Modeling the Water Barrier Properties of Nylon Film Intended for Food Packaging Applications

High-Barrier, Biodegradable Films with Polyvinyl Alcohol/Polylactic Acid + Wax Double Coatings: Influence of Relative Humidity on Transport Properties and Suitability for Modified Atmosphere Packaging Applications

Polyvinyl alcohol (PVOH) exhibits outstanding gas-barrier properties, which favor its use as a biodegradable, high-barrier coating on food-packaging films, possibly in combination with modified atmospheres. Nonetheless, its high sensitivity to water can result in a severe loss of barrier properties, significantly limiting its applications with fresh foods and in high-humidity conditions. In this work, the water vapor (PWV) and oxygen permeability (PO2) of high-barrier biodegradable films with PVOH/PLA + wax double coatings were extensively characterized in a wide range of relative humidity (from 30 to 90%), aimed at understanding the extent of the interaction of water with the wax and the polymer matrices and the impact of this on the permeation process. What is more, a mathematical model was applied to the PWV data set in order to assess its potential to predict the permeability of the multilayer films by varying storage/working relative humidity (RH) conditions. The carbon dioxide permeability (PCO2) of the films was further evaluated, and the corresponding permselectivity values were calculated. The study was finally augmented through modified atmosphere packaging (MAP) tests, which were carried out on double-coated films loaded with 0 and 5% wax, and UV-Vis analyses. The results pointed out the efficacy of the PLA + wax coating layer in hampering the permeation of water molecules, thus reducing PVOH swelling, as well as the UV-shielding ability of the multilayer structures. Moreover, the MAP tests underlined the suitability of the double-coated films for being used as a sustainable alternative for the preservation of foods under modified atmospheres.

Use of antimicrobial biodegradable packaging to control Listeria monocytogenes during storage of cooked ham

The antimicrobial effect against L. monocytogenes of biodegradable films (alginate, zein and polyvinyl alcohol) containing enterocins was investigated. Survival of the pathogen was studied by means of challenge tests performed at 6 degrees C during 8 and 29 days, for air-packed and vacuum-packed sliced cooked ham, respectively. Air packaging was tested with two concentrations of enterocins (200 and 2000 AU/cm2). Control air-packed cooked ham showed an increase of L. monocytogenes from 10(4) to 10(7) CFU/g after 8 days. By contrast, packaging with antimicrobial films effectively slowed down the pathogen's growth, leading to final counts lower than in control lots. Air-packaging with alginate films containing 2000 AU/cm2 of enterocins effectively controlled L. monocytogenes for 8 days. An increase of only 1 log unit was observed in zein and polyvinyl alcohol lots at the same enterocin concentration. Vacuum packaging with films containing enterocins (2000 AU/cm2) also delayed the growth of the pathogen. No increase from inoculated levels was observed during 15 days in antimicrobial alginate films. After 29 days of storage, the lowest counts were obtained in samples packed with zein and alginate films containing enterocins, as well as with zein control films. The most effective treatment for controlling L. monocytogenes during 6 degrees C storage was vacuum-packaging of sliced cooked ham with alginate films containing 2000 AU/cm2 of enterocins. From the results obtained it can concluded that antimicrobial packaging can improve the safety of sliced cooked ham by delaying and reducing the growth of L. monocytogenes.