"Green" Synthesis of Metallic Nanoparticles by Sonoelectrochemical and Sonogalvanic Replacement Methods

CO2 Electroreduction in Organic Aprotic Solvents: A Mini Review

An annual increase of CO2 concentrations in the atmosphere causes global environmental problems, addressed by systematic research to develop effective technologies for capturing and utilizing carbon dioxide. Electrochemical catalytic reduction is one of the effective directions of CO2 conversion into valuable chemicals and fuels. The electrochemical conversion of CO2 at catalytically active electrodes in aqueous solutions is the most studied. However, the problems of low selectivity for target products and hydrogen evolution are unresolved. Literature sources on CO2 reduction at catalytically active cathodes in nonaqueous mediums, particularly in organic aprotic solvents, are analyzed in this article. Two directions of cathodic reduction of CO2 are considered—nonaqueous organic aprotic solvents and organic aprotic solvents containing water. The current interpretation of the cathodic conversion mechanism of carbon (IV) oxide into CO and organic products and the main factors influencing the rate of CO2 reduction, Faradaic efficiency of conversion products, and the ratio of direct cathodic reduction of CO2 are given. The influence of the nature of organic aprotic solvent is analyzed, including the topography of the catalytically active cathode, values of cathode potential, and temperature. Emphasis is placed on the role of water impurities in reducing CO2 electroreduction overpotentials and the formation of new CO2 conversion products, including formate and H2.

Synthesis of silver nanoparticles by sonogalvanic replacement on aluminium powder in sodium polyacrylate solutions

The process of the formation of silver nanoparticles (AgNPs) via the method of galvanic replacement (GR) of Ag⁺ with aluminum powder in sodium polyacrylate (NaPA) solutions in the ultrasonic (US) field has been studied. It was observed, that the yellow colloidal solutions of stabilized AgNPs with the absorption maximum at ∼ 410 nm were obtained under the application of US power by 20 W and frequency by 20 kHz in the wide range of AgNO₃ and NaPA concentrations (0.1 - 0.5 mM and 0.5 - 5.0 g/L respectively) at 25 ⁰C. It was shown, that the GR process under US field occurs without of the significant induction period. Using the UV-vis spectroscopy the kinetics of AgNPs formation has been studied and it was observed the first order kinetics with respect to Ag⁺ ions both for the nucleation and growth processes. It was found that observable rate constants of nucleation are close for the all experimental conditions but the observable rate constants of growth decreased with increasing of initial concentration of AgNO₃. Based on the obtained kinetic data it was proposed a mechanism of the formation of AgNPs consisted of the following two main stages: 1) the nucleation with the formation of primary nanoclusters (AgNCs) on aluminum surface followed by their ablation from the surface of the sacrificial metal by ultrasound into bulk of solution; 2) the transformation of AgNCs in AgNPs via growth from the Al surface and / or agglomeration of AgNCs. Using TEM it was found that the size of obtained AgNPs does not exceed of 25 nm and slightly depends on the initial concentrations of precursors. High antimicrobial activity of obtained colloidal solutions against gram-negative and gram-positive bacteria as well as against fungi was observed.