Electrospun Fiber - Hydrogel Composites for Nucleus Pulposus Tissue Engineering

A review on gradient hydrogel/fiber scaffolds for osteochondral regeneration

Osteochondral tissue regeneration is a complicated field due to the distinct properties and healing potential of osseous and chondral phases. In a natural osteochondral region, the composition, mechanics, and structure vary smoothly from bony to cartilaginous phase. Therefore, a homogeneous scaffold cannot satisfy the complexity of the osteochondral matrix. In essence, a natural extracellular matrix is composed of fibrous proteins elongated into a gelatinous background. A hydrogel/fiber scaffold possessing gradient in both phases would be of the utmost interest to imitate tissue arrangement of a native osteochondral interface. However, there are limited research works that exploit hydrogel/fiber scaffolds for osteochondral restoration. In the present review, currently used fibrous or gelatinous scaffolds for osteochondral damages are discussed. Moreover, superiority of using gradient hydrogel/fiber composites for osteochondral regeneration and practical approaches to develop those scaffolds is debated.

Gelatin nanofiber-reinforced alginate gel scaffolds for corneal tissue engineering

A severe shortage of donor cornea is now an international crisis in public health. Substitutes for donor tissue need to be developed to meet the increasing demand for corneal transplantation. Current attempts in designing scaffolds for corneal tissue regeneration involve utilization of expensive materials. Yet, these corneal scaffolds still lack the highly-organized fibrous structure that functions as a load-bearing component in the native tissue. This work shows that transparent nanofiber-reinforced hydrogels could be developed from cheap, non-immunogenic and readily available natural polymers to mimic the cornea's microstructure. Electrospinning was employed to produce gelatin nanofibers, which were then infiltrated with alginate hydrogels. Introducing electrospun nanofibers into hydrogels improved their mechanical properties by nearly one order of magnitude, yielding mechanically robust composites. Such nanofiber-reinforced hydrogels could serve as alternatives to donor tissue for corneal transplantation.

Mechanical behaviour of electrospun fibre-reinforced hydrogels

Mechanically robust and biomimicking scaffolds are needed for structural engineering of tissues such as the intervertebral disc, which are prone to failure and incapable of natural healing. Here, the formation of thick, randomly aligned polycaprolactone electrospun fibre structures infiltrated with alginate is reported. The composites are characterised using both indentation and tensile testing and demonstrate substantially different tensile and compressive moduli. The composites are mechanically robust and exhibit large strains-to-failure, exhibiting toughening mechanisms observed in other composite material systems. The method presented here provides a way to create large-scale biomimetic scaffolds that more closely mimic the composite structure of natural tissue, with tuneable tensile and compressive properties via the fibre and matrix phases, respectively.

Composite electrospun gelatin fiber-alginate gel scaffolds for mechanically robust tissue engineered cornea

A severe shortage of good quality donor cornea is now an international crisis in public health. Alternatives for donor tissue need to be urgently developed to meet the increasing demand for corneal transplantation. Hydrogels have been widely used as scaffolds for corneal tissue regeneration due to their large water content, similar to that of native tissue. However, these hydrogel scaffolds lack the fibrous structure that functions as a load-bearing component in the native tissue, resulting in poor mechanical performance. This work shows that mechanical properties of compliant hydrogels can be substantially enhanced with electrospun nanofiber reinforcement. Electrospun gelatin nanofibers were infiltrated with alginate hydrogels, yielding transparent fiber-reinforced hydrogels. Without prior crosslinking, electrospun gelatin nanofibers improved the tensile elastic modulus of the hydrogels from 78±19 kPa to 450±100 kPa. Stiffer hydrogels, with elastic modulus of 820±210 kPa, were obtained by crosslinking the gelatin fibers with carbodiimide hydrochloride in ethanol before the infiltration process, but at the expense of transparency. The developed fiber-reinforced hydrogels show great promise as mechanically robust scaffolds for corneal tissue engineering applications.