Migration of acetyl-tributylcitrate from plastic film into poultry products during microwave cooking

Migration of di-(2-ethylhexylexyl)adipate plasticizer from food-grade polyvinyl chloride film into hard and soft cheeses

Food-grade polyvinyl chloride (PVC) film containing 28.3% di-(2-ethylhexylexyl)adipate (DEHA) plasticizer was used to wrap three different types of cheese (Kefalotyri, Edam, and Feta). Samples were split into two groups and stored at 5+/-0.5 degrees C. One group was analyzed for DEHA content at intervals between 1 and 240 h of contact (kinetic study), and a second group was cut into slices (1.2 mm thick) after 240 h of cheese/PVC contact and was analyzed for DEHA content (penetration study). The DEHA was determined by indirect gas chromatography. Statistically significant differences in migration of DEHA were observed between the cheese types. Migration of DEHA depended on contact time, fat, and moisture contents, and consistency of cheese samples. Equilibrium conditions were approached after approximately 100 h of contact for Edam and 150 h for Kefalotyri cheese. Equilibrium conditions were not reached for Feta cheese, even after 240 h of contact. After 240 h of contact under refrigeration, the migration of DEHA was approximately 345.4 mg/kg (18.9 mg/dm2) for Kefalotyri, 222.5 mg/kg (12.2 mg/dm2) for Edam, and 133.9 mg/kg (7.3 mg/dm2) for Feta. The loss of DEHA from the PVC film into the three cheese types was 37.8, 24.3, and 14.6%, respectively. These values, with the exception of Feta, were higher than the upper limit for global migration from plastic packaging materials into food and food stimulants set by the European Union (EU) (10 mg/dm2 or 60 mg/kg). After 240 h of cheese/film contact, DEHA was detected in the first three slices beneath the cheese surface (3.6 mm total depth) of Edam cheese and in the first two slices (2.4 mm total depth) of Kefalotryi and Feta cheeses. DEHA was not detected in subsequent layers. The effect of cheese rind on migration of DEHA was studied in Edam and Kefalotyri cheeses. The DEHA migration after 240 h into the first 1 mm beneath the surface of Kefalotyri cheese was 22.4 mg/kg, while DEHA was not detected in Edam cheese.

Effect of microwave heating on the migration of dioctyladipate and acetyltributylcitrate plasticizers from food-grade PVC and PVDC/PVC films into olive oil and water

Migration of dioctyladipate (DOA) and acetyltributylcitrate (ATBC) plasticizers from plasticized polyvinylchloride (PVC) and polyvinylidene chloride (PVDC)/PVC (Saran) films into both olive oil and distilled water during microwave heating has been studied. The plasticizer migrating into olive oil and water was determined using an indirect GC method after saponification of the ester-type plasticizer (DOA or ATBC) and subsequent collection of the alcohol component of the ester, namely: 2-ethyl-1-hexanol and 1-butanol, respectively. Migration was dependent on heating time, microwave power setting, the nature of the food simulant and the initial concentration of the plasticizer in the film. Migration of DOA into olive oil reached equilibrium after heating for 10 min at full power (604.6 mg DOA/l). Migration into distilled water was 74.1 mg/l after 8 min of microwave cooking at full power. The amount of ATBC migrating into olive oil reached equilibrium after heating for 10 min at full power (73.9 mg ATBC/l). Migration into distilled water was 4.1 mg/l after heating at full power for 8 min. Control samples containing olive oil gave DOA migration values which were significantly higher than the upper limit for global migration (60 mg/l) set by the European Community. It is proposed that PVC should not be used in direct contact with food in the microwave oven, while Saran may be used with caution in microwave heating and reheating applications, avoiding its direct contact with high fat foodstuffs.

Effect of gamma-radiation on migration behaviour of dioctyladipate and acetyltributylcitrate plasticizers from food-grade PVC and PVDC/PVC films into olive oil

Food-grade PVC and PVDC/PVC films containing 28.3% dioctyladipate (DOA) and 5.0% acetyltributylcitrate (ATBC) plasticizers, respectively, were brought into contact with olive oil and were irradiated with gamma-radiation [60Co] at doses equal to 4 kGy and 9 kGy corresponding to "cold pasteurization". Irradiation was carried out at 8-10 degrees C and samples were subsequently stored at 4-5 degrees C. Contaminated oil samples were analysed for DOA and ATBC at intervals between 7 h and 97 h of contact, using an indirect GC method. Identical nonirradiated (control) samples were also analysed for DOA and ATBC content. Results showed no statistically significant differences in migrated amounts of DOA and ATBC between irradiated and non-irradiated samples. Neither were differences observed between samples irradiated at 4 kGy and 9 kGy. This was supported by identical IR spectra recorded for irradiated and non-irradiated samples and leads to the conclusion that at such intermediate radiation doses (< or = 9 kGy) the migration characteristics of both PVC and PVDC/PVC films are not affected. The amount of DOA that migrated into olive oil was dependent on time, reaching equilibrium after approximately 47 h of contact (302.8 mg/l). The amount of ATBC that migrated into olive oil was non-detectable (< 1 mg/l) for all samples stored at 4-5 degrees C after 97 h. In non-irradiated samples (PVDC/PVC in contact with oil) stored at 20 degrees C, small amounts of migrated ATBC were determined (3.3 and 5.1 mg/l after 29 h 94 h of contact respectively).(ABSTRACT TRUNCATED AT 250 WORDS)

Migration from plasticized films into foods. 1. Migration of di-(2-ethylhexyl)adipate from PVC films during home-use and microwave cooking

Migration of di-(2-ethylhexyl)adipate (DEHA) into a diverse range of foods arising from the domestic use of plasticized PVC films has been determined using a stable isotope dilution GC/MS procedure. Aspects of home use reported in this study include the wrapping and covering of foods such as cheese, cooked meats, sandwiches, cakes, fresh fruit and vegetables; the use of films during food preparation such as marinading; covering during microwave reheating of previously prepared foods, and covering during microwave cooking. Contact between film and foods was for differing temperatures and times, representative of the range of conditions likely to be experienced in practice in the home. Migration increased with both the length of contact time and temperature of exposure, with the highest levels observed where there was a direct contact between the film and food, and where the latter had a high fat content on the contact surface. Highest levels of migration were observed for cheese, cooked meats, cakes and for microwave-cooked foods, whilst lower levels were observed for wrapping of unfilled sandwiches, fruit and vegetables (except avocado), and for food preparation including microwave reheating where there was covering of the food in a container but little or no direct contact.

Mutagenesis testing of acetyl-tributylcitrate and epoxidized soybean oil

Mutagenesis testing was conducted on two plasticizers commonly used in plastic wrap manufacture, acetyl-tributylcitrate and epoxidized soybean oil. There is no record of mutagenic testing using a bacterial screening method for these two compounds. The two plasticizers were screened using mutant strains of Salmonella typhimurium. The tests determined that they were not mutagenic.