Antimicrobial surface processing of polymethyl methacrylate denture base resin using a novel silica-based coating technology

OBJECTIVES

This study investigated the surface characteristics of denture base resin coatings prepared using a novel silica-based film containing hinokitiol and assessed the effect of this coating on Candida albicans adhesion and growth.

METHODS

Silica-based coating solutions (control solution; CS) and CS containing hinokitiol (CS-H) were prepared. C. albicans biofilm formed on denture base specimens coated with each solution and these uncoated specimens (control) were analyzed using colony-forming unit (CFU) assay, fluorescence microscopy, and scanning electron microscopy (SEM). Specimen surfaces were analyzed by measuring the surface roughness and wettability and with Fourier-transform infrared (FT-IR) and proton nuclear magnetic resonance (¹H NMR). Stability of coated specimens was assessed via immersion in water for 1 week for each group (control-1w, CS-1w, and CS-H-1w) followed by CFU assay, measurement of surface roughness and wettability, and FT-IR.

RESULTS

CS-H and CS-H-1w contained significantly lower CFUs than those present in the control and control-1w, which was also confirmed via SEM. Fluorescence microscopy from the CS-H group identified several dead cells. The values of surface roughness from coating groups were significantly less than those from the control and control-1w. The surface wettability from all coating groups exhibited high hydrophobicity. FT-IR analyses demonstrated that specimens were successfully coated, and ¹H NMR analyses showed that hinokitiol was incorporated inside CS-H.

CONCLUSIONS

A silica-based denture coating that incorporates hinokitiol inhibits C. albicans growth on denture.

CLINICAL RELEVANCE

We provide a novel antifungal denture coating which can be helpful for the treatment of denture stomatitis.

Water Treatment Using High Performance Antifouling Ultrafiltration Polyether Sulfone Membranes Incorporated with Activated Carbon

Membrane fouling is a continued critical challenge for ultrafiltration membranes performance. In this work, polyether sulfone (PES) ultrafiltration (UF) membranes were fabricated via phase-inversion method by incorporating varying concentrations of APTMS modified activated carbon (mAC). The mAC was thoroughly characterized and the fabricated membranes were studied for their surface morphology, functional groups, contact angle, water retention, swelling (%) porosity, and water flux. The hydrophilicity of mAC membranes also resulted in lower contact angle and higher values of porosity, roughness, water retention as well as water flux. Also, the membranes incorporated with mAC exhibited antibacterial performance against model test strains of gram-negative Ecoil and gram-positive S. aureus. The antifouling studies based on bovine serum albumin protein (BSA) solution filtration showed that mAC membranes have better BSA flux. The higher flux and antifouling characteristics of the mAC membranes were attributed to the electrostatic repulsion of the BSA protein from the unique functional properties of AC and network structure of APTMS. The novel mAC ultrafiltration membranes developed and studied in present work can provide higher flux and less BSA rejection thus can find antifouling applications for the isolation and concentration of proteins and macromolecules.

Influence of Air Cold Plasma Modification on the Surface Properties of Paper Used for Packaging Production

In this study, the effect of air plasma on the surface properties of printed and coated cardboard was investigated. The material was activated by low-pressure cold plasma for 1, 10, 20, and 30 s. Wettability changes on the surface were examined by contact angle measurements using the sessile droplet technique. The differences in the surface free energy were calculated using the Lifshitz–van der Waals/acid–base and Contact Angle Hysteresis approaches. Optical profilometry was used for the surface roughness evaluation and an X-ray photoelectron spectroscopy analysis was performed to find changes in surface chemistry. Adhesive strength tests were carried out to estimate the adhesion changes after the material’s modification. It was found that the water and formamide contact angles increased after the plasma treatment while the diiodomethane contact angle did not change. As a result of the modification, the surface free energy also increased significantly and the surface roughness increased. The pull-off tests confirmed the improvement in the material’s surface properties. Moreover, it was demonstrated that the optimal effect can be obtained after just 10 s of the plasma process.

Antialgal Synergistic Polystyrene Blended with Polyethylene Glycol and Silver Sulfadiazine for Healthcare Applications

Polystyrene (PS) was blended with polyethylene glycol (PEG) and silver sulfadiazine (SS) with different weight proportions to form polymeric blends. These synthesized blends were preliminary characterized in terms of functional groups through the FTIR technique. All compositions were subjected to thermogravimetric analysis for studying thermal transition and were founded thermally stable even at 280°C. The zeta potential and average diameter of algal strains of Dictyosphaerium sp. (DHM1), Dictyosphaerium sp. (DHM2), and Pectinodesmus sp. (PHM3) were measured to be -32.7 mV, -33.0 mV, and -25.7 mV and 179.6 nm, 102.6 nm, and 70.4 nm, respectively. Upon incorporation of PEG and SS into PS blends, contact angles were decreased while hydrophilicity and surface energy were increased. However, increase of surface energy did not led to decrease of antialgal activities. This has indicated that biofilm adhesion is not a major antialgal factor in these blended materials. The synergetic effect of PEG and SS in PS blends has exhibited significant antialgal activity via the agar disk diffusion method. The PSPS10 composition with 10 $w/w\%$ PEG and 10 $w/w\%$ SS has exhibited highest inhibition zones 10.8 mm, 10.8 mm, and 11.3 mm against algal strains DHM1, DHM2, and DHM3, respectively. This thermally stable polystyrene blends with improved antialgal properties have potential for a wide range of applications including marine coatings.

Transpicuous-Cum-Fouling Resistant Copolymers of 3-Sulfopropyl Methacrylate and Methyl Methacrylate for Optronics Applications in Aquatic Medium and Healthcare

The scope of optical sensors and scanners in aquatic media, fluids, and medical diagnostics has been limited by paucity of transparent shielding materials with antifouling potential. In this research endeavor, facile synthesis, characterization, and bioassay of antifouling transparent functional copolymers are reported. Copolymers of 3-sulfopropyl methacrylate (SPMA) and methyl methacrylate (MMA) were synthesized by free radical polymerization in various proportions. Samples PSM20, PSM30, PSM40, PSM50, and PSM60 contain 20%, 30%, 40%, 50%, and 60% SPMA by weight, respectively. Resultant products were characterized by FTIR and 1H-NMR spectroscopy. The synthesized copolymers have exhibited excellent transparency, i.e., 75% to 88%, as determined by the UV-Vis spectroscopic analysis. Transmittance was decreased from 6% to 2% in these copolymers upon changing the concentration of 3-sulfopropyl methacrylate from 20% to 50% owing to bacterial and algal biofilm formation. Water contact angle values were ranged from 18° to 63° and decreased with the increase in the polarity of copolymers. The surface energy lowest value 58 mJ/m2 and highest value 72 mJ/m2 were calculated for PSM20 and PSM50, respectively, by the Chibowski approach and Young equation. Sample PSM50 has exhibited the highest antibacterial activities, i.e., 18 mm and 19 mm, against Escherichia coli and Staphylococcus aureus, respectively, by the disk diffusion method. Copolymer PSM50 has shown minimum algal adhesion for Dictyosphaerium algae as observed by optical microscopy. This lower bacterial and algal adhesion is attributed to higher concentrations of anionic SPMA monomer that cause electrostatic repulsion between functional groups of the polymer and microorganisms. Thus, the resultant PSM50 product has exhibited good potential for optronics shielding application in aquatic medium and medical diagnostics.

Reply to Comment on "Solid-Liquid Work of Adhesion"

Extrand's interpretation in his "Comment on "Solid-Liquid Work of Adhesion" by Tadmor and Coworkers" may lead to an important discussion and physical understanding of the problem. Below, we compare the two approaches and elucidate the differences to put them in the right perspective.