No difference in whole-blood metal ions between 32-mm and 36- to 44-mm femoral heads in metal-on-polyethylene total hip arthroplasty: a 2-year report from a randomised control trial

The size of the femoral head does not influence metal ion levels after metal-on-polyethylene total hip arthroplasty: a five-year report from a randomized controlled trial

Aims

In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients.

Methods

A total of 96 patients were enrolled at two centres and randomized to undergo MoP THA using either a 32 mm metal head or a femoral head of between 36 mm and 44 mm in size, being the largest possible to fit the thinnest available polyethylene insert. The levels of metal ions and patient-reported outcome measures (Oxford Hip Score, University of California, Los Angeles Activity Scale) were recorded at two and five years postoperatively.

Results

At five years, the median levels of chromium, cobalt, and titanium were 0.5 μg/l (interquartile range (IQR) 0.50 to 0.62), 0.24 μg/l (IQR 0.18 to 0.30), and 1.16 μg/l (IQR 1.0 to 1.68) for the 32 mm group, and 0.5 μg/l (IQR 0.5 to 0.54), 0.23 μg/l (IQR 0.17 to 0.39), and 1.30 μg/l (IQR 1 to 2.05) for the 36 mm to 44 mm group, with no significant difference between the groups (p = 0.825, p = 1.000, p = 0.558). There were increased levels of metal ions at two years postoperatively in seven patients in the 32 mm group, compared with four in the 36 mm to 44 mm group, and at five years postoperatively in six patients in the 32 mm group, compared with seven in the 36 mm to 44 mm group. There was no significant difference in either the OHS (p = 0.665) or UCLA (p = 0.831) scores between patients with or without an increased level of metal ions.

Conclusion

In patients who underwent MoP THA, we found no differences in the levels of metal ions five years postoperatively between those with a femoral head of 32 mm and those with a femoral head of between 36 mm and 44 mm, and no corrosion-related revisions. As taper corrosion can start after five years, there remains a need for longer-term studies investigating the relationship between the size of the femoral head size and corrosion in patients undergoing MoP THA.

Similarly low blood metal ion levels at 10-years follow-up of total hip arthroplasties with Oxinium, CoCrMo, and stainless steel femoral heads. Data from a randomized clinical trial

The use of inert head materials such as ceramic heads has been proposed as a method of reducing wear and corrosion products from the articulating surfaces in total hip arthroplasty, as well as from the stem-head taper connection. The aim of the present study was to compare the blood metal ion levels in patients with Oxinium and CoCrMo modular femoral heads, as well as monoblock stainless steel Charnley prostheses at 10 years postoperatively. The 150 patients with osteoarthritis of the hip joint included in a randomized clinical trial were grouped according to femoral head material. One group (n = 30) had received the Charnley monoblock stainless steel stem (DePuy, UK). The other patients (n = 120) received a Spectron EF CoCrMo stem with either a 28 mm CoCrMo or Oxinium modular head (Smith & Nephew, USA). After 10 years, 38 patients had withdrawn, 19 deceased, 7 revised due to aseptic loosening and 5 revised due to infection. The 81 patients with median age of 79 years (70-91) were available for whole blood metal ion analysis. The levels of Co, Cr, Ni and Zr in the blood were generally low with all the head materials (medians <0.3 micrograms/L) and no statistical difference between the groups were found (p = .2-.8). Based on the low blood metal ion values in our study groups, no indication of severe trunnion corrosion in patients with CoCrMo heads was observed, neither was there any beneficial reduction in metal ion exposure with the Oxinium femoral heads.