Effects of Calcium Hypochlorite and Sodium Hypochlorite, as Root Canal Irrigants, on the Bond Strength of Glass Fiber Posts Cemented with Self-Adhesive Resin Cement

Effect of sodium hypochlorite-based formulations on the adhesion interface after fiber post cementation

The study evaluated the persistence of residues, bond strength and tags formation of a cementation system after post-space irrigation with different sodium hypochlorite-based irrigants. The groups were divided according to the irrigation protocol (DW: distilled water; SHS: sodium hypochlorite solution; SHG: sodium hypochlorite gel; and, SHT: sodium hypochlorite with surfactant). Forty roots (n=10) were used to evaluate the persistence of residues by scanning electron microscopy. Other forty roots were used to the push-out bond strength test, failure mode and tag formation analyses. Non-parametric data were submitted to Kruskal Wallis and Dunn tests, while parametric data were evaluated by one-way ANOVA. No difference was observed in the persistence of residues. DW showed the highest bond strength and tag formation. Type 2 failure mode was the most frequent in the experimental groups. Compared to control, SHT showed the best performance, since less negative effects on adhesive interface was observed.

The Effect of Antioxidants on Dentin Bond Strength after Application of Common Endodontic Irrigants: A Systematic Review

The purpose of this systematic review was to evaluate how an antioxidant treatment would influence the immediate bond strength of dental adhesives to endodontically treated dentine. Scientific evidence was researched in five databases using selected descriptors. Two independent reviewers conducted the investigation and assessed the data and methodological quality of the studies. Inclusion and exclusion criteria were specified for article selection; only studies in English and published between 2001 and 2022 were evaluated. A total of 18 studies were selected and analysed. According to most studies, the irrigation procedure and substrate preparation in endodontic therapy may affect the immediate bond strength. Antioxidants can improve bond strength and adhesion following the use of the most frequently used irrigants in root canal treatments. Therefore, antioxidant treatment can be considered a proper technique to enhance the bond strength of endodontically treated teeth.

Collagen-depletion strategies in dentin as alternatives to the hybrid layer concept and their effect on bond strength: a systematic review

Strategies aiming to improve the longevity of resin-dentin adhesive interface developed so far have only been able to retard the problem. Different approaches are thus needed. The objective of this review was to determine whether the use of collagen-depletion strategies after acid-etching procedures may improve the bond strength of resin-based materials to dentin. A systematic review was planned following 2021 PRISMA statement guidelines, with a search strategy performed in five electronic databases: PubMed/Medline, Scopus, EMBASE, SciELO and IADR Abstract Archive (last search: 17/01/2022). Inclusion criteria encompassed studies which evaluated a collagen-depletion strategy in acid-etched human dentin and tensile/shear bond strength tests. Risk of bias assessment was carried out by two reviewers, working independently on an adapted five-domain risk of bias (RoB) checklist for laboratory studies. Results were synthesized qualitatively, as a meta-analysis was not possible due to limited number of studies and their RoB. A total of eight studies were eligible for inclusion in the systematic review after inclusion/exclusion criteria application. Out of these, two evaluated the effect of using NaOCl followed by an antioxidant, and the remaining six evaluated different enzymatic treatments (bromelain, chondroitinase ABC, papain, and trypsin). None of the studies reported a decrease of bond strength when a collagen-depletion strategy was used, in comparison to traditional hybrid layers (control). All enzymatic treatment studies which respected the inclusion criteria improved the bond strength to dentin. Some specific collagen-depletion strategies seem to play a favorable role in improving immediate bond strengths to dentin. Further research with sound methodology is required to consolidate these findings, since limitations in RoB and a low number of studies were found. The assessment of further proteolytic agents and long-term outcomes is also required.

Bond strength and failure mode of glass fiber posts with different surface treatments prior to silanization: An in vitro comparative study

Aim

The use of chemical agents in the surface treatment of glass fiber posts can improve their bond strength to the root canal. The aim of this study was to assess the bond strength and failure mode of glass fiber posts that received different surface treatments prior to silanization.

Materials and Methods

In this cross-sectional and in vitro experimental study, 50 human lower premolar roots were randomly divided into five groups and subsequently prepared to receive the cementation of a fiberglass post prior to silanization. They were distributed as group 1 (with 24% hydrogen peroxide), group 2 (with 37% phosphoric acid), group 3 (with 1.23% acidulated phosphate fluoride for 2 minutes), group 4 (with 1.23% acidulated phosphate fluoride for 6 minutes), and group 5 (without pretreatment). After cementation, the roots were sectioned into two discs for each cervical, middle, and apical region. Bond strength was assessed using the push out technique. Adhesive, mixed, and cohesive failure modes were also assessed. For data analysis, ANOVA and Tukey's post hoc tests were used, as well as Pearson's chi-square test. A significance of P < 0.05 was considered in all statistical analyses.

Results

When comparing the bond strength of root regions, significant differences were obtained in groups pretreated with phosphoric acid (P = 0.018) and acidulated phosphate fluoride for 2 and 6 minutes (P = 0.001 and P = 0.000, respectively). Furthermore, significant differences were obtained between posts treated only with silane and those that received phosphoric acid pretreatment (P = 0.006) and acidulated phosphate fluoride for 6 minutes (P = 0.001). Significant association of mixed failure mode was observed with hydrogen peroxide (P = 0.014) and phosphoric acid (P = 0.006) pretreatments. Cohesive failure was significantly associated with acidulated phosphate fluoride pretreatment for 2 minutes (P = 0.032) and with posts that did not receive treatment prior to silanization (P = 0.000).

Conclusion

Posts treated only with silane and pretreated with hydrogen peroxide and acidulated phosphate fluoride for 2 minutes presented significantly higher bond strength with respect to those pretreated with phosphoric acid and acidulated phosphate fluoride for 6 minutes. However, acidulated phosphate fluoride for 2 minutes and silane were associated with a better bonding type.