Effect of storage temperature on sealing ability and solubility of white mineral trioxide aggregate

Storage Medium Affects the Surface Porosity of Dental Cements

INTRODUCTION

Calcium silicate-based cements physical properties is influenced by environmental changes.

AIM

Here, we intended to evaluate the effect of storage medium on surface porosity of root Mineral Trioxide Aggregate (MTA) and Biodentine cement.

MATERIALS AND METHODS

A total of 40 polyethylene tubes were selected and divided into two groups: Group A (MTA) and Group B (Biodentine). Each group was subdivided into two subgroups (n=10). In subgroups A1 and B1, tubes were transferred to Distilled Water (DW), while samples of subgroup A2 and B2 were transferred to Synthetic Tissue Fluid (STF) as storage medium and samples were stored for three days. All specimens were then placed in a desiccator for 24 hours and then subject to surface porosity evaluation by Scanning Electron Microscopy (SEM) at ×500, ×1000, ×2000 and ×5000 magnifications. The number and the surface porosities were determined by Image J analysis. Data were analyzed by ANOVA at level of significance of p<0.05.

RESULTS

The lowest surface porosity was observed in MTA samples stored in STF and the highest was in Biodentine samples stored in DW. Significant differences were noted between groups and subgroups of each group (p< 0.05). MTA samples stored in DW and STF showed significantly lower surface porosities compared to Biodentine samples (p < 0.05).

CONCLUSION

Storage medium can drastically affect the surface porosity of tested calcium silicate-based cements. However, MTA showed lower surface porosity compared to Biodentine cement, which can result in lower microleakage in applied area.

Solubility and bacterial sealing ability of MTA and root-end filling materials

Objective

To evaluate solubility and sealing ability of Mineral Trioxide Aggregate (MTA) and root-end filling materials.

Material and Methods

The materials evaluated were: MTA, Calcium Silicate Cement with zirconium oxide (CSC/ZrO₂), and zinc oxide/eugenol (ZOE). Solubility test was performed according to ANSI/ADA. The difference between initial and final mass of the materials was analyzed after immersion in distilled water for 7 and 30 days. Retrograde cavities in human teeth with single straight root canal were performed by using ultrasonic tip CVD 9.5107-8. The cavities were filled with the evaluated materials to evaluate sealing ability using the bacterial leakage test with Enterococcus faecalis. Bacterial leakage was evaluated every 24 hours for six weeks observing the turbidity of Brain Heart infusion (BHI) medium in contact with root apex. Data were submitted to ANOVA followed by Tukey tests (solubility), and Kruskal-Wallis and Dunn tests (sealing ability) at a 5% significance level.

Results

For the 7-day period, ZOE presented highest solubility when compared with the other groups (p<0.05). For the 30-day period, no difference was observed among the materials. Lower bacterial leakage was observed for MTA and CSC/ZrO₂, and both presented better results than ZOE (p<0.05).

Conclusion

MTA and CSC/ZrO₂ presented better bacterial sealing capacity, which may be related to lower initial solubility observed for these materials in relation to ZOE.

Effect of particle size on calcium release and elevation of pH of endodontic cements

BACKGROUND/AIM

Elevation of pH and calcium ion release are of great importance in antibacterial activity and the promotion of dental soft and hard tissue healing process. In this study, we evaluated the effect of particle size on the elevation of pH and the calcium ion release from calcium silicate-based dental cements.

MATERIAL AND METHODS

Twelve plastic tubes were divided into three groups, filled with white mineral trioxide aggregate (WMTA), WMTA plus 1% methylcellulose, and nano-modified WMTA (nano-WMTA), and placed inside flasks containing 10 ml of distilled water. The pH values were measured using a pH sensor 3, 24, 72, and 168 h after setting of the cements. The calcium ion release was measured using an atomic absorption spectrophotometer with same sample preparation method. Data were subjected to two-way analysis of variance (anova) followed by post hoc Tukey tests with significance level of P < 0.05.

RESULTS

Nano-WMTA showed significant pH elevation only after 24 h (P < 0.05) compared with WMTA, and after 3, 24, and 72 h compared with WMTA plus 1% methylcellulose (P < 0.05). Nano-WMTA showed significantly higher calcium ion release values compared to the other two groups (P < 0.05).

CONCLUSIONS

Nano-modification of WMTA remarkably increased the calcium ion release at all time intervals postsetting, which can significantly influence the osteogenic properties of human dental pulp cells and as a consequence enhance mineralized matrix nodule formation to achieve desirable clinical outcomes. However, the increase in pH values mainly occurred during the short time postsetting. Addition of 1% methylcellulose imposed a delay in elevation of pH and calcium ion release by WMTA.

Análise físico-química do MTA e do cimento Portland associado a quatro diferentes radiopacificadores

INTRODUÇÃO: O Mineral Trióxido Agregado (MTA) é composto por cimento Portland (CP) e um radiopacificador (óxido de bismuto).OBJETIVO: Avaliar tempo de presa, solubilidade, pH, liberação de íons Cálcio e radiopacidade do cimento Portland puro ou associado a quatro radiopacificadores (sulfato de bário, carbonato de bismuto, óxido de bismuto e iodofórmio), comparados ao MTA branco (Angelus, Londrina, Brasil).MATERIAL E MÉTODO: A proporção empregada CP/radiopacificador foi de 4:1 em peso, (80% de cimento Portland e 20% de radiopacificador). A especificação 57 da ADA foi usada para avaliação do tempo de presa. A solubilidade foi analisada segundo a especificação ISO 6876/2001. A avaliação do pH foi realizada com peagâmetro digital e a liberação de íons Ca++foi verificada por meio de espectrofotômetro de absorção atômica. A radiopacidade foi determinada em milímetros de alumínio (mm/Al). Os resultados foram submetidos aos testes de Análise de Variância e Tukey, nível de significância 5%.RESULTADO: O sulfato de bário não alterou o tempo de presa final do CP. Radiopacidade inferior ao mínimo recomendado pelas normas da ADA nº 57 e ISO 6876/2001 foi observada para CP e CP associado com sulfato de bário. O CP associado ao iodofórmio apresentou solubilidade acima dos 3% recomendados pela ISO 6876/2001. Todos os materiais proporcionaram alcalinização do meio e promoveram liberação de íons cálcio.CONCLUSÃO: Carbonato de bismuto ou óxido de bismuto proporcionaram tempo de presa inicial, solubilidade, pH, liberação de íons Cálcio e radiopacidade adequados quando associados ao CP.

Effects of various mixing techniques on physical properties of white mineral trioxide aggregate

INTRODUCTION

The aim of this study was to evaluate the effects of three different mixing techniques on surface microhardness, initial setting time, and phase formation of white mineral trioxide aggregate.

METHODS

Twenty-one cylindrical glass tubes were selected and divided into three groups of seven in each (n = 7). White mineral trioxide aggregate (WMTA) in groups A, B, and C were mixed by conventional, trituration, and ultrasonic techniques, respectively. Cements were mixed and packed into the glass tubes and incubated at 37°C for 3 days. After incubation, samples were subjected to microhardness evaluation, and four specimens from each group were prepared and observed under a scanning electron microscopy and X-ray diffraction. For setting time assessment, WMTA was mixed in three parts again, and Gilmore needle test was performed until the initial setting time of cement. Data were analyzed by one-way anova and post hoc Tukey's test.

RESULTS

Samples mixed by trituration technique significantly showed the highest microhardness (P < 0.001) and the lowest setting time, while the ultrasonically mixed specimens significantly revealed the highest setting time in comparison with other groups (P < 0.001). Samples mixed by trituration technique showed the highest uniformity in the bulk and highest amount of hydrated calcium silicate (CS) phases, while the lowest value was observed in ultrasonically mixed cements, which also showed the highest amount of anhydrated CS phases.

CONCLUSION

Trituration and conventional techniques were more suitable mixing methods for mineral trioxide aggregate in comparison with ultrasonic technique. Trituration resulted in better hydration and crystallization, which prevents clustering of powder and reduces voids and setting time of mixed cement.