Interplay of the Influence of Crosslinker Content and Model Drugs on the Phase Transition of Thermoresponsive PNiPAM-BIS Microgels

Swelling-Shrinking Behavior of a Hydrogel with a CO2-Switchable Volume Phase Transition Temperature

Macromolecules exhibit rich phase behavior that may be exploited for advanced material design. In particular, the volume phase transition in certain crosslinked hydrogels is a key property controlling the transition between a collapsed/dehydrated and a swollen/hydrated state, thereby regulating the release and absorption of water via a temperature change. In this work, a simple and tunable system exhibiting a carbon dioxide (CO2)-switchable volume phase transition is introduced, which displays isothermal swelling-shrinking behavior that is activated by addition and removal of CO2, respectively. Through systematic compositional studies, shifts in phase transition temperatures of up to 8.6 °C are measured upon CO2 exposure, which enables pronounced isothermal swelling in response to CO2, reaching up to a fivefold increase in mass. The shift in transition temperature and the extent of swelling are controlled by the hydrogel composition, thus enabling the transition temperature and swelling degree to be tuned a priori for a particular application. Controlled release experiments from these gels upon a CO2-induced phase transition suggest viability for drug delivery applications. It is anticipated that this work will motivate and expand efforts to exploit phase behavior for smart material development.

Leveraging novel innovative thermoresponsive polymers in microneedles for targeted intradermal deposition

Microneedles have garnered considerable attention over the years as a versatile pharmaceutical platform that could be leveraged to deliver drugs into and across the skin. In the current work, poly (N-isopropylacrylamide) (PNIPAm) is synthesized and characterized as a novel material for the development of a physiologically responsive microneedle-based drug delivery system. Typically, this polymer transitions reversibly between a swell state at lower temperatures and a more hydrophobic state at higher temperatures, enabling precise drug release. This study demonstrates that dissolving microneedles patches made from PNIPAm, incorporating BIS-PNIPAm, a crosslinked polymer variant, exhibit enhanced mechanical properties, evident from a smaller height reduction in microneedle (∼10 %). Although microneedles using PNIPAm alone were achievable, it displayed poor mechanical strength, requiring the inclusion of additional polymeric excipients like PVA to enhance mechanical properties. In addition, the incorporation of a thermoresponsive polymer did not have a significant (p > 0.05) impact on the insertion properties of the needles as all formulations inserted to a similar depth of 500 µm into ex vivo skin. Furthering this, the needles were loaded with a model payload, 1,1'-dioctadecyl-3,3,3',3'-tetramethylindodicarbocyanine perchlorate (DID) and the deposition of the cargo was monitored via multiphoton microscopy that showed that a deposit is formed at a depth of ≈200 µm. Also, it was revealed that crosslinked-PNIPAm (Bis-PNIPAm) formulations exhibited notable skin accumulationof the dye only after 4 h, independent of the excipient matrix used. This phenomenon was absent in non-crosslinked PNIPAm formulations, indicating a deposit formation in Bis-PNIPAm microneedle formulation. Collectively, this proof-of-concept study has advanced our understanding on the possibility to use PNIPAm for dissolving microneedle fabrication which could be harnessed for the deposition of nanoparticles into the dermis, for extended drug release within the skin.

Influence of Dopamine Methacrylamide on Swelling Behavior and Nanomechanical Properties of PNIPAM Microgels

The combination of the catechol-containing comonomer dopamine methacrylamide (DMA) with stimuli-responsive poly(N-isopropylacrylamide) (PNIPAM) microgels bears a huge potential in research and for applications due to the versatile properties of catechols. This research gives the first detailed insights into the influence of DMA on the swelling of PNIPAM microgels and their nanomechanical properties. Dynamic light scattering measurements showed that DMA decreases the volume phase transition temperature and completion temperature due to its higher hydrophobicity when compared to NIPAM, while sharpening the transition. The cross-linking ability of DMA decreases the swelling ratios and mesh sizes of the microgels. Microgels adsorbed at the solid surface are characterized by atomic force microscopy─as the DMA content increases, microgels protrude more from the surface. Force spectroscopy measurements below and above the volume phase transition temperature display a stiffening of the microgels with the incorporation of DMA and upon heating across its entire cross section as evidenced by an increase in the E modulus. This confirms the cross-linking ability of DMA. The affine network factor β, derived from the Flory-Rehner theory, is linearly correlated with the E moduli of both pure PNIPAM and P(NIPAM-co-DMA) microgels. However, large DMA amounts hinder the microgel shrinking while maintaining mechanical stiffness, possibly due to catechol interactions within the microgel network.

Theoretical Study of Microgel Functional Groups' Mobility

Polymer microgels, micrometer-sized cross-linked polymer particles, are considered to be a promising type of advanced materials for a wide range of applications. To enhance the microgels' applicability, it is essential to incorporate various functional groups into a microparticle polymer network. Yet, the availability of functional groups for the interaction with surroundings depends strongly on the properties of the polymer network and has a great impact on further effective usage. In this theoretical study, we address this question and, with the help of coarse-grained molecular dynamics computer simulations, assess the segmental mobility and accessibility of functional groups bound to polymer network depending on microgel architecture and solvent quality. Additionally, we evaluate the minimum number of functional groups needed to facilitate the hopping mechanism between the functional groups (i.e., charge transfer). As an example of practical implementation of the obtained results, we estimate the optimal network topology for redox-active microgels to provide the maximum charge capacity for the dispersion electrolyte in redox-flow batteries.

A Review on Thermal Properties of Hydrogels for Electronic Devices Applications

Hydrogels, as a series of three-dimensional, crosslinked, hydrophilic network polymers, exhibit extraordinary properties in softness, mechanical robustness and biocompatibility, which have been extensively utilized in various fields, especially for electronic devices. However, since hydrogels contain plenty of water, the mechanical and electrochemical properties are susceptible to temperature. The thermal characteristics of hydrogels can significantly affect the performance of flexible electronic devices. In this review, recent research on the thermal characteristics of hydrogels and their applications in electronic devices is summarized. The focus of future work is also proposed. The thermal stability, thermoresponsiveness and thermal conductivity of hydrogels are discussed in detail. Anti-freezing and anti-drying properties are the critical points for the thermal stability of hydrogels. Methods such as introducing soluble ions and organic solvents into hydrogels, forming ionogels, modifying polymer chains and incorporating nanomaterials can improve the thermal stability of hydrogels under extreme environments. In addition, the critical solution temperature is crucial for thermoresponsive hydrogels. The thermoresponsive capacity of hydrogels is usually affected by the composition, concentration, crosslinking degree and hydrophilic/hydrophobic characteristics of copolymers. In addition, the thermal conductivity of hydrogels plays a vital role in the electronics applications. Adding nanocomposites into hydrogels is an effective way to enhance the thermal conductivity of hydrogels.