Impact of Ce/Zr Ratio in the Nanostructured Ceria and Zirconia Composites on the Selective CO2 Adsorption

High surface-area, mesoporous CeO2, ZrO2, and Ce-Zr composite nanoparticles were developed using the hydrothermal template-assisted synthesis method. Samples were characterized using XRD, N2 physisorption, TEM, XPS, and FT-IR spectroscopic methods. The CO2 adsorption ability of the obtained materials was tested under dynamic and equilibrium conditions. A high CO2 adsorption capacity in CO2/N2 flow or CO2/N2/H2O was determined for all studied adsorbents depending on their composition flow. A higher CO2 adsorption was registered for Ce-Zr composite nanomaterials due to the presence of strong O2- base sites and enriched surface oxygen species. The role of the Ce/Zr ratio is the process of the formation of highly active and selective adsorption sites is discussed. The calculated heat of adsorption revealed the processes of chemisorption and physisorption. Experimental data could be appropriately described by the Yoon-Nelson kinetic model. The composites reused in five adsorption/desorption cycles showed a high stability with a slight decrease in CO2 adsorption capacities in dry flow and in the presence of water vapor.

A New Approach for the Synthesis of Powder Zinc Oxide and Zinc Borates with Desired Properties

Zinc borates are widely used in industry due to their thermal stability as a flame retardant in the production of plastics, rubber, and other polymer compositions. We have developed a simple and effective approach for the synthesis of zinc borate powders with desired properties, including desired particle size, low bulk density, high reactivity, etc. Zinc borates were prepared by the thermal treatment of a concentrated water–carbohydrate solution of a zinc salt until finely dispersed ZnO was formed, followed by its hydrothermal treatment at 90–300 °C as part of a suspension based on a hot aqueous solution of H3BO3. According to X-ray powder diffraction, IR spectroscopy, and TG–DSC data, depending on the temperature of hydrothermal treatment, a decrease in the water content in the structure of synthesized zinc borate particles is observed. TEM and SEM data indicate the formation of isometrically shaped zinc borate particles in the nanometer range during hydrothermal treatment above 250 °C. Varying the temperature of the hydrothermal treatment affects the average size and fineness of the structure of the zinc borate particles.