Immobilization of aminoglycosidic aminocyclitols antibiotic onto soap-free poly(MMA-EA-AA) latex particles

Inherently Antimicrobial Biodegradable Polymers in Tissue Engineering

Many of the strategies currently being explored in the field of tissue engineering involve the combination of cells and degradable engineered scaffolds for the regeneration of biological tissues. However, infection of the wound or the scaffold itself results in failure of healing. Therefore, a new area of development in the field is the synthesis of polymer-based scaffolds that inherently have the ability to resist microbial infection as degradation occurs and new tissue replaces the scaffold. These scaffolds, defined as inherently antimicrobial biodegradable polymers (IABPs), can be classified based on their monomeric components as follows: (1) traditional antimicrobials (such as beta-lactams, fluoroquinolones, glycopeptides, and aminoglycosides), (2) naturally derived compounds (such as extracellular matrix components, chitosan, and antimicrobial peptides), and (3) novel synthetic antimicrobials. After validation of chemical synthesis as well as physicochemical characterization of a newly created IABP, thorough in vitro and in vivo assays must be conducted to ensure antimicrobial efficacy as well as biocompatibility as a tissue-engineered scaffold system. In this review, we will introduce existing IABPs, discuss the current platforms that have been developed for the synthesis of IABPs, and highlight future directions as well as challenges in the field.

Synthesis and characterization of monodispersed P(St-co-DMAEMA) nanoparticles as pH-sensitive drug delivery system

Monodispersed poly(styrene-co-N,N'-dimethylaminoethyl methacrylate) nanoparticles (P(St-co-DMAEMA) NPs) were synthesized by emulsion polymerization. Zeta potential, volume swelling ratio and in vitro release of fluorescer coumarin-6 from the NPs were determined in buffer of various pH. With an optimized formulation, the diameter of NPs is 100 nm approximately and the polydispersity index (PI) is less than 0.1. The NPs have a hydrophilic surface and alterable surface charge which is almost neutral at normal physiological pH, but becomes much more positive under acidic conditions. The volume swelling ratios and in vitro release of coumarin-6 are highly dependent on pH, which are significantly increased at the lower pH and higher DMAEMA/St molar ratio. More than 70% of the loaded coumarin-6 could be released in 24 h at pH2, which is 2.3-folds higher than that at normal physiological pH. The P(St-co-DMAEMA) NPs show promising applications to targeted drug delivery to tumors.