Engineering of TeO2-ZnO-BaO-Based Glasses for Mid-Infrared Transmitting Optics

Effect of Yb3+ on the Structural and Visible to Near-Infrared Wavelength Photoluminescence Properties in Sm3+-Yb3+-Codoped Barium Fluorotellurite Glasses

We report on the Sm³⁺ and Sm³⁺:Yb³⁺-doped barium fluorotellurite glasses prepared using the conventional melting and quenching method. The spectroscopic characterisations were investigated with Raman and FTIR to evaluate the glasses’ structural and hydroxyl (-OH) content. The Raman analysis revealed a structural modification in the glass network upon adding and increasing the Yb³⁺ concentration from a TeO₃ trigonal pyramid to a TeO₄ trigonal bi-pyramid polyhedral. At the same time, the FTIR measurements showed the existence of -OH groups in the glass. Thus, under the current experimental conditions and nominal composition, the -OH group contents are too large to enable an effective removal. The near-infrared region of the absorption spectra is employed to determine the nephelauxetic ratio and bonding parameters. The average nephelauxetic ratio decreases, and the bonding parameter increases with the increasing Yb³⁺ content in the glasses. A room temperature visible and near-infrared photoluminescence ranging from 500 to 1500 nm in wavelength and decay properties were investigated for glasses doped with Sm³⁺ and Sm³⁺-Yb³⁺ by exciting them with 450 and 980 nm laser sources. Exciting the Sm³⁺- and Sm³⁺-Yb³⁺-doped glasses by 450 nm excitation reveals a new series of photoluminescence emissions at 1200, 1293, and 1418 nm, corresponding to the ⁶F_11/2 state to the ⁶H_J (J = 7/2, 9/2, 11/2) transitions. Under the 976 nm laser excitation, a broad photoluminescence emission from 980 to 1200 nm was detected. A decay lifetime decreased from ~244 to ~43 μs by increasing the Yb³⁺ content, ascribing to concentration quenching and the OH content.

Physicochemical Properties and Fiber-Drawing Ability of Tellurite Glasses in the TeO2-ZnO-Y2O3 Ternary System

Glasses in the TeO₂-ZnO-Y₂O₃ (TZY) ternary system are examined in the present work. The vitrification domain of the chosen oxide matrix is determined and differential scanning calorimetry as well as X-ray diffraction measurements are carried out. The material characterizations reveal that Y₂O₃ incorporation cannot exceed 5 mol.% without causing detrimental crystallization within the glass. Optical transmission and refractive index investigations are conducted on compositions yielding fully amorphous samples. Next, the fiber drawing ability of selected yttrium-containing zinc-tellurite glasses is assessed and fiber-attenuation measurements in the mid-infrared are presented. Finally, a multimode step-index fiber is fabricated by combining a TZY cladding glass with a La₂O₃-based tellurite core glass. It is believed that yttrium-containing glasses could prove useful in association with other high glass transition temperature (>300 °C) TeO₂-based materials for the design of robust optical fibers with precisely engineered refractive index profiles.