Evolution of Microstructural and Mechanical Properties during Cold-Rolling Deformation of a Biocompatible Ti-Nb-Zr-Ta Alloy

The Effect of Solution Treatment Duration on the Microstructural and Mechanical Properties of a Cold-Deformed-by-Rolling Ti-Nb-Zr-Ta-Sn-Fe Alloy

The study presented in this paper is focused on the effect of varying the solution treatment duration on both the microstructural and mechanical properties of a cold-deformed by rolling Ti-30Nb-12Zr-5Ta-2Sn-1.25Fe (wt.%) alloy, referred to as TNZTSF. Cold-crucible induction using the levitation synthesis technique, conducted under an argon-controlled atmosphere, was employed to fabricate the TNZTSF alloy. After synthesis, the alloy underwent cold deformation by rolling, reaching a total deformation degree (total applied thickness reduction) of 60%. Subsequently, a solution treatment was conducted at 850 °C, with varying treatment durations ranging from 2 to 30 min in 2 min increments. X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques were utilized for the structural analysis, while the mechanical properties were assessed using both tensile and hardness testing. The findings indicate that (i) in both the cold-deformed-by-rolling and solution-treated states, the TNZTSF alloy exhibits a microstructure consisting of a single β-Ti phase; (ii) in the solution-treated state, the microstructure reveals a rise in the average grain size and a decline in the internal average microstrain as the duration of the solution treatment increases; and (iii) owing to the β-phase stability, a favorable mix of elevated strength and considerable ductility properties can be achieved.

Effects of Cold Rolling or Precipitation Hardening Treatment on the Microstructure, Mechanical Properties, and Corrosion Resistance of Ti-Rich Metastable Medium-Entropy Alloys

Titanium-rich metastable medium-entropy alloys, designed for low elastic moduli, sacrifice strength. However, enhancing their mechanical strength is crucial for bio-implant applications. This study aims to enhance the mechanical properties and corrosion resistance of a metastable Ti80-Nb10-Mo5-Sn5 medium-entropy alloy using various treatments, including cold rolling (at 50% and 75% reduction) and precipitation hardening (at room temperature, 150 °C, 350 °C, 550 °C, and 750 °C). The results showed that the alloy underwent a stress-induced martensitic transformation during the rolling process. Notably, the α phase was precipitated in the β grain boundaries after 30 days of precipitation hardening at room temperature. The yield strengths of the alloy increased by 51% and 281.9% after room-temperature precipitation and 75% cold rolling, respectively. In potentiodynamic corrosion tests conducted in phosphate-buffered saline solution, the pitting potentials of the alloy treated using various conditions were higher than 1.8 V, and no pitting holes were observed on the surface of the alloys. The surface oxide layer of the alloy was primarily composed of TiO2, Nb2O5, MoO3, and SnO2, contributing to the alloy's exceptional corrosion and pitting resistance. The 75% rolled Ti80-Nb10-Mo5-Sn5 demonstrates exceptional mechanical properties and high corrosion resistance, positioning it as a promising bio-implant candidate.