Influence of the Processing Method on the Properties of Ti-23 at.% Mo Alloy

Ultrafine-Grained Ti-31Mo-Type Composites with HA and Ag, Ta2O5 or CeO2 Addition for Implant Applications

Ultrafine-grained Ti31Mo alloy and Ti31Mo5HA, Ti31Mo5HA-Ag (or Ta₂O₅, CeO₂) composites with a grain size of approximately 2 μm were produced by the application of mechanical alloying and powder metallurgy. Additionally, the surface of the Ti31Mo alloy was modified. In the first stage, the specimens were immersed in 5M NaOH for 24 h at 60 °C. In the second stage, hydroxyapatite (HA) was deposited on the sample surface. The cathodic deposition at −5 V vs. open circuit potential (OCP) in the electrolyte containing 0.25M CaNa₂-EDTA (di-calcium ethylenediaminetetraacetic acid), 0.25M K₂HPO₄ in 1M NaOH at 120 °C for 2 h was applied. The bulk Ti31Mo alloy is a single β-type phase. In the alkali-modified surface titanium oxide, Ti₃O is formed. After hydrothermal treatment, the surface layer mostly consists of the Ca₁₀(PO₄)₆(OH)₂ (81.23%) with about 19% content of CaHPO₄·2H₂O. Using optical profiler, roughness 2D surface topography parameters were estimated. The in vitro cytocompatibility of synthesized materials was studied. The cell lines of normal human osteoblasts (NHost) and human periodontal ligament fibroblasts (HPdLF) was conducted in the presence of tested biomaterials. Ultrafine-grained Ti-based composites altered with HA and Ag, Ta₂O₅ or CeO₂ have superior biocompatibility than the microcrystalline Ti metal. NHost and HPdLF cells in the contact with the synthesized biomaterial showed stable proliferation activity. Biocompatibility tests carried out indicate that the ultrafine-grained Ti31Mo5HA composites with Ag, Ta₂O_5, or CeO₂ could be a good candidate for implant applications.

Development of tantalum with highly hydrophilic surface and antimicrobial properties obtained by micro-arc oxidation process

Tantalum (Ta) and its application in biomaterials has been attracting more and more attention recently. It can be considered as a material for hard tissue implants. This study focuses on antimicrobial and surface characterization of micro-arc oxidized (MAO) nanocrystalline Ta compared with its microcrystalline equivalent. For the purposes of the investigation, x-ray diffractometry (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), wetting analysis, optical profilometry, corrosion resistance measurement, and antimicrobial tests were performed. Nanocrystalline Ta was fabricated using high-energy ball milling (HEBM) and pulse plasma sintering (PPS). The MAO process done at 250 V results in the formation of a porous oxide surface. An XRD analysis confirmed the presence of a Ta₂ O₅ oxide layer. Based on the SEM pictures, the obtained oxide layer was approximately 3-4 μm thick for nanocrystalline Ta substrate. For microcrystalline Ta, the oxide layer was thinner, in the range of 0.3-0.6 μm. The analysis of polarization curves showed a significant improvement of corrosion resistance for MAO nanocrystalline Ta (2.62 × 10^-8 A/cm² ) versus not oxidized nanocrystalline Ta (1.20 × 10^-5 A/cm² ). The surface roughness of MAO nanocrystalline Ta proved to be several times higher than that of unoxidized Ta. Wetting analysis showed that the oxide layer on the nanocrystalline substrate is hydrophilic. This research provides detailed information about MAO microcrystalline and MAO nanocrystalline Ta antimicrobial activity against Staphylococcus aureus and Pseudomonas aeruginosa. A significant decrease of S. aureus for MAO nanocrystalline Ta (control 10,435 ± 981 vs. sample 3,453 ± 130) was noticed. No significant difference was noticed for MAO microcrystalline and nanocrystalline Ta tested for P. aeruginosa.