An improved time-of-flight method for cluster deposition and ion-scattering experiments

A molecular beam apparatus has been developed for deposition and scattering experiments of size-selected clusters. The new setup combines a bimetallic laser ablation cluster source with a collinear time-of-flight mass spectrometer. Mass selection is achieved with a pulsed electrostatic mirror. A significantly improved transmission in combination with a reduction of the kinetic energy distribution of the mass selected clusters has been obtained. Without further modification of the apparatus, surface-induced dissociation of mass selected tin clusters has been investigated, demonstrating the possibility to combine cluster beam deposition and scattering experiments.

Unisized two-dimensional platinum clusters on silicon(111)-7x7 surface observed with scanning tunneling microscope

Uni-sized platinum clusters (size range of 5-40) on a silicon(111)-7 x 7 surface were prepared by depositing size-selected platinum cluster ions on the silicon surface at the collision energy of 1.5 eV per atom at room temperature. The surface thus prepared was observed by means of a scanning tunneling microscope (STM) at the temperature of 77 K under an ambient pressure less than 5 x 10(-9) Pa. The STM images observed at different cluster sizes revealed that (1) the clusters are flattened and stuck to the surface with a chemical-bond akin to platinum silicide, (2) every platinum atom occupies preferentially the most reactive sites distributed within a diameter of approximately 2 nm on the silicon surface at a cluster size up to 20, and above this size, the diameter of the cluster increases with the size, and (3) the sticking probability of an incoming cluster ion on the surface increases with the cluster size and reaches nearly unity at a size larger than 20.

Electronic structures of size-selected single-layered platinum clusters on silicon(111)-7×7 surface at a single cluster level by tunneling spectroscopy

Tunneling spectra of size-selected single-layered platinum clusters (size range of 5-40) deposited on a silicon(111)-7x7 surface were measured individually at a temperature of 77 K by means of a scanning tunneling microscope (STM), and the local electronic densities of states of individual clusters were derived from their tunneling spectra measured by placing an STM tip on the clusters. In a bias-voltage (V(s)) range from -3 to 3 V, each tunneling spectrum exhibits several peaks assignable to electronic states associated with 5d states of a constituent platinum atom and an energy gap of 0.1-0.6 eV in the vicinity of V(s)=0. Even when platinum cluster ions having the same size were deposited on the silicon(111)-7x7 surface, the tunneling spectra and the energy gaps of the deposited clusters are not all the same but can be classified in shape into several different groups; this finding is consistent with the observation of the geometrical structures of platinum clusters on the silicon(111)-7x7 surface. The mean energy gap of approximately 0.4 eV drops to approximately 0.25 eV at the size of 20 and then decreases gradually as the size increases, consistent with our previous finding that the cluster diameter remains unchanged, but the number density of Pt atoms increases below the size of 20 while the diameter increases, but the density does not change above it. It is concluded that the mean energy gap tends to decrease gradually with the mean cluster diameter. The dependence of the mean energy gap on the mean Pt-Pt distance shows that the mean energy gap decreases sharply when the mean Pt-Pt distance exceeds that of a platinum metal (0.28 nm).