Mechanism underlying the acceleration of pitting corrosion of B30 copper-nickel alloy by Pseudomonas aeruginosa

Sub-minimum inhibitory concentration of tetrakis(hydroxymethyl)phosphonium sulfate enhances biocorrosion of carbon steel by Pseudomonas aeruginosa

Biocide treatments are commonly employed to mitigate unwanted microbial activities in industrial water systems. This study illuminates the intriguing phenomenon wherein sub-minimum inhibitory concentration (sub-MIC) of tetrakis(hydroxymethyl)phosphonium sulfate (THPS), a frequently used biocide, stimulates the formation of biofilms by Pseudomonas aeruginosa, consequently intensifying the corrosion of carbon steel. Introducing 160 µg/ml THPS, constituting a sub-MIC level, into the culture medium resulted in a notable increase in biofilm thickness and corrosion rate, elevating them from 82 µm and 10 mpy to 97 µm and 18.7 mpy, respectively. Electrochemical impedance spectroscopy, Tafel polarization and linear polarization resistance measurements substantiated the extent of corrosion. Furthermore, the treated biofilm exhibited a heightened presence of extracellular polymeric substances, improved adherence to the metal surface, enhanced structural integrity, and an extended dispersal phase. Confocal laser scanning microscopy (CLSM) images revealed a greater abundance of viable sessile cells within the inner layers of the treated biofilm. These findings underscore the role of sub-MIC levels of biocides as a potential driving force for developing more corrosive biofilms on industrial materials, emphasizing the critical importance of precise biocide dosing.

The effect of Desulfovibrio caledoniensis and Pseudomonas aeruginosa on the corrosion behaviour of 70Cu-30Ni alloy

This work investigated the effect of Desulfovibrio caledoniensis (D. caledoniensis) and Pseudomonas aeruginosa (P. aeruginosa) on the microbiologically influenced corrosion (MIC) behaviour of 70Cu-30Ni alloy using surface analysis and electrochemical techniques. The results demonstrated that the mixed medium containing D. caledoniensis and P. aeruginosa further accelerated the MIC of 70Cu-30Ni alloy compared to the single species medium. The addition of exogenous pyocyanin (PYO) to the D. caledoniensis medium increased the maximum pit depth on 70Cu-30Ni alloy from 5.40 μm to 6.59 μm, and the corrosion current density (icorr) increased by one order of magnitude. From the perspective of bioenergetics and extracellular electron transfer (EET), the comprehensive MIC mechanism of 70Cu-30Ni alloy induced by D. caledoniensis and P. aeruginosa was proposed.

Study on mechanism underlying the acceleration of pitting corrosion of B30 copper-nickel alloy by sulfate-reducing bacteria in seawater

In this paper, the relationship between the pitting corrosion formation of B30 copper-nickel (CuNi) alloy and the metabolism of sulfate-reducing bacteria (SRB) was investigated. Combined with the influence of temperature during the actual operation of the cooling systems, the evolution law of the alloy passivation film was analyzed, and the mechanism of SRB promoting the accelerated development of B30 CuNi alloy pitting corrosion was revealed. The results show that SRB significantly promoted the pitting formation and development of B30 CuNi alloy. The maximum pitting depth was 3.9 μm in the sterile system and 15.3 μm with SRB, which was 3.9 times higher than that of sterile system. The loose porous Cu2S film formed by SRB metabolites and copper matrix was easily penetrated by corrosive anions, which promoted copper dissolution and led to pit nucleation. The sulfide adsorbed on the surface prevented or delayed the passivation of B30 CuNi alloy by blocking the adsorption site of O atom, and the corrosion nuclei continued to grow. The non-uniformity caused by the film peeling accelerated the longitudinal development of pitting corrosion, and the expansion and coalescence of adjacent pits caused the transverse development of pitting corrosion. Temperature had a certain influence on the SRB and the formation of B30 CuNi alloy passivation film. The passivation film was formed rapidly at 50 °C with poor quality and the passivation property of Cu2O film was weakened. With the increase of temperature, the pitting potential of sterile system negative shifted from 0.447 to 0.360 V (vs. SCE), while SRB system from 0.340 to 0.198 V (vs. SCE), and the pitting resistance decreased. The passivation film with defects and the Cu2S reduced the barrier efficiency of the film and accelerated the pitting corrosion of B30 CuNi alloy.

Mechanism of 5-chloro-2-methyl-4-isothiazolin-3-one (CMIT) in controlling microbial problems in aircraft fuel systems

This research investigated the potential use of 5-chloro-2-methyl-4-isothiazolin-3-one (CMIT) as a biocide in aircraft fuel systems, which is rarely studied due to the unique properties of such systems. The study assessed the effectiveness of CMIT against three microbial isolates using minimum inhibitory concentrations and bacteriostatic tests, and showed that CMIT had good activity against them. Electrochemical studies were conducted to determine the impact of CMIT on the 7B04 aluminum alloy, which demonstrated that CMIT acted as a cathodic inhibitor and exhibited certain levels of short-term and long-term corrosion inhibition effects at concentrations of 100 mg L^-1 and 60 mg L^-1, respectively. Additionally, the research provided insights into the mechanisms governing microbial problems by studying the reaction of CMIT with glutathione and sulfate. Overall, the study suggested that CMIT may be a useful biocide in aircraft fuel systems and provided important information on its efficacy and mechanism of action.