The Effect of Liquid Rubber Addition on the Physicochemical Properties, Cytotoxicity, and Ability to Inhibit Biofilm Formation of Dental Composites

Considerations about Cytotoxicity of Resin-Based Composite Dental Materials: A Systematic Review

The dental material industry is rapidly developing resin-based composites (RBCs), which find widespread use in a variety of clinical settings. As such, their biocompatibility has gained increasing interest. This literature review presents a summary of research into the cytotoxicity of methacrylate-based composites published from 2017 to 2023. Subject to analysis were 14 in vitro studies on human and murine cell lines. Cytotoxicity in the included studies was measured via MTT assay, LDH assay, and WST-1 assay. The QUIN Risk of Bias Tool was performed to validate the included studies. Included studies (based entirely on the results of in vitro studies) provide evidence of dose- and time-dependent cytotoxicity of dental resin-based composites. Oxidative stress and the depletion of cellular glutathione (GSH) were suggested as reasons for cytotoxicity. Induction of apoptosis by RBCs was indicated. While composites remain the golden standard of dental restorative materials, their potential cytotoxicity cannot be ignored due to direct long-term exposure. Further in vitro investigations and clinical trials are required to understand the molecular mechanism of cytotoxicity and produce novel materials with improved safety profiles.

Composite and Polymeric Materials for Dentistry: Enhancing Antimicrobial and Mechanical Properties

Billions of people suffer from dental problems and that number is constantly increasing [...].

Miscibility and Optimization of the Liquid Rubber Content in the Resins of Light-Cured Dental Composites

Fracture toughness is one of the main factors influencing the durability of light-cured composites used for dental restorations and fillings. One of the methods of increasing the fracture toughness is the modification of the matrix with liquid acrylonitrile-free liquid rubber. This study aimed to assess the miscibility of acrylonitrile-free liquid rubber with a blend of resins and their stability over time, and to determine the optimal amount of liquid rubber (LR) in the blend due to mechanical properties. Two blends of dimethacrylate resins were used: resin "F" composed of BisGMA (60 wt.%), TEGDMA (20 wt.%), BisEMA (10 wt.%) and UDMA (10 wt.%), and "C" resin containing BisGMA (40 wt.%), TEGDMA (40 wt.%), BisEMA (10 wt.%) and UDMA (10 wt.%). The modifier Hypro^® 2000X168LC VTB liquid rubber was used in at 1%, 2%, 3%, 4%, 5%, 10%, 15% and 20% by weight in the resin blend. The miscibility was assessed by microscopy. The fracture toughness, flexural strength and Young's modulus were determined in the bending test. The results showed that the solubility of the liquid rubber depends on the ratio of BisGMA/TEGDMA in the resins. In resins with 40 wt.% TEGDMA, the LR solubility was as high as 5%, while resins with 20 wt.% TEGDMA, the liquid rubber did not dissolve. The LR-resin mixtures showed good time stability, and no changes in the size or morphology of the rubber domains were found after 24 h of mixing. The maximum fracture toughness (2.46 MPa m^1/2) was obtained for 5 wt.% LR in resin F and for 15 wt.% LR in resin C (2.53 MPa m^1/2). The modification with liquid rubber resulted in an exponential reduction in both flexural strength and Young's modulus. The analysis of the results of the mechanical tests allowed us to determine the optimal amount of LR for both resins. For resin F it was 5.4 wt.%, and for resin C it was 8.3 wt.%. It can be stated that the optimal amount of liquid rubber increases with its solubility in the resin.

Study on Nitrile Oxide for Low-Temperature Curing of Liquid Polybutadiene

As a significant component of composite solid propellants, the cross-link alkenyl polymers need to cure at high temperatures and the current isocyanate curing systems are highly humidity sensitive. This paper presented a low-temperature curing method for a cross-linked polymer (polybutadiene) with stable wettability by using cycloaddition of the nitrile oxide of tetramethyl-terephthalobisnitrile oxide (TTNO) and the C=C group of liquid polybutadiene (PB). The TTNO was synthesized in four steps from 1,2,4,5-tetramethylbenzene and evaluated as a low-temperature hardener for curing liquid PB. To characterize the reaction ability of TTNO at 25 °C, the cross-linked rubber materials of various contents (8%, 10%, 12%, 14%, 16%) of curing agent TTNO were prepared. The feasibility of the curing method can be proved by the disappearance of the absorption peak of the nitrile oxide group (2300 cm⁻¹) by FT-IR analysis. Contact angle, TG-DTA and tensile-test experiments were conducted to characterize the wettability, thermo-stability and mechanical properties of the obtained cross-linked rubber materials, respectively. The results showed that the curing agent TTNO could cure PB at room temperature. With the growing content of the curing agent TTNO, the tensile strength of the obtained cross-linked rubber material increased by 260% and the contact angle increased from 75.29° to 89.44°. Moreover, the thermo-stability performances of the cross-linked rubber materials have proved to be very stable, even at a temperature of 300 °C, by TGA analysis.