[Factors affecting the setting time of zinc oxide-eugenol impression materials--the influence of humidity and temperature to the reaction velocity]

An in vitro study of a custom-made device for thermoregulation of the mixing slab on the setting properties of zinc oxide eugenol impression paste

Aim

The present study was aimed to investigate the functional relationship between the mixing temperature and properties of a commercially available zinc oxide eugenol impression paste (ZnOE paste).

Settings and Design

In-vitro study.

Materials and Methods

A custom-made simulated mixing device was indigenously designed to maintain different mixing temperatures, simulating cold, ambient, and hot weather. A commercially available ZnOE paste was mixed according to the manufacturer's instructions in the simulated mixing device at the temperatures ranging from 10°C to 50°C. Initial setting time and consistency were measured according to A. D. A. Specification No. 16 (n = 8). A stainless-steel die having 25, 50, and 75 μm lines was used for surface detail reproduction. Detail reproduction of the stone casts of the impressions was evaluated with a stereomicroscope at 30 magnification (n = 8). The shear bond strength of ZnOE paste to self-cure acrylic tray resin was measured by using the UTM at a crosshead speed of 0.5 mm/min (n = 8).

Statistical Analysis Used

Data were analyzed by using one-way analysis of variance (ANOVA) and Tukey's post hoc tests at a confidence interval of 95% (alpha =0.05).

Results

Initial setting time, consistency, and detail reproduction of the ZnOE paste were affected by the mixing temperature (P < 0.001). Mixing ZnOE paste at a lower temperature of 10°C and higher temperatures of 40°C and 50°C resulted in shorter initial setting time, thicker consistency, and poor detail reproduction. However, no significant difference was obtained in the shear bond strength among the different mixing temperatures evaluated (P > 0.05).

Conclusion

Based on this in vitro study, it is advisable to perform the manipulation of ZnOE paste at a clinical/laboratory temperature of 30°C for optimum performance. The simulated mixing device used in this study can be an alternative for extreme climatic conditions.

Antimicrobial and physicochemical characterization of endodontic sealers after exposure to chlorhexidine digluconate

OBJECTIVES

Assess the antibacterial, physical and chemical properties of AH Plus, BioRoot RCS and Pulp Canal Sealer (PCS) in contact with 2% chlorhexidine digluconate (CHX) used as final irrigant prior to root canal obturation.

METHODS

The antimicrobial properties were investigated by direct contact tests for planktonic and biofilm growth of E. faecalis, S. mutans, S.epidermidis and S.aureus in vitro. The setting time, wettability, microhardness and surface roughness were also assessed. The sealers were studied in no contact, 1-minute (short-term) and continuous contact (long-term) with CHX. Chemical characterization of sealers was performed by scanning electron microscopy, X-ray diffraction analysis and Fourier-transform infrared spectroscopy after CHX or saline used as the last irrigant in an ex vivo tooth model and in endo training blocks.

RESULTS

CHX increased the antibacterial activity of all the sealers investigated against planktonic bacteria and biofilms with PCS exerting the highest antimicrobial activity with and without the presence of CHX. The setting of AH Plus and BioRoot RCS was retarded, while for PCS accelerated in the presence of CHX. AH Plus and PCS were more hydrophilic after contact with CHX, whilst BioRoot RCS was hydrophobic in a time-dependent manner. The microhardness of sealers was compromised and the surface roughness increased after CHX exposure for AH Plus and BioRoot RCS, and decreased for PCS. CHX did not affect the sealers' chemistry, but PCS that exhibited two extra phases.

SIGNIFICANCE

CHX improved the antibacterial efficacy of endodontic sealers but further evidence is needed to confirm its suitability as a final irrigant prior to root canal obturation.

To study the flow property of seven commercially available zinc oxide eugenol impression material at various time intervals after mixing

Aims and objective of the study was to evaluate the flow property of seven commercially available zinc oxide eugenol impression materials at various time intervals, after mixing 49 samples (seven groups) were fabricated for flow property of the material. The sample were fabricated as equal length of base and accelerator paste of the test materials was taken on the glass slab and mixed with a rigid stainless steel spatula as per manufacturers recommendation till the homogenous mix was obtained. The mix material was loaded in glass syringe and 0.5 ml material was injected on a cellophane sheet placed on marked glass plate. A cellophane sheet and glass plate 70 and 500 g weight was carefully placed on freshly dispensed zinc oxide eugenol impression paste sequentially. The diameter of the mix was noted after 30 s and 1 min of load application and also after the final set of material. The diameter gives the flow of material. The samples were stored at the room temperature. The data of the flow property was analyzed with analysis of variance, Post hoc test and t test. The flow of the zinc oxide eugenol impression paste after 30 s, 1 min and final set of load application for Group A to Group G was noted. Maximum flow was seen for Group G zinc oxide eugenol impression material followed by Group F, D, E, B, C and A in descending order respectively after 30 s, where as the flow property changed after 1 min in the sequence of maximum for Group G followed by Group E, D, B, A, C, and F. Lastly after final set of the impression material the flow maximum for Group G followed by Group E, D, C, F, A and B in descending order. Based on statistical analysis of the results and within in the limitations of this in-vitro study, the following conclusions were drawn that; the flow of zinc oxide eugenol impression material after 30 s, 1 min and that after the final set was maximum for P.S.P. (Group G) and the flow for PYREX (Group A) was minimum.