Effect of Pyrolysis Temperature on the Electrical Property and Photosensitivity of a PAN-PMMA Derived Carbon Fiber

Carbon-α-Fe2O3 Composite Active Material for High-Capacity Electrodes with High Mass Loading and Flat Current Collector for Quasi-Symmetric Supercapacitors

In this work, we report the synthesis of an active material for supercapacitors (SCs), namely α-Fe2O3/carbon composite (C-Fe2O3) made of elongated nanoparticles linearly connected into a worm-like morphology, by means of electrospinning followed by a calcination/carbonization process. The resulting active material powder can be directly processed in the form of slurry to produce SC electrodes with mass loadings higher than 1 mg cm−2 on practical flat current collectors, avoiding the need for bulky porous substrate, as often reported in the literature. In aqueous electrolyte (6 M KOH), the so-produced C-Fe2O3 electrodes display capacity as high as ~140 mAh g−1 at a scan rate of 2 mV s−1, while showing an optimal rate capability (capacity of 32.4 mAh g−1 at a scan rate of 400 mV s−1). Thanks to their poor catalytic activity towards water splitting reactions, the electrode can operate in a wide potential range (−1.6 V–0.3 V vs. Hg/HgO), enabling the realization of performant quasi-symmetric SCs based on electrodes with the same chemical composition (but different active material mass loadings), achieving energy density approaching 10 Wh kg−1 in aqueous electrolytes.

Porous Mixed-Metal Oxide Li-Ion Battery Electrodes by Shear-Induced Co-assembly of Precursors and Tailored Polymer Particles

Due to their various applications, metal oxides are of high interest for fundamental research and commercial usage. Per applications as catalysts or electrochemical devices, the tailored design of metal oxides featuring a high specific surface area and additional functionalities is of the utmost importance for the performance of the resulting materials. We report a new method for preparing free-standing films consisting of hierarchically porous metal oxides (titanium and niobium based) by combining emulsion polymerization and shear-induced monodisperse particle self-assembly in the presence of sol-gel precursors. After thermal treatment, the resulting porous materials can be used as electrodes in Li-ion batteries. The titanium and niobium sol-gel precursors were partially immobilized to the surface of organic core-interlayer particles featuring hydroxyl groups to obtain hybrid organic-inorganic particles through the melt-shear organization process. Free-standing particle-based films, in analogy to elastomeric opal films and colloidal crystals, can be prepared in a convenient one-step preparation process. After thermal treatment, ordered pores are obtained, while the pristine metal oxide precursor shell can be converted to the (mixed) metal oxide matrix. Heat treatment under CO₂ leads to mixed-TiNb oxide/carbon hybrid materials. The highly porous derivative structure enhances electrolyte permeation. When tested as Li-ion battery electrodes, it shows a specific capacity of 335 mAh·g^-1 at a rate of 10 mA·g^-1. After 1000 cycles at 250 mA·g^-1, the electrodes still provided a specific capacity of 191 mAh·g^-1.

Electrospun Polyacrylonitrile/Lignin/Poly(Ethylene Glycol)-Based Porous Activated Carbon Nanofiber for Removal of Nickel(II) Ion from Aqueous Solution

The issue of heavy metal contamination has caused a great deal of concern among water quality experts today, as it contributes to water pollution. Activated carbon nanofibers (ACNFs) showed a significant ability in removing heavy metals from the wastewater. In this study, polyacrylonitrile (PAN) was blended and electrospun with an abundant and inexpensive biopolymer, lignin and a water soluble polymer, poly(ethylene glycol) (PEG), by using an electrospinning technique to form nanofibers. The electrospun nanofibers were then investigated as a precursor for the production of porous ACNFs to study the removal of nickel(II) ions by adsorption technique. PEG was added to act as a porogen and to create the porous structure of carbon nanofibers (CNFs). CNFs were prepared by thermal treatment of the electrospun nanofibers and followed by activation of CNFs by thermal and acid treatment on CNFs. Attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) spectral analysis of the ACNFs showed a strong absorption peak of the C-O functional group, indicating the increase in the oxygenated compound. Field emission scanning electron microscopy (FESEM) images concluded that the ACNFs have more porous and compact fibers with a smaller fiber diameter of 263 ± 11 nm, while the CNFs are less compact and have slightly larger fiber diameter of 323 ± 6 nm. The adsorption study showed that the ACNFs possessed a much higher adsorption capacity of 18.09 mg/g compared with the CNFs, which the amount adsorbed was achieved only at 2.7 mg/g. The optimum adsorption conditions that gave the highest percentage of 60% for nickel(II) ions removal were 50 mg of adsorbent dosage, 100 ppm of nickel(II) solution, pH 3, and a contact time of 60 min. The study demonstrated that the fabrication of ACNFs from PAN/lignin/PEG electrospun nanofibers have potential as adsorbents for the removal of heavy metal contaminants.

Advances in Manufacturing Composite Carbon Nanofiber-Based Aerogels

This article provides an overview on manufacturing composite carbon nanofiber-based aerogels through freeze casting technology. As known, freeze casting is a relatively new manufacturing technique for generating highly porous structures. During the process, deep cooling is used first to rapidly solidify a well-dispersed slurry. Then, vacuum drying is conducted to sublimate the solvent. This allows the creation of highly porous materials. Although the freeze casting technique was initially developed for porous ceramics processing, it has found various applications, especially for making aerogels. Aerogels are highly porous materials with extremely high volume of free spaces, which contributes to the characteristics of high porosity, ultralight, large specific surface area, huge interface area, and in addition, super low thermal conductivity. Recently, carbon nanofiber aerogels have been studied to achieve exceptional properties of high stiffness, flame-retardant and thermal-insulating. The freeze casting technology has been reported for preparing carbon nanofiber composite aerogels for energy storage, energy conversion, water purification, catalysis, fire prevention etc. This review deals with freeze casting carbon nanofiber composite materials consisting of functional nanoparticles with exceptional properties. The content of this review article is organized as follows. The first part will introduce the general freeze casting manufacturing technology of aerogels with the emphasis on how to use the technology to make nanoparticle-containing composite carbon nanofiber aerogels. Then, modeling and characterization of the freeze cast particle-containing carbon nanofibers will be presented with an emphasis on modeling the thermal conductivity and electrical conductivity of the carbon nanofiber network aerogels. After that, the applications of the carbon nanofiber aerogels will be described. Examples of energy converters, supercapacitors, secondary battery electrodes, dye absorbents, sensors, and catalysts made from composite carbon nanofiber aerogels will be shown. Finally, the perspectives to future work will be presented.