Profound Interfacial Effects in CoFe2O4/Fe3O4 and Fe3O4/CoFe2O4 Core/Shell Nanoparticles

Assessing the Heat Generation and Self-Heating Mechanism of Superparamagnetic Fe3O4 Nanoparticles for Magnetic Hyperthermia Application: The Effects of Concentration, Frequency, and Magnetic Field

Magnetite nanoparticles (MNPs) exhibit favorable heating responses under magnetic excitation, which makes them particularly suited for various hyperthermia applications. Herein, we report the detailed self-heating mechanisms of MNPs prepared via the Ko-precipitation Hydrolytic Basic (KHB) methodology. The as-prepared MNPs were fully characterized using various spectroscopic techniques including transmission electron microscopy (TEM), dynamic light scattering (DLS), X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), and vibrating sample magnetometry (VSM). MNPs exhibited stable 15 nm quasi-spherical small-sized particles, pure crystalline cubic Fe₃O₄ phases, high saturation magnetizations (Ms = ~40 emu·g^-1), and superparamagnetic behavior. In response to alternating magnetic fields (AMFs), these MNPs displayed excellent self-heating efficiencies with distinctive heating responses, even when minimal doses of MNPs were used. Heating efficacies and specific absorption rate (SAR) values as functions of concentration, frequency, and amplitude were systematically investigated. Remarkably, within only a few minutes, MNPs (2.5 mg/mL) showed a rapid dissipation of heat energy, giving a maximum intrinsic loss power (ILP) of 4.29 nHm²/kg and a SAR of 261 W/g. Hyperthermia temperatures were rapidly reached in as early as 3 min and could rise up to 80 °C. In addition, Rietveld refinement, Langevin, and linear response theory (LRT) models were studied to further assess the magnetic and heating mechanisms. The LRT model was used to determine the Néel relaxation time (τ_R = 5.41 × 10^-7 s), which was compared to the Brownian relation time value (τ_B = 11 × 10^-7 s), showing that both mechanisms are responsible for heat dissipated by the MNPs. Finally, the cytotoxicity assay was conducted on aqueous dispersions of MNPs, indicating their biocompatibility and low toxicity. Our results strongly suggest that the as-prepared Fe₃O₄ MNPs are promising vehicles for potential magnetically triggered biomedical hyperthermia applications.

Hyperthermia of Magnetically Soft-Soft Core-Shell Ferrite Nanoparticles

Magnetically soft-soft MnFe₂O₄-Fe₃O₄ core-shell nanoparticles were synthesized through a seed-mediated method using the organometallic decomposition of metal acetyl acetonates. Two sets of core-shell nanoparticles (S1 and S2) of similar core sizes of 5.0 nm and different shell thicknesses (4.1 nm for S1 and 5.7 nm for S2) were obtained by changing the number of nucleating sites. Magnetic measurements were conducted on the nanoparticles at low and room temperatures to study the shell thickness and temperature dependence of the magnetic properties. Interestingly, both core-shell nanoparticles showed similar saturation magnetization, revealing the ineffective role of the shell thickness. In addition, the coercivity in both samples displayed similar temperature dependencies and magnitudes. Signatures of spin glass (SG) like behavior were observed from the field-cooled temperature-dependent magnetization measurements. It was suggested to be due to interface spin freezing. We observed a slight and non-monotonic temperature-dependent exchange bias in both samples with slightly higher values for S2. The effective magnetic anisotropy constant was calculated to be slightly larger in S2 than that in S1. The magnetothermal efficiency of the chitosan-coated nanoparticles was determined by measuring the specific absorption rate (SAR) under an alternating magnetic field (AMF) at 200-350 G field strengths and frequencies (495.25-167.30 kHz). The S2 nanoparticles displayed larger SAR values than the S1 nanoparticles at all field parameters. A maximum SAR value of 356.5 W/g was obtained for S2 at 495.25 kHz and 350 G for the 1 mg/mL nanoparticle concentration of ferrogel. We attributed this behavior to the larger interface SG regions in S2, which mediated the interaction between the core and shell and thus provided indirect exchange coupling between the core and shell phases. The SAR values of the core-shell nanoparticles roughly agreed with the predictions of the linear response theory. The concentration of the nanoparticles was found to affect heat conversion to a great extent. The in vitro treatment of the MDA-MB-231 human breast cancer cell line and HT-29 human colorectal cancer cell was conducted at selected frequencies and field strengths to evaluate the efficiency of the nanoparticles in killing cancer cells. The cellular cytotoxicity was estimated using flow cytometry and an MTT assay at 0 and 24 h after treatment with the AMF. The cells subjected to a 45 min treatment of the AMF (384.50 kHz and 350 G) showed a remarkable decrease in cell viability. The enhanced SAR values of the core-shell nanoparticles compared to the seeds with the most enhancement in S2 is an indication of the potential for tailoring nanoparticle structures and hence their magnetic properties for effective heat generation.

Structural, magnetic and hyperthermia properties and their correlation in cobalt-doped magnetite nanoparticles

Cobalt doped magnetite nanoparticles (Co_xFe_3−xO₄ NPs) are investigated extensively because of their potential hyperthermia application. However, the complex interrelation among chemical compositions and particle size means their correlation with the magnetic and heating properties is not trivial to predict. Here, we prepared Co_xFe_3−xO₄ NPs (0 ≤ x ≤ 1) to investigate the effects of cobalt content and particle size on their magnetic and heating properties. A detailed analysis of the structural features indicated the similarity between the crystallite and particle sizes as well as their non-monotonic change with the increase of Co content. Magnetic measurements for the Co_xFe_3−xO₄ NPs (0 ≤ x ≤ 1) showed that the blocking temperature, the saturation magnetization, the coercivity, and the anisotropy constant followed a similar trend with a maximum at x = 0.7. Moreover, ⁵⁷Fe Mössbauer spectroscopy adequately explained the magnetic behaviour, the anisotropy constant, and saturation magnetization of low Co content samples. Finally, our study shows that the relaxation loss is a primary contributor to the SAR in Co_xFe_3−xO₄ NPs with low Co contents as well as their potential application in magnetic hyperthermia.

The interrelation among chemical compositions, structure, and heating properties of cobalt doped magnetite nanoparticles (Co_xFe_3−xO₄ NPs) for their potential hyperthermia application.

Interplay between inter- and intraparticle interactions in bi-magnetic core/shell nanoparticles

The synthesis strategy and magnetic characterisation of two systems consisting of nanoparticles with core/shell morphology are presented: an assembly of hard/soft nanoparticles with cores consisting of magnetically hard cobalt ferrite covered by a magnetically soft nickel ferrite shell, and the inverse system of almost the same size and shape. We have successfully designed these nanoparticle systems by gradually varying the magnetic anisotropy resulting in this way in the modulation of the magnetic dipolar interactions between particles. Both nanoparticle systems exhibit high saturation magnetisation and display superparamagnetic behaviour at room temperature. We have shown strong exchange coupling at the core/shell interface of these nanoparticles systems which was also confirmed by mesoscopic modelling. Our results demonstrate the possibility of modulating magnetic anisotropy not only by chemical composition but also by adopting the proper nano-architecture.