Cytotoxicity and bioactive potential of new root repair materials for use with BMP-2 transfected human osteoblast cells

Physicochemical properties and antibiofilm activity of mineral trioxide aggregate associated with farnesol

This study assessed the physicochemical and antibiofilm properties of white mineral trioxide aggregate (MTA) associated with 1 or 2% of farnesol. Setting time was evaluated based on ISO 6876/2012. Radiopacity was evaluated by radiographic analysis. pH was assessed after time intervals of 1, 3, 7, 14, 21, and 28 days. Solubility (% mass loss) and volumetric change (by micro-CT) of the cements were evaluated after immersion in distilled water. The presence of voids inside the materials was assessed by using micro-CT. Antibiofilm activity against Enterococcus faecalis was evaluated by crystal violet assay and the modified direct contact test performed with biofilm previously formed on bovine root dentin for 14 days. Data were submitted to ANOVA/Tukey tests with 5% significance level. The incorporation of farnesol into MTA increased its setting time, but decreased its solubility at 30 days and its volumetric loss in all periods (p < 0.05). Radiopacity and solubility after 7 days were similar among the materials (p > 0.05). The association of farnesol showed the highest pH value after 1 and 3 days (p < 0.05). The association of farnesol with MTA promoted a decrease in the presence of voids, and increased the antimicrobial activity on biofilm biomass of E. faecalis (p < 0.05). In conclusion, the addition of farnesol can be suggested to improve the antimicrobial properties and the consistency of MTA.

The osteoinductive potential of different root-filling materials in a rat femur model

In pediatric dentistry, the enduring success of root-end filling materials employed for the establishment of apical plugs in immature teeth undergoing endodontic intervention is contingent upon their possessing a robust osteoinductive capacity. Hence, the primary objective of this study was to histologically assess the osteoinductive potential of four distinct dental materials, specifically recommended for retrograde filling applications, utilizing an animal hard tissue model. Within the designed experimental model, two bone defects measuring 2 mm in diameter and 2 mm in depth were created in both femurs of a cohort comprising 21 male Wistar albino rats. The first defect in the right femur was left blank as the control group, and Neo MTA Plus was placed in the second defect. The EndoSequence BCRRM Fast Set Putty was placed in the first of the defects on the left femur, and Endo Repair was placed in the second defect. Subjects were sacrificed after 7, 14, and 28 days of follow-up, and sections were examined to assess the degree of inflammation, connective tissue formation, and new bone formation. The data were statistically evaluated with Kruskal‒Wallis and post hoc Dunn's tests using SPSS 12 software. The bone healing levels of the Neo MTA Plus group were significantly higher than those of the other groups in all periods (p < 0.05). Bone organization in all groups decreased over time, and fibrous tissue was enriched. The results of this study demonstrate that NeoMta Plus has superior osteoinductive properties compared to other materials but that EndoSequence and Endo Repair have the potential to be developed.