Influence of Anticorrosive Surface Treatment of Steel Reinforcement Fibers on the Properties of Ultra-High Performance Cement Composite

The influence on the bond between the steel fiber and the matrix of the anticorrosive treatments of steel used for concrete reinforcement is not yet fully understood. The topic of steel fiber treatment was not also studied clearly in terms of brass removal before. This paper deals with how the brass on the surface of steel fibers behaves in the UHPC matrix and how it affects its properties. The steel fibers were firstly modified with a number of surface treatments to remove brass on their surface. Some of the treatments have never been tried before for this purpose. Secondly, the surface of the fibers was analyzed by SEM, EDS, XRF, and stereomicroscopy. Lastly, the properties of the composites were analyzed. It was found out that the majority of brass on the surface of the fibers could be removed by mixture of NH₃ and H₂O₂ with a ratio of 3:1 (v/v). It was also found out that the surface treatment slightly affects the mechanical properties, but it does that only by mechanical interlocking between the fiber and the matrix. No dissolution of the surface treatment was observed under the given conditions. According to the results, steel fibers without surface treatment should be used in UHPC if available.

Effect of Sulfate Ions on Galvanized Post-Tensioned Steel Corrosion in Alkaline Solutions and the Interaction with Other Ions

Zinc protection of galvanized steel is initially dissolved in alkaline solutions. However, a passive layer is formed over time which protects the steel from corrosion. The behavior of galvanized steel exposed to strong alkaline solutions (pH values of 12.7) with a fixed concentration of sulfate ions of 0.04 M is studied here. Electrochemical measurement techniques such as corrosion potential, linear polarization resistance and electrochemical impedance spectroscopy are used. Synergistic effects of sulfate ions are also studied together with other anions such as chloride Cl− or bicarbonate ion HCO3− and with other cations such as calcium Ca2+, ammonium NH4+ and magnesium Mg2+. The presence of sulfate ions can also depassivate the steel, leading to a corrosion current density of 0.3 µA/cm2 at the end of the test. The presence of other ions in the solution increases this effect. The increase in corrosion current density caused by cations and anions corresponds to the following orders (greater to lesser influence): NH4+ > Ca2+ > Mg2+ and HCO3− > Cl− > SO42−.

Kinetics of Zinc Corrosion in Concrete as a Function of Water and Oxygen Availability

This paper studies the effect of water as an oxidation agent and also of oxygen on zinc corrosion kinetics in active state in concrete, using high-sensitivity electrical resistance sensors. It was proven that zinc corrosion in active state is strongly affected by the presence of water at its surface. Zinc corrosion in real concrete in the absence of water can be misinterpreted as salt passivity. The presence of oxygen results in an increase of zinc corrosion rate, however at pH 12.6, passivity can occur. It was verified that corrosion products consisting primarily of Ca[Zn(OH)₃]₂·2H₂O cannot effectively passivate zinc surface in concrete, even after 1800 h of exposure and zinc, or hot-dip galvanized steel can corrode at an unacceptable corrosion rate (more than 4 µm·a⁻¹).