Confined Growth of NiAl-Layered Double Hydroxide Nanoparticles Within Alginate Gel: Influence on Electrochemical Properties

Cellulose Nanofiber-Alginate Biotemplated Cobalt Composite Multifunctional Aerogels for Energy Storage Electrodes

Tunable porous composite materials to control metal and metal oxide functionalization, conductivity, pore structure, electrolyte mass transport, mechanical strength, specific surface area, and magneto-responsiveness are critical for a broad range of energy storage, catalysis, and sensing applications. Biotemplated transition metal composite aerogels present a materials approach to address this need. To demonstrate a solution-based synthesis method to develop cobalt and cobalt oxide aerogels for high surface area multifunctional energy storage electrodes, carboxymethyl cellulose nanofibers (CNF) and alginate biopolymers were mixed to form hydrogels to serve as biotemplates for cobalt nanoparticle formation via the chemical reduction of cobalt salt solutions. The CNF-alginate mixture forms a physically entangled, interpenetrating hydrogel, combining the properties of both biopolymers for monolith shape and pore size control and abundant carboxyl groups that bind metal ions to facilitate biotemplating. The CNF-alginate hydrogels were equilibrated in CaCl2 and CoCl2 salt solutions for hydrogel ionic crosslinking and the prepositioning of transition metal ions, respectively. The salt equilibrated hydrogels were chemically reduced with NaBH4, rinsed, solvent exchanged in ethanol, and supercritically dried with CO2 to form aerogels with a specific surface area of 228 m2/g. The resulting aerogels were pyrolyzed in N2 gas and thermally annealed in air to form Co and Co3O4 porous composite electrodes, respectively. The multifunctional composite aerogel's mechanical, magnetic, and electrochemical functionality was characterized. The coercivity and specific magnetic saturation of the pyrolyzed aerogels were 312 Oe and 114 emu/gCo, respectively. The elastic moduli of the supercritically dried, pyrolyzed, and thermally oxidized aerogels were 0.58, 1.1, and 14.3 MPa, respectively. The electrochemical testing of the pyrolyzed and thermally oxidized aerogels in 1 M KOH resulted in specific capacitances of 650 F/g and 349 F/g, respectively. The rapidly synthesized, low-cost, hydrogel-based synthesis for tunable transition metal multifunctional composite aerogels is envisioned for a wide range of porous metal electrodes to address energy storage, catalysis, and sensing applications.

Biocompatible MgFeCO3 Layered Double Hydroxide (LDH) for Bone Regeneration-Low-Temperature Processing through Cold Sintering and Freeze-Casting

Layered Double Hydroxides (LDHs) are inorganic compounds of relevance to various domains, where their surface reactivity and/or intercalation capacities can be advantageously exploited for the retention/release of ionic and molecular species. In this study, we have explored specifically the applicability in the field of bone regeneration of one LDH composition, denoted "MgFeCO₃", of which components are already present in vivo, so as to convey a biocompatibility character. The propensity to be used as a bone substitute depends, however, on their ability to allow the fabrication of 3D constructs able to be implanted in bone sites. In this work, we display two appealing approaches for the processing of MgFeCO₃ LDH particles to prepare (i) porous 3D scaffolds by freeze-casting, involving an alginate biopolymeric matrix, and (ii) pure MgFeCO₃ LDH monoliths by Spark Plasma Sintering (SPS) at low temperature. We then explored the capacity of such LDH particles or monoliths to interact quantitatively with molecular moieties/drugs in view of their local release. The experimental data were complemented by computational chemistry calculations (Monte Carlo) to examine in more detail the mineral-organic interactions at play. Finally, preliminary in vitro tests on osteoblastic MG63 cells confirmed the high biocompatible character of this LDH composition. It was confirmed that (i) thermodynamically metastable LDH could be successfully consolidated into a monolith through SPS, (ii) the LDH particles could be incorporated into a polymer matrix through freeze casting, and (iii) the LDH in the consolidated monolith could incorporate and release drug molecules in a controlled manner. In other words, our results indicate that the MgFeCO₃ LDH (pyroaurite structure) may be seen as a new promising compound for the setup of bone substitute biomaterials with tailorable drug delivery capacity, including for personalized medicine.

A Comparison of Nitrate Release from Zn/Al-, Mg/Al-, and Mg-Zn/Al Layered Double Hydroxides and Composite Beads: Utilization as Slow-Release Fertilizers

Nitrate-loaded Zn/Al, Mg/Al, and Mg-Zn/Al layered double hydroxides (LDHs) were synthesized using the coprecipitation method. The slow-release properties of LDHs were measured in powder form at various pH conditions. Sodium alginate was used to encapsulate Mg/Al LDH to produce composite beads (LB) to further slow down the release of nitrate ions. The prepared LDH samples and LB were characterized by X-ray diffraction, attenuated total reflectance Fourier transform infrared spectroscopy, thermogravimetric analysis, and inductively coupled plasma optical emission spectroscopy. The surface morphologies of LDHs and LB were obtained from scanning electron microscopy analysis. The slow-release properties of the materials were evaluated using a kinetic study of nitrate release in tap water, soil solution, as well as plant growth experiments using coriander (Coriandrum sativum). The nitrate release ability of LDHs and LB was compared with a soluble nitrate source. The plant growth experiments showed that all three LDHs were able to supply an adequate amount of nitrate to the plant similar to the soluble fertilizer while maintaining the availability of nitrate over extended periods. The ability of LDHs to increase soil pH was also demonstrated.

Layered double hydroxide-based nanomaterials for biomedical applications

Against the backdrop of increased public health awareness, inorganic nanomaterials have been widely explored as promising nanoagents for various kinds of biomedical applications. Layered double hydroxides (LDHs), with versatile physicochemical advantages including excellent biocompatibility, pH-sensitive biodegradability, highly tunable chemical composition and structure, and ease of composite formation with other materials, have shown great promise in biomedical applications. In this review, we comprehensively summarize the recent advances in LDH-based nanomaterials for biomedical applications. Firstly, the material categories and advantages of LDH-based nanomaterials are discussed. The preparation and surface modification of LDH-based nanomaterials, including pristine LDHs, LDH-based nanocomposites and LDH-derived nanomaterials, are then described. Thereafter, we systematically describe the great potential of LDHs in biomedical applications including drug/gene delivery, bioimaging diagnosis, cancer therapy, biosensing, tissue engineering, and anti-bacteria. Finally, on the basis of the current state of the art, we conclude with insights on the remaining challenges and future prospects in this rapidly emerging field.