Shear bond strengths of calcium silicate-based sealer to dentin and calcium silicate-impregnated gutta-percha

AIM

To compare the shear bond strengths of a calcium silicate-based root canal sealer (CSS), to dentin or calcium silicate-impregnated gutta-percha (CSGP), with the shear bond strengths of an epoxy resin-based sealer.

METHODS

For sealer/dentin testing, 40 hemisectioned roots were divided into 2 groups. Coronal root dentin discs were bonded with CSS or epoxy resin-based sealer. For sealer/core material testing, CSGP and conventional gutta-percha discs were bonded with a matching sealer (N = 20 per group). The shear bond strengths were tested using a universal testing machine. The failed modes were analyzed using stereomicroscopy and scanning electron microscopy.

RESULTS

The CSS sealer had significantly higher shear bond strength to dentin than did epoxy resin-based sealer (P < .01). However, shear bond strengths of the 2 sealers to core materials did not significantly differ (P = .74). The remnants of the CSS sealer adhering to dentin or calcium silicate gutta-percha disc were observed.

CONCLUSIONS

The CSS sealer had better adhesion to dentin than did epoxy resin-based sealer. However, the bond of the CSS sealer to impregnated gutta-percha was not superior to the epoxy resin-based sealer bonded to conventional gutta-percha.

The effect of Er,Cr:YSGG laser irradiation on the push-out bond strength of RealSeal self-etch sealer

OBJECTIVE

The aim of this study was to evaluate the effect of an erbium, chromium: yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser on the push-out bond strength of RealSeal Self-Etch (SE) sealer.

BACKGROUND DATA

Various methods are used for smear layer removal in endodontics, such as the application of Er,Cr:YSGG lasers. This laser system may influence the bond strength of resin-based sealers.

METHODS

Sixty single-rooted extracted teeth were selected. After root canal preparation, samples were divided into two experimental groups and one positive control group (n=20 per group). In group 1, the smear layer was removed by irrigation with ethylenediaminetetraacetic acid (EDTA) and sodium hypochlorite (NaOCl). In group 2, the smear layer was removed using a 2.78 μm Er,Cr:YSGG laser with radial firing tips (RFT3) (parameters: 1.5 W, 140 μs, 20 Hz, and 15% water to 15% air ratio), moving at 2 mm/sec in an apico-coronal direction. Group 3 served as a positive control group. Five specimens from each group were selected for scanning electron microscope (SEM) observation. The remaining 45 roots were obturated with RealSeal SE/Resilon and subjected to push-out tests. Data were analyzed using one way analysis of variance (ANOVA) and Tamhane's test.

RESULTS

The results showed no significant difference between push-out bond strength of root canal fillings in the EDTA+NaOCl group and the 1.5 W laser group (p>0.05). The positive control group showed the lowest push-out bond strength.

CONCLUSIONS

The results of the present study indicate that the application of an Er,Cr:YSGG laser with radial firing tips did not adversely affect the push-out bond strength of RealSeal SE sealer to dentin.