Steam stable mesoporous silica MCM-41 stabilized by trace amounts of Al

Evaluation of low and ultralow Al content (Si/Al between 50 and 412) aluminosilicate Al-MCM-41 materials synthesized via three contrasting alumination routes, namely, direct mixed-gel synthesis, post-synthesis wet grafting, and post-synthesis dry grafting, indicates that trace amounts of Al introduced via dry grafting can stabilize mesoporous silica MCM-41 to steaming at 900 °C for 4 h. It was found that trace amounts of Al (Si/Al > 400) introduced via so-called dry grafting of Al stabilize the virtually purely siliceous MCM-41 to steaming, whereas Al incorporated via other methods that involve aqueous media such as direct mixed gel synthesis or wet grafting of Al offer only limited protection at low Al content. It is particularly remarkable that a post-synthesis dry grafted Al-MCM-41 material possessing trace amounts of Al (i.e., Si/Al ratio of 412) and surface area and pore volume of 1112 m(2)/g and 1.20 cm(3)/g, respectively, retains 90% (998 m(2)/g) of the surface area and 85% (1.03 cm(3)/g) of the pore volume after exposure to steaming at 900 °C for 4 h. Under similar steam treatment conditions, the mesostructure of pure silica Si-MCM-41 is virtually destroyed and undergoes a 93% reduction in surface area (958 m(2)/g to 69 m(2)/g) and 88% decrease in pore volume (0.97 cm(3)/g to 0.12 cm(3)/g). The steam stable ultralow (i.e., trace) Al containing MCM-41 materials is found to be virtually similar to mesoporous pure silica Si-MCM-41 with hardly any detectable acidity. The improvement in steam stability arises from not only the presence of trace amounts of Al, but also from an apparent increase in the level of silica condensation that is specific to dry grafted alluminosilicate MCM-41 materials. The more highly condensed framework has fewer silanol groups and therefore is more resistant to hydrolysis under steaming conditions.

CO2 adsorption over Si-MCM-41 materials having basic sites created by postmodification with La2O3

Moderate basic sites could be created onto mesoporous Si-MCM-41 materials by postsynthesis modification with highly dispersed La2O3. The La2O3-modified MCM-41 materials (designated here as LaM) have been characterized by Fourier transform infrared spectroscopy, temperature-programmed desorption, X-ray photoelectron spectroscopy, X-ray diffraction (XRD), and N2 adsorption/desorption and have been tested as model adsorbents for CO2 adsorption. XRD and N2 adsorption results showed that all LaM materials still maintained their uniform hexagonal mesoporous structure even after postsynthesis modification with La2O3 loading up to 20 wt %. Although the surface area, pore size, and pore volume of LaM materials decreased with increasing La2O3 loading, their capacity for CO2 storage could be significantly improved when La2O3 loading was increased from 0 to 10 wt %. Unidentate and bidentate carbonates have been identified by in situ FTIR as the two types of CO2 species adsorbed on LaM surface. The LaM material also possesses good thermal stability, allowing the model adsorbent to be regenerated at high temperature and recyclable.