Biodegradable Polymer (D,L-Lactide-ε-Caprolactone) in Aortic Vascular Prosthesis: Morphological Evaluation in an Animal Model

Biocompatibility of different biopolymers after being implanted into the rat cochlea. Otol Neurotol. 2008;29:714-719. [PMID: 18580700 DOI: 10.1097/mao.0b013e31817d874b]

OBJECTIVE

To assess the biocompatibility of different biopolymers with cochlea implant.

MATERIALS AND METHODS

Six bioabsorbable polymers and biostable silicone were used for testing histologic reactions in the cochlea of the rat. The samples were prepared from three 50/50 poly(DL-lactide-co-glycolide) PDLLGA having different inherent viscosity (IV) values and 75/25 poly(DL-lactide-co-epsilon-caprolactone) P(DLLA/CL), poly-epsilon-caprolactone PCL, silicone, and chitosan by extruding the biomaterial as a rod using melt molding (for 50/50 PDLLGAs and 75/25 P(DLLA/CL) and PCL), blending (for silicone), and solving (for chitosan). The rods were cut into samples of diameter of 0.5 mm and length of 2 mm. All the samples were packed and sterilized by gamma irradiation (18 kGy, less than 42 degrees C). Twenty-two male and female Sprague-Dawley rats were used in the study. Four months after the implantation, the animals were killed for histologic observation.

RESULTS

Chitosan does not degrade in the cochlea 4 months after implantation and, therefore, stimulates very weak inflammatory reaction. The 50/50 PDLLGA (IV, 0.83 dL/g) degrades in the cochlea 4 months after implantation and does not stimulate inflammatory reaction. The 50/50 PDLLGA (IV, 0.41 dL/g; IV, 0.37 dL/g), 75/25 P(DLLA/CL), PCL, and silicone might induce strong inflammatory reaction in the cochlea.

CONCLUSION

Different degradation property of biomaterials in the cochlea indicates diverse drug releasing time in a controlled way. Chitosan is suitable for long-lasting drug delivery, whereas 50/50 PDLLGA (IV, 0.83 dL/g) favors quicker releasing. Both chitosan and 50/50 PDLLGA (IV, 0.83 dL/g) are ideal materials for cochlear drug delivery.

Adhesion prevention comparing liquid and solid barriers in the rabbit uterine horn model

OBJECTIVE

The purpose of this study was to assess the ability of four different either solid or fluid barriers to reduce adhesions in an established model of gynecological surgery.

STUDY DESIGN

50 Chinchilla rabbits underwent bilateral deperitonealization and devascularization of the uterine horns (DUH). Afterwards solid membranes of either hyaluronic acid-carboxymethylcellulose (HA-CMC) or lactide-caprolactone-copolymer (LCC) were placed around the injured uterine horns or fluids (icodextrin (ID) or phospholipids (PL)) were intraperitonealy administered. The control group went without protection. After 10 days, adhesions were measured by planimetry.

RESULTS

Phospholipids (median 49.8 mm2) significantly reduced adhesion areas in comparison to all other groups: surgical controls (median 230.6 mm2), HA-CMC (median 194.9 mm2), LCC (median 327.1 mm2), and icodextrin (median 242.1 mm2).

CONCLUSIONS

These results prove the efficacy of phospholipids to reduce primary adhesion formation in the Chinchilla double uterine horn model compared to HA-CMC, LCC and icodextrin. Future clinical studies are recommended.

Evaluation of biodegradable synthetic scaffold coated on arterial prostheses implanted in rat subcutaneous tissue

Polyester arterial prostheses impregnated with various synthetic biodegradable materials and with gelatin were implanted subcutaneously in rats for 3-180 days. The inflammation was assessed by quantifying the activity of alkaline phosphatase and by histology. The degradation of the scaffold materials was determined by scanning electron microscopy (SEM), size exclusion chromatography (SEC), and differential scanning calorimetry (DSC). The alkaline phosphatase activity induced by the polymer-impregnated grafts was similar to that induced by the non-impregnated controls during most of the post-implantation periods. Histological studies revealed that the acute inflammatory response was moderate to mild and was similar for all types of specimens, except for the gelatin-impregnated grafts that induced a severe acute inflammation during the first 2 weeks post-implantation. At 4 and 6 months, significant disintegration of the scaffold was observed, accompanied by enhanced tissue infiltration and a reactivation of the acute inflammatory phase. Linear and exponential degradation rates of the synthetic polymers were described. The relative degradation rates of the biodegradable polymers were ranked as following: PLLACL > PDLLA > PLLA > PCEL. In conclusion, biodegradable polymers may provide an option as sealant/scaffolding materials for vascular prosthesis. It is suggested that the degradation rate of the polymer scaffolding materials should be higher to achieve early healing while without inducing strong inflammation.