Clinical Evaluation of Resin Composite CAD/CAM Restorations Placed by Undergraduate Students

Comparison of Clinical Efficacy of CAD/CAM Endocrowns Made of Feldspathic, Zirconia Lithium Silicate, and Lithium Disilicate: A Two-year Mixed Cohort Study

OBJECTIVE

Endocrowns can be fabricated from various materials as a treatment option for endodontically treated teeth. This mixed cohort study aimed to demonstrate the clinical efficacy of endocrowns made of feldspathic, zirconia lithium silicate, and lithium disilicate ceramics using a chairside CAD/CAM system.

METHODS

The present study compared the clinical outcomes of 141 endocrown restorations in posterior teeth of 85 patients in a two-year follow-up. The efficacy of restorations was evaluated in three aspects: esthetics, biological response, and function, with the aid of the FDI guideline, and presented as descriptive analyses. Additionally, the data were analyzed using Chi-square and Spearman correlation tests. The significance level was set at p = 0.05.

RESULTS

The study findings revealed that the type of restorations (feldspathic, zirconia lithium silicate, and lithium disilicate) (p > 0.05) and underlying teeth (molars and premolars) (p > 0.05) play no part in restorations' failure. Caries' recurrence is primarily responsible for the failure of the endocrowns. Secondary caries and radiolucency were observed in four teeth (2.83%). The clinical efficacy of 126 restorations (89.36%) fell into the category of "clinically excellent" and "clinically good." Ten restorations (7.09%) were classified as "clinically sufficient/satisfactory," and only five restorations (3.54%) needed replacement due to having "clinically unsatisfactory" and "clinically poor" quality.

CONCLUSIONS

With endocrowns made of the mentioned ceramics showing a high success rate and durability in the short term, they can be considered a safe choice for restoring endodontically treated teeth. It is worth noting that caries were the most common reason for the failure of the restorations.

CLINICAL SIGNIFICANCE

Endocrowns made of different ceramics have been proven reliable restorations for endodontically treated molars and premolars.

Impact of CAD/CAM Material Thickness and Translucency on the Polymerization of Dual-Cure Resin Cement in Endocrowns

The objective of this study is to evaluate the impact of the thickness and translucency of various computer-aided design/computer-aided manufacturing (CAD/CAM) materials on the polymerization of dual-cure resin cement in endocrown restorations. Three commercially available CAD/CAM materials-lithium disilicate glass (e.max CAD), resin composite (CERASMART), and a polymer-infiltrated ceramic network (ENAMIC)-were cut into plates with five different thicknesses (1.5, 3.5, 5.5, 7.5, and 9.5 mm) in both high-translucency (HT) and low-translucency (LT) grades. Panavia V5, a commercial dual-cure resin cement, was polymerized through each plate by light irradiation. Post-polymerization treatment was performed by aging at 37 °C for 24 h under light-shielding conditions. The degree of conversion and Vickers hardness measurements were used to characterize the polymerization of the cement. The findings revealed a significant decrease in both the degree of conversion and Vickers hardness with increasing thickness across all CAD/CAM materials. Notably, while the differences in the degree of conversion and Vickers hardness between the HT and LT grades of each material were significant immediately after photoirradiation, these differences became smaller after post-polymerization treatment. Significant differences were observed between samples with a 1.5 mm thickness (conventional crowns) and those with a 5.5 mm or greater thickness (endocrowns), even after post-polymerization treatment. These results suggest that dual-cure resin cement in endocrown restorations undergoes insufficient polymerization.

Effect of Additional Dry Heat Curing on Microflexural Strength in Three Types of Resin Composite: An In Vitro Study

Aim: Additional dry heat curing is a method that favorably influences the mechanical properties of an indirect resin composite restoration. Microflexural strength is a property currently applied for the evaluation of indirect resin composite restorations. The aim of the present study was to assess the effect of additional dry heat curing on microflexural strength in three types of direct-use resin composites. Materials and Methods: This in vitro study consisted of 70 resin composites samples made with a 6 × 2 × 1 mm metal matrix and divided into seven experimental groups, which included Gr1a: Tetric N-Ceram without additional dry heat curing (n = 10); Gr1b: Tetric N-Ceram with additional dry heat curing (n = 10); Gr 2a: Filtek Z350 XT without additional dry heat curing (n = 10); Gr2b: Filtek Z350 XT with additional dry heat curing (n = 10); Gr3a: Filtek Z250 without additional dry heat curing (n = 10); Gr3b: Filtek Z250 with additional dry heat curing (n = 10); and Gr4: SR Nexco Paste (control) without additional dry heat curing (n = 10). The samples were stored in distilled water at 37 °C for 24 h. A universal testing machine with a 2000 N load cell at a speed of 1 mm/min was used to assess flexural strength. The data were analyzed with a parametric ANOVA test with Tukey’s post hoc intergroup factor (for groups without heat treatment) and a nonparametric Kruskall Wallis test with Bonferroni’s post hoc (for groups with heat treatment). In addition, the comparison of independent groups in each resin composite type with and without heat treatment was performed with a Mann Whitney U test. A significance level of p < 0.05 was considered. Results: The Filtek Z250 resin composite with and without additional dry heat curing presented the highest microflexural strength values with 137.27 ± 24.43 MPa and 121.32 ± 9.74 MPa, respectively, while the SR Nexco Paste (control) resin composite presented the lowest microflexural strength values with 86.06 ± 14.34 MPa compared to all the resin composites with additional dry heat curing. The Filtek Z250 and Filtek Z350XT resin composites with and without additional dry heat curing presented significantly higher microflexural strength versus the SR Nexco (p < 0.05) and Tetric N-Ceram (p < 0.05) resin composites. In addition, the Filtek Z350XT and Tetric N-Ceram resin composites with additional dry heat curing showed significantly higher microflexural strength (p < 0.05) compared to those without additional dry heat curing. Conclusions: The Filtek Z250 and Z350XT resin composites had significantly higher microflexural strength values with and without additional dry heat curing. In addition, the Filtek Z350XT and Tetric N-Ceram resin composites subjected to additional dry heat curing showed significantly higher microflexural strength compared to when they did not receive the same procedure, a situation that did not occur with the Filtek Z250 resin composite.