Effects of White Chicken Eggshell Powder on Compressive Strength, Water Solubility, and Setting Time of Calcium-Enriched Mixture

Introduction

The present study aimed to evaluate the effects of adding chicken eggshell powder (CESP) to calcium-enriched mixture (CEM) cement on its compressive strength (CS), solubility, and setting time.

Materials and Methods

In this study, CESP was added at weight percentages of 3% and 5% to the powder component of the CEM cement. To measure the CS, a total of 36 samples (height, 6 mm; diameter, 4 mm) were tested in a universal testing machine. The setting time was assessed for 18 disk-shaped samples (diameter, 10 mm; height, 1 mm). Additionally, solubility test was performed on 18 samples (diameter, 8 mm; height, 1 mm) after 24 hours, 72 hours, seven days, and 14 days under dehydration conditions by calculating the weight changes; the results were then subjected to a normality test. Next, for the comparison of different test groups, parametric ANOVA test and post-hoc Tukey's multiple comparison test were performed at a significance level of 0.05.

Results

The addition of 5% CESP to the CEM cement significantly reduced its setting time and water solubility (P=0.02 and P=0.01, respectively). Moreover, it significantly increased the CS over a 21-day period (P<0.001). Additionally, the addition of 3% CESP also resulted in a significant increase in CS (P<0.001). While 3% CESP reduced setting time and water solubility, the difference was not statistically significant.

Conclusion

The findings suggest that the addition of 5% CESP to CEM cement has the potential to improve its sealing ability, durability, and ability to withstand chewing forces in endodontic treatments. These results highlight the relevance of CESP as an additive for cement modifications and indicate its potential clinical implications.

Primary tooth pulpectomy overfilling by different placement techniques: A systematic review and meta-analysis

Background. This study was conducted to investigate root canal overfilling with different material placement techniques in primary teeth. Methods. A systematic search was undertaken by searching PubMed/MEDLINE and Scopus for English language peer-reviewed articles published until February 2018 that reported primary tooth pulpectomy overfilling. Two reviewers independently screened and identified studies in terms of the selection criteria and independently collected the data using a specially designed data extraction form. The overfilling rate was the primary summary measure. The weighted pooled overfilling rates were estimated by random-effects meta-analysis. Results. Twenty clinical and four in vitro studies met the eligibility criteria. In the clinical studies, the pooled overfilling rate for zinc oxide-eugenol (ZOE) was 23.3% with a lentulo spiral mounted on a handpiece, 22.7% with a hand-held lentulo spiral, and 17% with a plugger. The pooled overfilling rate for calcium hydroxide-based materials was 16.7% with a lentulo spiral mounted on a handpiece, 14.7% with a hand-held lentulo spiral, 19.6% with a syringe, and 25.7% with a plugger. In the in vitro studies, neither individual overfilling rates nor two-by-two comparisons were subjected to meta-analysis because of an inadequate number of studies. Conclusion. The lowest overfilling rate in the clinical studies was related to plugger and handheld lentulo spiral techniques for ZOE and calcium hydroxide-based materials, respectively.