Synthesis of Microporous Mo2C-W2C Binary Carbides by Thermal Decomposition of Molybdenum-Tungsten Blues

Synthesis and Characterization of Supported Mixed MoW Carbide Catalysts

For mixed MoW carbide catalysts, the relationship between synthesis conditions, evolution of (mixed) phases, extent of mixing, and catalytic performance of supported Mo/W carbides remains unclear. In this study, we prepared a series of carbon nanofiber-supported mixed Mo/W-carbide catalysts with varying Mo and W compositions using either temperature-programmed reduction (TPR) or carbothermal reduction (CR). Regardless of the synthesis method, all bimetallic catalysts (Mo:W bulk ratios of 1:3, 1:1, and 3:1) were mixed at the nanoscale, although the Mo/W ratio in individual nanoparticles varied from the expected bulk values. Moreover, the crystal structures of the produced phases and nanoparticle sizes differed depending on the synthesis method. When using the TPR method, a cubic carbide (MeC_1-x ) phase with 3-4 nm nanoparticles was obtained, while a hexagonal phase (Me₂C) with 4-5 nm nanoparticles was found when using the CR method. The TPR-synthesized carbides exhibited higher activity for the hydrodeoxygenation of fatty acids, tentatively attributed to a combination of crystal structure and particle size.

Molybdenum-Tungsten Blue Nanoparticles as a Precursor for Ultrafine Binary Carbides

Herein, we demonstrate a promising method for the synthesis of ultrafine carbide particles using dispersions of molybdenum–tungsten nanoparticles. Dispersions of molybdenum–tungsten blue nanoparticles with different initial molar ratios of molybdenum/tungsten were synthesized through the reduction of molybdate and tungstate ions by ascorbic acid in an acidic medium (pH = 1.0–2.5). Molybdenum–tungsten blue nanoparticles were characterized by ultraviolet–visual (UV–VIS), infrared (FTIR), and X-ray photoelectron (XPS) spectroscopies; transmission electronic microscopy (TEM); and dynamic light scattering (DLS). We demonstrated that molybdenum–tungsten blue nanoparticles belong to toroidal polyoxometalate clusters (λ_max = 680–750 nm) with a predominant particle size of 4.0 nm. Molybdenum–tungsten blue dispersions were shown to be monodispersed systems with a small particle size and long-term stability (>30 days) and are suitable for further catalytic applications.