FeSiCr Alloy Powder to Carbonyl Iron Powder Mixing Ratio Effects on the Magnetic Properties of the Iron-Based Alloy Powder Cores Prepared Using Screen Printing

Magnetic Properties of the Soft Magnetic Composites Prepared Using Mixtures of Carbonyl Iron, FeSiCr, and FeSiAl Alloy Powders

The effect of carbonyl iron powder, FeSiCr alloy powder, and annealed FeSiAl alloy powder, both individually and in binary combinations, on the density, microstructure, and magnetic properties (including permeability and power loss) of inductors manufactured by molding compaction was investigated in this study. The investigation demonstrates that hysteresis loss dominates power loss in the tested frequency range. Due to higher compacted density and reduced coercivity, adding 50% carbonyl iron powder to annealed powder resulted in the lowest hysteresis loss, allowing for domain wall movement. On the other hand, adding 50% FeSiCr alloy powder to annealed powder resulted in higher hysteresis loss due to impurity components hindering domain wall motion. Due to extreme plastic deformation, the carbonyl iron powder and FeSiCr alloy powder combinations displayed the most significant hysteresis loss. Eddy current loss followed the same trends as hysteresis loss in the mixtures. This study provides important insights for refining the soft magnetic composite design to obtain higher magnetic performance, while minimizing power loss.

Power Molding Inductors Prepared Using Amorphous FeSiCrB Alloy Powder, Carbonyl Iron Powder, and Silicone Resin

In this study, amorphous FeSiCrB alloy powder, carbonyl iron powder, and high-temperature heat-resistant silicone resin were used to prepare power molding inductors, and the effects of different heat treatment procedures on the magnetic properties were investigated. Two heat treatment procedures were used. Procedure 1: Amorphous FeSiCrB alloy powder was pre-heat-treated, then mixed with carbonyl iron powder and silicone resin and uniaxially pressed to prepare power inductors. Procedure 2: A mixture of amorphous FeSiCrB alloy powder, carbonyl iron powder, and silicone resin was uniaxially pressed. After dry pressing, the compacted body was heat-treated at 500 °C. Heat treatment after compaction can reduce the internal strain caused by high-pressure compaction and promote the crystallization of superparamagnetic nano-grains simultaneously. Therefore, the compacted sample after heat treatment exhibited better magnetic properties.