A Fresh View on Limestone Calcined Clay Cement (LC3) Pastes

Physical and Chemical Effects in Blended Cement Pastes Elaborated with Calcined Clay and Nanosilica

Supplementary cementitious materials (SCMs) are commonly used in the manufacture of commercial cements with lower clinker content and carbon footprints, enabling environmental and performance improvements. The present article evaluated a ternary cement combining 23% calcined clay (CC) and 2% nanosilica (NS) to replace 25% of the Ordinary Portland Cement (OPC) content. For this purpose, a series of tests were performed, such as compressive strength, isothermal calorimetry, thermogravimetry (TG/DTG), X-ray diffraction (XDR), and mercury intrusion porosimetry (MIP). The ternary cement studied, 23CC2NS, presents a very high surface area, which influences hydration kinetics by accelerating silicate formation and causes an undersulfated condition. The pozzolanic reaction is potentialized by the synergy between the CC and NS, resulting in a lower portlandite content at 28 days in the 23CC2NS paste (6%) compared with the 25CC paste (12%) and 2NS paste (13%). A significant reduction in total porosity and conversion of macropores in mesopores was observed. For example, 70% of pores in OPC paste were macropores that were converted in the 23CC2NS paste into mesopores and gel pores.

Clays and Clay Minerals in the Construction Industry

Clay is a naturally occurring material that can be converted to different clay minerals through thermal treatments, and can be used for the development of different products. Clays and clay minerals have been used for different applications in different sectors. Detailed information regarding the applications of these materials in the construction industry are described. Clay has been used as a supplementary cementitious material in Portland cement (OPC) mortars and concretes. These minerals decrease raw materials and CO2 emissions during the production of Portland cement clinker and, at the same time, increase the compressive strength of concrete at a later age. Therefore, they are conducive to the sustainability of construction materials. A new type of cement, Limestone calcined clay cement (LC3), and a binding material geopolymer cement have also been developed using clay minerals. The properties of these binders have been discussed. Applications of clay products for making bricks have are also described in this article.

An Atomistic Model Describing the Structure and Morphology of Cu-Doped C-S-H Hardening Accelerator Nanoparticles

Calcium silicate hydrate (C-S-H) is the main binding phase in Portland cement. The addition of C-S-H nanoparticles as nucleation seeds has successfully been used to accelerate the hydration process and the precipitation of binding phases either in conventional Portland cement or in alternative binders. Indeed, the modulation of the hydration kinetics during the early-stage dissolution-precipitation reactions, by acting on the nucleation and growth of binding phases, improves the early strength development. The fine-tuning of concrete properties in terms of compressive strength and durability by designed structural modifications can be achieved through the detailed description of the reaction products at the atomic scale. The nano-sized, chemically complex and structurally disordered nature of these phases hamper their thorough structural characterization. To this aim, we implement a novel multi-scale approach by combining forefront small-angle X-ray scattering (SAXS) and synchrotron wide-angle X-ray total scattering (WAXTS) analyses for the characterization of Cu-doped C-S-H nanoparticles dispersed in a colloidal suspension, used as hardening accelerator. SAXS and WAXTS data were analyzed under a unified modeling approach by developing suitable atomistic models for C-S-H nanoparticles to be used to simulate the experimental X-ray scattering pattern through the Debye scattering equation. The optimization of atomistic models against the experimental pattern, together with complementary information on the structural local order from ²⁹Si solid-state nuclear magnetic resonance and X-ray absorption spectroscopy, provided a comprehensive description of the structure, size and morphology of C-S-H nanoparticles from the atomic to the nanometer scale. C-S-H nanoparticles were modeled as an assembly of layers composed of 7-fold coordinated Ca atoms and decorated by silicate dimers and chains. The structural layers are a few tens of nanometers in length and width, with a crystal structure resembling that of a defective tobermorite, but lacking any ordering between stacking layers.