Effect of Incorporation of Zeolite Containing Silver-Zinc Nanoparticles into Mineral Trioxide Aggregate on Odontogenic Activity of Human Dental Pulp Stem Cells

Effect of Silver Nanoparticles of Herbal Origin on the Compressive and Push-out Bond Strengths of Mineral Trioxide Aggregate

Introduction

The purpose of this in vitro study was to investigate the effect of incorporating silver nanoparticles (AgNPs) of herbal origin into mineral trioxide aggregate (MTA) on the push-out bond strength (PBS) and compressive strength (CS) in simulated furcal area perforations.

Materials and Methods

In this in vitro study, simulated furcal area perforations (1.3 mm in diameter and 2 mm in depth) were created in 40 extracted human lower molar teeth, which were divided into two groups (n=20): MTA alone and MTA combined with AgNPs (2% wt). Using a universal testing machine, PBS was evaluated by performing push-out tests, while CS was assessed using cylindrical specimens. The normal distribution of data was checked using the Kolmogorov-Smirnov test, and statistical analysis was performed using two-way ANOVA.

Results

The CS results showed no significant difference between the MTA group at 4 and 21 days (P=0.297), but a significant difference was observed in the nanosilver/MTA group (P=0.013). However, there was no significant difference in the push-out bond strength among the study groups (P>0.05).

Conclusion

The incorporation of herbal origin silver nanoparticles did not significantly affect the PBS or CS of MTA.

Modified Mineral Trioxide Aggregate—A Versatile Dental Material: An Insight on Applications and Newer Advancements

Mineral Trioxide Aggregate (MTA) has been a material of revolution in the field of dentistry since its introduction in the 1990s. It is being extensively used for perforation repairs, apexification, root-end filling, obturation, tooth fracture repair, regenerative procedures, apexogenesis, pulpotomies, and as a pulp-capping material because of its desired features such as biocompatibility, bioactivity, hydrophilicity, sealing ability, and low solubility. Even though its application is wide, it has its own drawbacks that prevent it from reaching its full potential as a comprehensive replacement material, including a long setting time, discoloration, mud-like consistency, and poor handling characteristics. MTA is a material of research interest currently, and many ongoing studies are still in process. In this review, the newer advancements of this versatile material by modification of its physical, chemical, and biological properties, such as change in its setting time, addressing the discoloration issue, inclusion of antimicrobial property, improved strength, regenerative ability, and biocompatibility will be discussed. Hence, it is important to have knowledge of the traditional and newer advancements of MTA to fulfill the shortcomings associated with the material.