porous media, was used to evaluate the permeability of the scaffolds. Furthermore, an anticancer drug (Mitomycin C) was loaded onto these scaffolds, wherein these scaffolds depicted good release behavior. Overall, gyroid-structured scaffolds were found to be the most suitable among the three scaffolds considered in this study for bone tissue engineering and drug-delivery applications.

Additive Manufacturing of Iron Carbide Incorporated Bioactive Glass Scaffolds for Bone Tissue Engineering and Drug Delivery Applications

In this study, we have synthesized a bioactive glass with composition 45SiO2-20Na2O-23CaO-6P2O5-2.5B2O3-1ZnO-2MgO-0.5CaF2 (wt %). Further, it has been incorporated with 0.4 wt % iron carbide nanoparticles to prepare magnetic bioactive glass (MBG) with good heat generation capability for potential applications in magnetic field-assisted hyperthermia. The MBG scaffolds have been fabricated using extrusion-based additive manufacturing by mixing MBG powder with 25% Pluronic F-127 solution as the binder. The saturation magnetization of iron carbide nanoparticles in the bioactive glass matrix has been found to be 80 emu/g. The morphological analysis (pore size distribution, porosity, open pore network modeling, tortuosity, and pore interconnectivity) was done using an in-house developed methodology that revealed the suitability of the scaffolds for bone tissue engineering. The compressive strength (14.3 ± 1.6 MPa) of the MBG scaffold was within the range of trabecular bone. The in vitro test using simulated body fluid (SBF) showed the formation of apatite indicating the bioactive nature of scaffolds. Further, the drug delivery behaviors of uncoated and polycaprolactone (PCL) coated MBG scaffolds have been evaluated by loading an anticancer drug (Mitomycin C) onto the scaffolds. While the uncoated scaffold demonstrated the drug's burst release for the initial 80 h, the PCL-coated scaffold showed the gradual release of the drug. These results demonstrate the potential of the proposed MBG for bone tissue engineering and drug delivery applications.

3D printed PLGA/MgO/PDA composite scaffold by low-temperature deposition manufacturing for bone tissue engineering applications

Introduction

Bones are easily damaged. Biomimetic scaffolds are involved in tissue engineering. This study explored polydopamine (PDA)-coated poly lactic-co-glycolic acid (PLGA)-magnesium oxide (MgO) scaffold properties and its effects on bone marrow mesenchymal stem cells (BMSCs) osteogenic differentiation.

Methods

PLGA/MgO scaffolds were prepared by low-temperature 3D printing technology and PDA coatings were prepared by immersion method. Scaffold structure was observed by scanning electron microscopy with an energy dispersive spectrometer (SEM-EDS), fourier transform infrared spectrometer (FTIR). Scaffold hydrophilicity, compressive/elastic modulus, and degradation rates were analyzed by water contact angle measurement, mechanical tests, and simulated-body fluid immersion. Rat BMSCs were cultured in scaffold extract. Cell activity on days 1, 3, and 7 was detected by MTT. Cells were induced by osteogenic differentiation, followed by evaluation of alkaline phosphatase (ALP) activity on days 3, 7, and 14 of induction and Osteocalcin, Osteocalcin, and Collagen I expressions.

Results

The prepared PLGA/MgO scaffolds had dense microparticles. With the increase of MgO contents, the hydrophilicity was enhanced, scaffold degradation rate was accelerated, magnesium ion release rate and scaffold extract pH value were increased, and cytotoxicity was less when magnesium mass ratio was less than 10%. Compared with other scaffolds, compressive and elastic modulus of PLGA/MgO (10%) scaffolds were increased; BMSCs incubated with PLGA/MgO (10%) scaffold extract had higher ALP activity and Osteocalcin, Osteopontin, and Collagen I expressions. PDA coating was prepared in PLGA/MgO (10%) scaffolds and the mechanical properties were not affected. PLGA/MgO (10%)/PDA scaffolds had better hydrophilicity and biocompatibility and promoted BMSC osteogenic differentiation.

Conclusion

Low-temperature 3D printing PLGA/MgO (10%)/PDA scaffolds had good hydrophilicity and biocompatibility, and were conducive to BMSC osteogenic differentiation.

Design, Preparation, and Mechanical Property Study of Polylactic Acid/Ca2BO3Cl: Eu2+, Dy3+ Composite Material for 3D Printing

To break through the simplification of three-dimensional printing (3DP) materials and realize the application of long-persistent phosphors in more fields, polylactic acid doped with Ca2BO3Cl: Eu2+, Dy3+ was prepared in this study. The structure of the mixtures was analyzed and determined by infrared spectroscopy. The luminescence properties of phosphors and the composites were studied by fluorescence spectra and afterglow decay curve measurements. The yellow light of the mixtures could be attributed to the 5d-4f energy level transition of Eu2+. After the excitation of 254 nm ultraviolet lamp, the luminance and duration of the composites could be clearly observed. The mechanical properties of the composite filaments were tested, including maximal force and elasticity modulus. In particular, the influence of humidity on mechanical properties was analyzed in detail. The prepared composite filaments were printed into hollow dodecahedrons and presented in this study. Therefore, the composites had great properties and might be expected to put into practical applications of 3DP technology.

Inflammation Responses to Bone Scaffolds under Mechanical Stimuli in Bone Regeneration

Physical stimuli play an important role in one tissue engineering. Mechanical stimuli, such as ultrasound with cyclic loading, are widely used to promote bone osteogenesis; however, the inflammatory response under physical stimuli has not been well studied. In this paper, the signaling pathways related to inflammatory responses in bone tissue engineering are evaluated, and the application of physical stimulation to promote osteogenesis and its related mechanisms are reviewed in detail; in particular, how physical stimulation alleviates inflammatory responses during transplantation when employing a bone scaffolding strategy is discussed. It is concluded that physical stimulation (e.g., ultrasound and cyclic stress) helps to promote osteogenesis while reducing the inflammatory response. In addition, apart from 2D cell culture, more consideration should be given to the mechanical stimuli applied to 3D scaffolds and the effects of different force moduli while evaluating inflammatory responses. This will facilitate the application of physiotherapy in bone tissue engineering.