Characterization and in vivo study of decellularized aortic scaffolds using closed sonication system

Extracellular matrix (ECM) based bioscaffolds prepared by decellularization has increasingly emerged in tissue engineering application because it has structural, biochemical, and biomechanical cues that have dramatic effects upon cell behaviors. Therefore, we developed a closed sonication decellularization system to prepare ideal bioscaffolds with minimal adverse effects on the ECM. The decellularization was achieved at 170 kHz of ultrasound frequency in 0.1% and 2% Sodium Dodecyl Sulphate (SDS) solution for 10 hours. The immersion treatment as control was performed to compare the decellularization efficiency with our system. Cell removal and ECM structure were determined by histological staining and biochemical assay. Biomechanical properties were investigated by the indentation testing to test the stiffness, a residual force and compression of bioscaffolds. Additionally, in vivo implantation was performed in rat to investigate host tissue response. Compared to native tissues, histological staining and biochemical assay confirm the absence of cellularity with preservation of ECM structure. Moreover, sonication treatment has not affected the stiffness [N/mm] and a residual force [N] of the aortic scaffolds except for compression [%] which 2% SDS significantly decreased compared to native tissues showing higher SDS has a detrimental effect on ECM structure. Finally, minimal inflammatory response was observed after 1 and 5 weeks of implantation. This study reported that the novelty of our developed closed sonication system to prepare ideal bioscaffolds for tissue engineering applications.

Evaluation of recellularization on decellularized aorta scaffolds engineered by ultrasonication treatment

Aortic scaffolds prepared using sonication decellularization treatment has provided a successful medium for repopulation with vascular smooth muscle cells (VSMCs). The objective of this study is to explore the potential of tissue decellularization using ultrasonication treatment and its recellularization before implantation of the cell-seeded scaffolds into host. Aorta tissue samples are decellularized in 2% SDS with sonication for 10 hours and compared with the native tissues. The 4',6-diamidino-2-phenylindole (DAPI) staining was used to evaluate the decellularization and Hematoxylin-Eosin (H-E) staining was used to compare the VSMCs infiltrations onto the decellularized tissues at day-0 and day-6 after cell-seeding. The results histologically showed complete DNA removal from scaffolds after decellularization and subsequent recellularization resulted in successful VSMCs infiltration. Accordingly, the decellularized tissues treated with 2% SDS in sonication demonstrated successful VSMCs repopulation afterward and is speculated to have less toxicity and able to be effectively implanted into host.