DEVELOPMENT OF NACL-BASED OPTICALLY STIMULATED LUMINESCENT PHOSPHORS FOR THE POSSIBLE APPLICATIONS IN DOSIMETRY

Dosimetric properties of thermoluminescent NaCl pellets from Khewra Salt Mines, Pakistan

Thermoluminescence (TL) and extended dosimetric characteristics of naturally occurring NaCl salt were studied. Pellets were prepared from mined crystalline salt obtained from Khewra salt mines, Pakistan and irradiated from 1 mGy to 10,000 mGy using Co-60 gamma source. The TL response showed two dominant peaks around 125 °C and 230 °C respectively at low doses, with an additional peak in between at doses beyond 300 mGy. A linear and supra-linear TL response was observed between 1 mGy-100 mGy and 100 mGy-10 Gy dose ranges respectively. During first 24 hours post irradiation, the TL intensity dropped by 20%. A maximum angular dependence of up to 50% was observed between 0 to 360°. For photon energies between 33 keV-1.25 MeV significant energy dependence was observed for photons <100 keV only. Sample sensitivity increased with dose a qualitatively similar behaviour to TLD-200. Zeff of the sample (14.6) was comparable to TLD-200 (16.3). No significant dose rate effects (deviation for a Co-60 source within 3.5%) on the TL sensitivity of the sample were found. The lowest detectable dose limit (LDDL) for salt sample was found to be 0.8 mGy whereas the sample reproducibility test showed a maximum of ±11% deviation from the first value.