Application of combined EBSD and 3D-SEM technique on crystallographic facet analysis of steel at low temperature

Facet type determination based on combined atomic force microscopy and electron backscatter diffraction

The distribution of facet types affects the functionality of the surfaces of polycrystalline films. However, we are not aware of a previously published convenient method to determine their distribution. This work describes and demonstrates a process to determine and map the Miller indexes (hkl) of crystal facets exposed at the surfaces of polycrystalline films. To find facet types in non-trivial cases, one must know the orientation of the crystal and the direction in which the facet is facing. The method presented here combines the crystal orientations obtained with electron backscatter diffraction with the topography of the same sample area measured with atomic force microscopy. A challenging step is to transfer the data from the two instruments into a common coordinate system. The sequence of steps in the data processing is presented, with methods to verify the results. The process is illustrated with the analysis of an etched copper clad laminate (CCL) and an electroless Cu film deposited on the CCL. This example relates to facet selection in electroless and galvanic plating processes in printed circuit board production, where an uncontrolled transition from epitaxial to non-epitaxial growth can lead to surfaces with unacceptable roughness.

Metallurgical Aspects in the Welding of Clad Pipelines—A Global Outlook

In the present work, the metallurgical changes in the welding of clad pipelines are studied. Clad pipes consist of a complex multi-material system, with (i) the clad being stainless steel or a nickel-based superalloy, (ii) the pipe being API X60 or X65 high-strength carbon steel, and (iii) the welding wire being a nickel-based superalloy or stainless steel in the root and hot pass, with a nickel or iron buffer layer, followed by filling with carbon steel wire. Alternatively, the corrosion resistant alloy may be used only. During production of the clad pipe, at the diffusion bonding temperature, substantial material changes may occur. These are carbon diffusion from the carbon steel to the clad, followed by the formation of hard martensite at the interface on cooling. The solidification behavior and microstructure evolution in the weld metal and in the heat-affected zone are further discussed for the different material combinations. Solidification behavior was also numerically estimated to show solidification parameters and resulting solidification modes.