Enhanced Development of Sweat Latent Fingerprints Based on Ag-Loaded CMCS/PVA Composite Hydrogel Film by Electron Beam Radiation

Over time, difficulties have been encountered in detecting potential fingerprints. In this study, an Ag/CMCS/PVA(ACP) hydrogel film was developed for fingerprint development by electron beam radiation method. The chemical bond, thermostability, chemical components, microstructure, and micromorphology of the CMCS/PVA composite hydrogel film were characterized by FT-IR, TG, XRD, and SEM, respectively. Swelling behaviors and mechanical performance of the CMCS/PVA composite hydrogel were also investigated at different irradiation doses, pH, media, and NaCl contents to obtain the optimum preparation conditions. Through experimental exploration, we found that the fingerprints appeared more obvious when the irradiated prepared ACP hydrogel film was sprayed with 0.6 mg/mL of Ag+ and the excitation wavelength was about 254 nm with UV lamp irradiation for 20 min. The cytotoxicity the CMCS/PVA composite hydrogel on mouse skin fibroblasts L929 cells was also studied, confirming its biological security. Sweat latent fingerprint manifestation has important scientific significance with respect to the development of new processes and functional materials in the field of fingerprint manifestation, enriching and complementing the application of composite hydrogels.

Synthesis and characterisation of zinc oxide modified biorenewable polysaccharides based sustainable hydrogel nanocomposite for Hg2+ ion removal: Towards a circular bioeconomy

Industrial metal ion pollution has been considered the chief source of water contaminants all over the world. In the present research, we have prepared gum tragacanth cross-linked 2-hydroxyethyl methacrylate-co-acrylamide (GT-cl-(HEMA-co-AAm)) hydrogel and gum tragacanth cross-linked 2-hydroxyethyl methacrylate-co-acrylamide/zinc oxide (GT-cl-(HEMA-co-AAm)/ZnO) hydrogel composite with better Hg²⁺ adsorption capability. GT-cl-(HEMA-co-AAm)/ZnO hydrogel composite (154.8 mg g^-1) exhibited higher Hg²⁺ adsorption than GT-cl-(HEMA-co-AAm) hydrogel. To address the performance of GT-cl-(HEMA-co-AAm) hydrogel and GT-cl-(HEMA-co-AAm)/ZnO hydrogel composite, batch adsorption experiments were successfully conducted under different optimised conditions. At last, in-vitro antibacterial activities of Hg²⁺ loaded GT-cl-(HEMA-co-AAm) and GT-cl-(HEMA-co-AAm)/ZnO were performed in two different well Staphylococcus aureus (gram-positive) and Pseudomonas aeruginosa (gram-negative) bacteria. As a positive control, ampicillin was employed against both types of bacteria. This methodology for the reusability of material has a great ecofriendly impression for minimising secondary waste derived from adsorption and can help design upgraded antibacterial agents.