Root dentinal microcracks - absence of evidence is not evidence of absence

Laboratory simulation of longitudinally cracked teeth using the step-stress cyclic loading method

AIM

To simulate in a laboratory setting longitudinal cracking in root filled premolar teeth, using cyclic mechanical fatigue.

METHODOLOGY

Mesial-occlusal-distal (MOD) cavities were prepared in twenty root filled, single-rooted, mandibular premolars restored with fibre posts and resin composites. The samples were randomly divided into two groups based on the loading approaches: static loading with a crosshead speed of 0.5 mm/min and step-stress cyclic loading (1 Hz) with increasing amplitude. The loads and numbers of cycles to failure were recorded. Micro-CT was also used to identify the fracture modes. Statistical analysis was performed using Student's t-test. The level of significance was set at 0.05.

RESULTS

The mean fracture loads for the static loading and cyclic loading groups were 769 ± 171 N and 720 ± 92 N, respectively. There was no significant difference between the two groups (P > 0.05). The proportions of longitudinal, cuspal and mixed-mode fractures under cyclic loading were 50%, 20% and 30%, respectively. Longitudinal fractures occurred with larger numbers of cycles and higher average loads per cycle compared with the other fractures. Static loading produced only cuspal fractures.

CONCLUSIONS

Longitudinally cracked premolar teeth with root fillings were successfully produced using the step-stress cyclic loading method. This provides a more clinically representative methodology for studying cracked teeth in a laboratory setting.

The potential effect of instrumentation with different nickel titanium rotary systems on dentinal crack formation-An in vitro study

The potential mechanical impact of different rotary systems used for root canal preparation has been a matter of debate for long. The aim of this study was to explore the incidence of dentinal cracks after root canal instrumentation with various rotary systems, in vitro. One hundred and eighty intact lower central incisors were selected and randomly divided into fourteen treatment groups (n = 12/group) and a control group (n = 12). After decoronation, the root canals were instrumented with fourteen different rotary systems (E3, E3 azure, NT2, Hyflex CM, Hyflex EDM, 2Shape, OneCurve, ProTaper Next, ProTaper Gold, WaveOne Gold, Mtwo, Reciproc Blue, TF adaptive, K3XF). All roots were horizontally sectioned at 3, 6, and 9 mm from the apex with a low-speed saw under water-cooling. The slices were then examined under stereomicroscope for dentinal cracks. No cracks were found in the control group. Cracks were found in all treatment groups, predominantly in the 3 mm slices. There was no statistically significant difference in the number of cracks when comparing the different systems to each other at any section level. At 3 mm, however, five of the studied systems, namely K3XF (p = 0.004), Protaper Next (p = 0.001), Reciproc Blue (p<0.001), TF adaptive (p = 0.050), and 2Shape (p = 0.009) presented a significantly higher number of cracks than the control group. Within the limitations of this study, instrumented canals presented dentinal cracks, while uninstrumented ones presented no cracks after sectioning. There seems to be no significant difference among the tested systems regarding crack formation in the instrumented root canal wall. Crack formation occurred irrespective of the motion of the rotary system (rotational or reciprocation). Further studies are needed to clarify the factors that contribute to crack formation in the case of each individual rotary system.