The effect of different energy levels of the Er: YAG laser on the repair bond strength of a nanohybrid composite resin

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance

OBJECTIVE

The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites.

MATERIALS AND METHODS

Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis.

RESULTS

The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups.

CONCLUSION

The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material.

CLINICAL RELEVANCE

The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.

Evaluation of the Shear Bond Strength of Immediate and Delayed Restorations of Various Calcium Silicate-Based Materials with Fiber-Reinforced Composite Resin Materials

Due to significant tissue loss in teeth requiring pulp treatments, hermetic restoration of the remaining dental tissues is one of the most crucial factors in determining the treatment's success. The adhesion of composite resins to calcium silicate cements (CSCs) is considered challenging. Consequently, it is crucial to identify the optimal method for obtaining optimal adhesion. The aim of the present study is to evaluate the shear bond strength (SBS) values of immediate and delayed restorations with fiber-reinforced composites on powder-liquid, premixed, and resin-containing flowable CSCs. In the present study, the SBS values obtained after immediate (14 min) and delayed (7 days) restorations of three different CSCs (NeoMTA2, NeoPutty, and TheraCal PT) with three different resin composite materials (EverX FlowTM, EverX PosteriorTM, and Filtek Z550) were compared. The fracture types were evaluated using a stereomicroscope and SEM. TheraCal PT had the highest SBS values for both immediate and delayed restorations, and the comparison with other materials showed a statistically significant difference (p = 0.001). In contrast, there was no statistically significant difference between the SBS values of NeoMTA and NeoPutty (p > 0.05). In both immediate and delayed restorations, there was no statistically significant difference between nanohybrid and fiber-reinforced composites (p > 0.05). The simple use and strong bonding ability of TheraCal PT with composite resins may provide support for the idea that it is suitable for pulpal interventions. Nevertheless, due to the in vitro nature of this study, additional in vitro and clinical studies are required to investigate the material's physical, mechanical, and biological properties for use in clinical applications.

Evaluation of repair bond strength of a dental CAD/CAM resin composite after surface treatment with two Er,Cr:YSGG laser protocols following artificial aging

The aim of the present study was to evaluate the impact of two Er,Cr:YSGG laser surface treatments on the repair bond strength of a dental CAD/CAM resin composite (Brilliant Crios) after artificial aging. Twenty-four resin-based CAD/CAM blocks were cut and 48 rectangular slabs (3 x 12 x 14 mm) were prepared. Preliminary SEM observations indicated the most favorable laser settings regarding surface modification of the tested restorative material. The CAD/CAM specimens were then divided into 4 groups (n=12) based on their surface pretreatment: no treatment, air abraded with 50-μm Al2O3 particles, and laser irradiated with two different protocols using Er,Cr:YSGG laser with average power 3.5 and 4.5 W, pulse repetition rate 35 and 50 Hz, and pulse energy 100 and 90 mJ, respectively. After surface treatments each group followed a bonding protocol with silane and a flowable resin composite was used to prepare 48 microrods. Half of the microrods of each group were subjected on shear bond strength (SBS) test (chisel-shaped blade, load cell of 500 N, crosshead speed of 1 mm/min) after 24 h, while the other half underwent artificial aging (15,000 cycles, 5-55 °C) and then SBS test. The debonded specimens were examined under an optical microscope to determine the failure mode. All specimens were also evaluated using SEM to assess the surface topography after the treatments. The results showed that SBS significantly decreased after thermocycling in all the experimental groups (p<0.05). Control group presented much lower SBS values than the other groups after both 24 h and thermocycling (p<0.05). The highest values of SBS exhibited air-abrasion group (p<0.05), followed by the two laser groups, which did not differ to each other (p>0.05). The results of the current study indicated that Er,Cr:YSGG laser irradiation can be an alternative treatment for repairing the tested resin-based CAD/CAM restorative material.

A Comparative Study of the Repair Bond Strength of New Self-Adhesive Restorative Materials With a Resin Composite Material

AIM

The aim of the present study is to compare the repair bond strengths (RBSs) of Cention-N (light-cure and self-cure modes), Equia Forte HT Fil and a nanohybrid resin composite.

MATERIALS AND METHODS

Equia Forte HT Fil (GC, Tokyo, Japan), Cention-N (Ivoclar Vivadent, Schaan, Liechtenstein) and Filtek Z550 (3M ESPE, St Paul, MN, USA) were used in this study. Equia Forte HT Fil (EQF), Cention-N self-cure (CSC), Cention-N light-cure (CLC) and Filtek Z550 (Z550) groups were formed. A total of 40 samples were prepared; 10 samples in each group (n = 10). After the polymerization was completed according to the manufacturer's instructions, the samples were polished with OptiDisc (Kerr Corporation, Orange, USA) for 5 s each, from extra-course to extra-fine. After all samples were stored in 37°C water for 24 h, 10,000 cycles of brushing simulator and thermal cycles were applied to the samples. The samples were prepared in accordance with the selected repair protocol, and microshear bond strength (µSBS) test was performed. Fracture analysis on debonded surfaces was visualized by scanning electron microscopy. The conformity of the data to normal distribution was analyzed by the Shapiro-Wilk test. Multiple comparisons were performed using Dunn's test.

RESULTS

 Z550 showed significantly higher µSBS as compared to the other three groups. There is no difference between CSC, CLC and EQF.

CONCLUSION

The use of Cention-N's self-cure or light-cure mode did not affect the RBS values. The RBS values of Cention-N and Equia Forte HT Fil materials are lower than those of the composite resin material.