Sustainable and Environmentally Friendly Microwave Synthesis of Nano-Hydroxyapatite from Decarbonized Eggshells. MATERIALS (BASEL, SWITZERLAND) 2024; 17:1832. [PMID: 38673189 PMCID: PMC11050794 DOI: 10.3390/ma17081832] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Subscribe] [Scholar Register] [Received: 03/16/2024] [Revised: 03/30/2024] [Accepted: 04/11/2024] [Indexed: 04/28/2024]
Abstract
The sustainable microwave (MW) synthesis of hydroxyapatite (HAp) from decarbonized eggshells was investigated. Decarbonization of eggshells, as a natural source of calcium carbonate (CaCO3), was carried out in the current study at ambient conditions to reduce the footprint of CO2 emissions on our environment where either calcination or acidic direct treatments of eggshells produce CO2 emissions, which is a major cause for global warming. Eggshell decarbonization was carried out via the chemical reaction with sodium hydroxide (NaOH) alkaline solution in order to convert eggshell waste into calcium hydroxide (Ca(OH)2) and simultaneously store CO2 as a sodium carbonate (Na2CO3) by-product which is an essential material in many industrial sectors. The produced Ca(OH)2 was mixed with ammonium dihydrogen phosphate (NH4H2PO4) reagent at pH~11 before being subjected to MW irradiation at 2.45 GHz frequency for 5 min using 800 Watts to prepare HAp. The prepared Nano-HAp was characterized using X-ray diffraction (XRD) where the crystal size was ~28 nm using the Scherrer equation. The elongated rod-like nano-HAp crystals were characterized using scanning electron microscopy (SEM) equipped with dispersive energy X-ray spectroscopy (EDS), Fourier transform infrared spectroscopy (FTIR), and transmission electron microscopy (TEM). MW synthesis of decarbonized eggshells is considered as a sustainable and environmentally friendly route to produce promising bioceramics such as nano-HAp. Concurrently, decarbonization of eggshells offers the ability to store CO2 as a high value-added Na2CO3 material.
Collapse
|
2
|
Comparison between Two Different Synthesis Methods of Strontium-Doped Hydroxyapatite Designed for Osteoporotic Bone Restoration. MATERIALS (BASEL, SWITZERLAND) 2024; 17:1472. [PMID: 38611986 PMCID: PMC11012538 DOI: 10.3390/ma17071472] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 02/09/2024] [Revised: 03/15/2024] [Accepted: 03/17/2024] [Indexed: 04/14/2024]
Abstract
Development of efficient controlled local release of drugs that prevent systemic side effects is a challenge for anti-osteoporotic treatments. Research for new bone-regeneration materials is of high importance. Strontium (Sr) is known as an anti-resorptive and anabolic agent useful in treating osteoporosis. In this study, we compared two different types of synthesis used for obtaining nano hydroxyapatite (HA) and Sr-containing nano hydroxyapatite (SrHA) for bone tissue engineering. Synthesis of HA and SrHA was performed using co-precipitation and hydrothermal methods. Regardless of the synthesis route for the SrHA, the intended content of Sr was 1, 5, 10, 20, and 30 molar %. The chemical, morphological, and biocompatibility properties of HA and SrHA were investigated. Based on our results, it was shown that HA and SrHA exhibited low cytotoxicity and demonstrated toxic behavior only at higher Sr concentrations.
Collapse
|
3
|
Synthesis of nano-hydroxyapatite using emulsion, pyrolysis, combustion, and sonochemical methods and biogenic sources: a review. RSC Adv 2024; 14:3548-3559. [PMID: 38259993 PMCID: PMC10801447 DOI: 10.1039/d3ra07559a] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/05/2023] [Accepted: 01/06/2024] [Indexed: 01/24/2024] Open
Abstract
Hydroxyapatite (HAp) is comparable to materials in bone because its chemical components are similar to those contained in animal bone, and thus, its bioactive and biocompatible properties are similar. There are applications for HAp and relevant calcium phosphate in the medical and industrial sectors, and due to the rising demand for HAp nanoparticles, considerable work has been performed to develop a variety of synthetic pathways that incorporate scientifically and practically novel aspects. Numerous studies have been conducted to examine how changes in reaction parameters will successfully influence crucial HAp features. HAp can also be synthesized from biogenic sources such as HAp-rich fish scales or animal bones as an alternative to chemical precursors. Various preparation techniques produce crystals with varying sizes, but it has been found that nano-sized HAp exhibits a greater number of bioactive properties as compared to micron-sized HAp. Rather than considering conventional methods, this review focuses on alternative approaches such as emulsion, pyrolysis, combustion, and sonochemical methods along with waste bio-sources (biogenic sources) to obtain HAp. We summarize the currently accessible information pertaining to each synthesis process, while also focusing on their benefits and drawbacks.
Collapse
|
4
|
The impact of deproteinized bovine bone particle size on histological outcomes in sinus floor elevation: a systematic review and meta-analysis. Int J Implant Dent 2023; 9:35. [PMID: 37782429 PMCID: PMC10545653 DOI: 10.1186/s40729-023-00502-1] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/26/2023] [Accepted: 09/25/2023] [Indexed: 10/03/2023] Open
Abstract
OBJECTIVES The main purpose of this study was to evaluate whether large granular bovine bone can be as effective as small granular bovine bone in maxillary sinus floor elevation. METHODS A comprehensive online search of eligible articles was conducted using PubMed, EMBASE, Cochrane Library, Scopus, and Web of Science, and a systematic review and meta-analysis was performed from establishment to February, 2023. The outcome indicators were the percentage of connective tissue, the percentage of newly formed bone and the percentage of residual xenograft respectively. The meta-analysis was conducted by using the Stata 15.1 (Stata Conpernarn, USA) and Review Manager software5.4.1. RESULTS After careful screening and review, a total of 4 studies were included for systematic review and meta-analysis. The data were extracted to compare the histological performance of bovine bones with different particle sizes after maxillary sinus elevation. No significant differences were found in the percentage of connective tissue, the percentage of newly formed bone, and the percentage of residual xenograft. CONCLUSION In this study, a systematically review of the previous literature showed that similar histological results were obtained for both large-particle bovine bone and small-particle bovine bone. Therefore, the large granular bovine bone and the small granular bovine bone were equally effective in maxillary sinus elevation. It is difficult to make conclusion from limited evidence from four studies. More clinical evidence was needed.
Collapse
|
5
|
In vitro evaluation of granules obtained from 3D sphene scaffolds and bovine bone grafts: chemical and biological assays. J Mater Chem B 2023; 11:8775-8787. [PMID: 37665632 DOI: 10.1039/d3tb00499f] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 09/05/2023]
Abstract
Sphene is an innovative bone graft material. The aim of this study was to investigate and compare the physicochemical and biological properties of Bio-Oss® (BO) and in-lab synthesized and processed sphene granules. BO granules of 1000-2000 μm (BO-L), 250-1000 μm (BO-S) and 100-200 μm (BO-p) for derived granules, and corresponding groups of sphene granules obtained from 3D printed blocks (SB-L, SB-S, SB-p) and foams (SF-L, SF-S and SF-p) were investigated. The following analyses were conducted: morphological analysis, specific surface area and porosity, inductively coupled plasma mass spectrometry (ICP-MS), cytotoxicity assay, Alizarin staining, bone-related gene expression, osteoblast migration and proliferation assays. All pulverized granules exhibited a similar morphology and SF-S resembled natural bone. Sphene-derived granules showed absence of micro- and mesopores and a low specific surface area. ICP-MS revealed a tendency for absorption of Ca and P for all BO samples, while sphene granules demonstrated a release of Ca. No cellular cytotoxicity was detected and osteoblastic phenotype in primary cells was observed, with significantly increased values for SF-L, SF-S, BO-L and BO-p. Further investigations are needed before clinical use can be considered.
Collapse
|
6
|
Fabrication and Characterization of Porous Diopside/Akermanite Ceramics with Prospective Tissue Engineering Applications. MATERIALS (BASEL, SWITZERLAND) 2023; 16:5548. [PMID: 37629839 PMCID: PMC10456605 DOI: 10.3390/ma16165548] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 07/06/2023] [Revised: 08/04/2023] [Accepted: 08/07/2023] [Indexed: 08/27/2023]
Abstract
Tissue engineering requires new materials that can be used to replace damaged bone parts. Since hydroxyapatite, currently widely used, has low mechanical resistance, silicate ceramics can represent an alternative. The aim of this study was to obtain porous ceramics based on diopside (CaMgSi2O6) and akermanite (Ca2MgSi2O7) obtained at low sintering temperatures. The powder synthesized by the sol-gel method was pressed in the presence of a porogenic agent represented by commercial sucrose in order to create the desired porosity. The ceramic bodies obtained after sintering thermal treatment at 1050 °C and 1250 °C, respectively, were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR) to determine the chemical composition. The open porosity was situated between 32.5 and 34.6%, and the compressive strength had a maximum value of 11.4 MPa for the samples sintered at 1250 °C in the presence of a 20% wt porogenic agent. A cell viability above 70% and the rapid development of an apatitic phase layer make these materials good candidates for use in hard tissue engineering.
Collapse
|
7
|
Piezoelectric Biocomposites for Bone Grafting in Dentistry. Polymers (Basel) 2023; 15:polym15112446. [PMID: 37299245 DOI: 10.3390/polym15112446] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/23/2023] [Revised: 05/21/2023] [Accepted: 05/22/2023] [Indexed: 06/12/2023] Open
Abstract
In this research, Hydroxyapatite-Potassium, Sodium Niobate-Chitosan (HA-KNN-CSL) biocomposites were synthesized, both as hydrogel and ultra-porous scaffolds, to offer two commonly used alternatives to biomaterials in dental clinical practice. The biocomposites were obtained by varying the content of low deacetylated chitosan as matrix phase, mesoporous hydroxyapatite nano-powder, and potassium-sodium niobate (K0.47Na0.53NbO3) sub-micron-sized powder. The resulting materials were characterized from physical, morpho-structural, and in vitro biological points of view. The porous scaffolds were obtained by freeze-drying the composite hydrogels and had a specific surface area of 18.4-24 m2/g and a strong ability to retain fluid. Chitosan degradation was studied for 7 and 28 days of immersion in simulated body fluid without enzymatic presence. All synthesized compositions proved to be biocompatible in contact with osteoblast-like MG-63 cells and showed antibacterial effects. The best antibacterial effect was shown by the 10HA-90KNN-CSL hydrogel composition against Staphylococcus aureus and the fungal strain Candida albicans, while a weaker effect was observed for the dry scaffold.
Collapse
|
8
|
Comparison of Low and High Temperature Sintering for Processing of Bovine Bone as Block Grafts for Oral Use: A Biological and Mechanical In Vitro Study. Bioengineering (Basel) 2023; 10:bioengineering10040473. [PMID: 37106660 PMCID: PMC10136185 DOI: 10.3390/bioengineering10040473] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/01/2023] [Revised: 04/07/2023] [Accepted: 04/07/2023] [Indexed: 04/29/2023] Open
Abstract
Large oral bone defects require grafting of bone blocks rather than granules to give physically robust, biocompatible and osteoconductive regeneration. Bovine bone is widely accepted as a source of clinically appropriate xenograft material. However, the manufacturing process often results in both reduced mechanical strength and biological compatibility. The aim of this study was to assess bovine bone blocks at different sintering temperatures and measure the effects on mechanical properties and biocompatibility. Bone blocks were divided into four groups; Group 1: Control (Untreated); Group 2: Initial boil for 6 h; Group 3: Boil 6 h followed by sintering at 550 °C for 6 h; Group 4: Boil 6 h followed by sintering at 1100 °C for 6 h. Samples were assessed for their purity, crystallinity, mechanical strength, surface morphology, chemical composition, biocompatibility and clinical handling properties. Statistical analysis was performed using one-way ANOVA and post-hoc Tukey's tests for normally distributed and Friedman test for abnormally distributed quantitative data from compression tests and PrestoBlue™ metabolic activity tests. The threshold for statistical significance was set at p < 0.05. The results showed that higher temperature sintering (Group 4) removed all organic material (0.02% organic components and 0.02% residual organic components remained) and increased crystallinity (95.33%) compared to Groups 1-3. All test groups (Group 2-4) showed decreased mechanical strength (MPa: 4.21 ± 1.97, 3.07 ± 1.21, 5.14 ± 1.86, respectively) compared with raw bone (Group 1) (MPa: 23.22 ± 5.24, p <0.05), with micro-cracks seen under SEM in Groups 3 and 4. Group 4 had the highest biocompatibility (p < 0.05) with osteoblasts as compared to Group 3 at all time points in vitro. Clinical handling tests indicated that Group 4 samples could better withstand drilling and screw placement but still demonstrated brittleness compared to Group 1. Hence, bovine bone blocks sintered at 1100 °C for 6 h resulted in highly pure bone with acceptable mechanical strength and clinical handling, suggesting it is a viable option as a block grafting material.
Collapse
|
9
|
Influence of the contact area of the sub-antral space with sinus bone and the Schneiderian membrane on osteogenesis in lateral window sinus elevation surgery: a prospective experiment. BMC Oral Health 2022; 22:650. [PMID: 36578061 PMCID: PMC9798614 DOI: 10.1186/s12903-022-02694-1] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/27/2022] [Accepted: 12/23/2022] [Indexed: 12/29/2022] Open
Abstract
BACKGROUND Osteogenesis of lateral window sinus elevation surgery is the key to placement of the subsequent implant, excessive collapse of the sub-antral space may adversely affect long-term stability of implants. At present, few studies focus on the influence of the contact area of the sub-antral space on osteogenesis. This study evaluated whether the change in the contact area of the sub-antral space with maxillary sinus bone and the Schneiderian membrane can affect osteogenesis. METHODS Cone beam computed tomography (CBCT) images were collected of patients requiring maxillary sinus floor elevation (residual bone height < 6 mm) for standard-length implant placement before surgery, after surgery, and at 6-month follow-up visits. The postoperative sub-antral space volume (V1) and surface area (S1), and the remaining volume after six months of healing (V2) were measured. Then, the contact area of sub-antral space with maxillary sinus bone (Sbc) and the Schneiderian membrane (Smc), the absorbed volume during healing (Va), and the percentage of remaining volume (V2%) and absorbed volume (Va%) were calculated. The correlation between anatomical parameters was analyzed using multiple linear regression. RESULTS A total of 62 maxillary sinuses from 56 patients were augmented, of which 57 were considered for the final analysis (5 withdrew due to perforation). Multiple linear regression results demonstrated that Sbc was significantly positively correlated with Va (β coefficient = 0.141, p < 0.01) without correlation between Smc and Va (β coefficient = - 0.046, p = 0.470). There was a positive correlation between Sbc and V2% (β coefficient = 2.269, p < 0.05). CONCLUSIONS This study confirmed that the size of the Sbc in lateral window sinus elevation surgery affected osteogenesis after six months of healing. Clinicians should assess the sinus contour type preoperatively, then consider whether it is necessary to expand the range of the Schneiderian membrane elevation to avoid excessive collapse of the sub-antral space. TRIAL REGISTRATION Chinese Clinical Trial Registry (ChiCTR), ChiCTR2200057924. Registered 22 March 2022-Retrospectively registered.
Collapse
|
10
|
Application of Tissue Engineering in Manufacturing Absorbable Membranes to Improve the Osteopromoting Potential of Collagen. BIOENGINEERING (BASEL, SWITZERLAND) 2022; 10:bioengineering10010015. [PMID: 36671587 PMCID: PMC9855111 DOI: 10.3390/bioengineering10010015] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 09/30/2022] [Revised: 11/26/2022] [Accepted: 11/28/2022] [Indexed: 12/24/2022]
Abstract
The membranes are an important biomaterial that contribute to osteopromotion. This study aimed to evaluate the osteopromotive potential of collagen membranes associated with Hydroxyapatite (HA) in critical size calvaria rat's defects. Ninety-six Albinus Wistar rats were divided into four groups: (CG) negative control: clot only (CG); positive control: porcine collagen membrane (BG); fish collagen membrane associated with HA (CP); bovine collagen membrane associated with HA (CB), analyzed at 7, 15, 30, and 60 postoperative days. At 30 days, membrane integrity was observed in the CB and fragments in the CP and BG groups were dispersed in the center of the defect. At 60 days, BG demonstrated better results with no statistical difference for the CP group (p = 0.199) and a statistically significant difference for the CB group (p = 0.013). The inflammatory profiles of the BG and CP groups were similar. Immunohistochemistry demonstrated at 60 days moderate osteopontin staining for the BG and CP groups, light staining for the CB, and intense osteocalcin staining for the BG, while the CB and CP groups demonstrated moderate staining. Microtomography revealed the highest mean bone volume (14.247 mm3) in the BG, followed by the CB (11.850 mm3), and CP (9.560 mm3) group. The collagen membranes associated with HA demonstrated an osteopromotive potential.
Collapse
|
11
|
Extraction of natural hydroxyapatite for biomedical applications—A review. Heliyon 2022; 8:e10356. [PMID: 36082327 PMCID: PMC9445296 DOI: 10.1016/j.heliyon.2022.e10356] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/27/2022] [Revised: 07/18/2022] [Accepted: 08/15/2022] [Indexed: 01/04/2023] Open
Abstract
Hydroxyapatite has recently played a crucial role in the sustainable development of biomedical applications. Publications related to hydroxyapatite as filler for biopolymers have exhibited an increasing trend due to the expanding research output. Based on the latest publications, the authors reviewed the research trends regarding hydroxyapatite use in biomedical applications. Analysis of the Scopus database using the keywords ‘hydroxyapatite” and “biomedical applications” determined that 1,714 papers were produced between 2012 and 2021. The number of publications related to these keywords more than doubled between 2012 (99) and 2021 (247). The hydrothermal method, solid-state reactions, the sol-gel process, emulsion, micro-emulsion, and mostly chemical precipitation were used to produce synthetic hydroxyapatite. Meanwhile, calcination, alkaline hydrolysis, precipitation, hydrothermal, and a combination of these techniques were used in producing natural hydroxyapatite. Studies in the current literature reveal that shell-based animal sources have been frequently used as hydroxyapatite resources during investigations concerning biomedical applications, while calcination was the extraction method most often applied. Essential trace elements of fish bone, oyster shell, and eggshell were also found in hydroxyapatite powder. Abalone mussel shell and eggshell showed Ca/P ratios closer to the stoichiometric ratio due to the use of effective extraction methods such as manipulating aging time or stirring process parameters. This review should greatly assist by offering scientific insights to support all the recommended future research works, not only that associated with biomedical applications.
Collapse
|
12
|
Biocompatibility Assessment of Two Commercial Bone Xenografts by In Vitro and In Vivo Methods. Polymers (Basel) 2022; 14:polym14132672. [PMID: 35808724 PMCID: PMC9268806 DOI: 10.3390/polym14132672] [Citation(s) in RCA: 2] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/13/2022] [Revised: 06/26/2022] [Accepted: 06/28/2022] [Indexed: 02/07/2023] Open
Abstract
Bone substitutes based on xenografts have been used for a long time in bone regeneration thanks to their inductive capacity for bone tissue regeneration. Some bone-based scaffolds have been modified by adding collagen and other proteins to improve their regenerative capacity and prevent migration and aggregation, especially particles. However, rejection of this graft has been reported due to protein residues caused by poor material preparation. We compared the in vitro and in vivo biological response of two commercial xenografts (InterOss®, F1 and InterOss® Collagen, F2) and a commercial porcine collagen membrane (InterCollagen® Guide, F3) as a rapid degradation control. Fourier Transform Infrared Spectroscopy (FT-IR) analysis evidenced the presence of hydroxyl, orthophosphate, and carbonate groups of the xenografts and amide groups of collagen. Thermogravimetric analysis (TGA) of the xenografts demonstrated their thermal stability and the presence of a few amounts of organic material. The study by differential scanning calorimetry showed the presence of endothermic peaks typical of the dehydration of the xenografts (F1 and F2) and for the collagen membrane (F3), the beginning of structural three-dimensional protein changes. Subsequently, in vitro biocompatibility tests were carried out for the materials with Artemia salina and MTT cell viability with HeLa cells, demonstrating the high biocompatibility of the materials. Finally, in vivo biocompatibility was studied by implanting xenografts in biomodels (Wistar rats) at different periods (30, 60, and 90 days). The F1 xenograft (InterOss) remained remarkably stable throughout the experiment (90 days). F2 (InterOss Collagen) presented a separation of its apatite and collagen components at 60 days and advanced resorption at 90 days of implantation. Finally, the collagen membrane (F3) presented faster resorption since, at 90 days, only some tiny fragments of the material were evident. All the in vivo and in vitro test results demonstrated the biocompatibility of the xenografts, demonstrating the potential of these materials for tissue engineering.
Collapse
|
13
|
The Effect of Low-Processing Temperature on the Physicochemical and Mechanical Properties of Bovine Hydroxyapatite Bone Substitutes. MATERIALS 2022; 15:ma15082798. [PMID: 35454491 PMCID: PMC9025514 DOI: 10.3390/ma15082798] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 02/24/2022] [Revised: 03/22/2022] [Accepted: 03/24/2022] [Indexed: 11/29/2022]
Abstract
Bovine bone grafts (BBX) require protein removal as part of the manufacturing process to reduce antigenicity and, in consequence, to be safely used in humans. Deproteinisation may have direct effects on the characteristics of the bone material and on in vivo material performance. This research aimed to comprehensively study the physicochemical and mechanical properties of BBX processed at low deproteinisation processing temperatures. Cubes of bovine bone (8 mm3) were treated with temperatures between 100 °C and 220 °C at 30 °C intervals and with pressures ranging from 1.01 to 24.58 Bar. The samples were characterised topographically and mechanically using scanning electron microscopy (SEM), atomic force microscopy (AFM), and uniaxial bending tests. The organic content and the chemical composition were determined using thermogravimetric analysis (TGA) and Fourier-transform infrared spectroscopy (FTIR). X-ray diffraction (XRD) and FTIR were also used to quantitatively determine the specimen crystallinity. Increasing temperature/pressure was associated with decreasing protein levels and compressive strength and increasing surface irregularities and crystallinity. The findings suggest that low-temperature processed bone is likely to exhibit a rapid in vivo degradation rate. The deproteinisation temperature can be adjusted to tailor the graft properties for specific applications.
Collapse
|
14
|
Inorganic Nanoparticles in Bone Healing Applications. Pharmaceutics 2022; 14:pharmaceutics14040770. [PMID: 35456604 PMCID: PMC9027776 DOI: 10.3390/pharmaceutics14040770] [Citation(s) in RCA: 17] [Impact Index Per Article: 8.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/24/2022] [Revised: 03/24/2022] [Accepted: 03/28/2022] [Indexed: 12/13/2022] Open
Abstract
Modern biomedicine aims to develop integrated solutions that use medical, biotechnological, materials science, and engineering concepts to create functional alternatives for the specific, selective, and accurate management of medical conditions. In the particular case of tissue engineering, designing a model that simulates all tissue qualities and fulfills all tissue requirements is a continuous challenge in the field of bone regeneration. The therapeutic protocols used for bone healing applications are limited by the hierarchical nature and extensive vascularization of osseous tissue, especially in large bone lesions. In this regard, nanotechnology paves the way for a new era in bone treatment, repair and regeneration, by enabling the fabrication of complex nanostructures that are similar to those found in the natural bone and which exhibit multifunctional bioactivity. This review aims to lay out the tremendous outcomes of using inorganic nanoparticles in bone healing applications, including bone repair and regeneration, and modern therapeutic strategies for bone-related pathologies.
Collapse
|
15
|
The Effect of Low-Temperature Thermal Processing on Bovine Hydroxyapatite Bone Substitutes, toward Bone Cell Interaction and Differentiation. MATERIALS 2022; 15:ma15072504. [PMID: 35407837 PMCID: PMC8999525 DOI: 10.3390/ma15072504] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 02/24/2022] [Revised: 03/26/2022] [Accepted: 03/26/2022] [Indexed: 12/17/2022]
Abstract
Ideal bone grafting scaffolds are osteoinductive, osteoconductive, and encourage osteogenesis through the remodeling processes of bone resorption, new bone formation, and successful integration or replacement; however, achieving this trifecta remains challenging. Production methods of bone grafts, such as thermal processing, can have significant effects on the degree of cell-surface interactions via wide-scale changes in the material properties. Here, we investigated the effects of small incremental changes at low thermal processing temperatures on the degree of osteoclast and osteoblast attachment, proliferation, and differentiation. Bovine bone scaffolds were prepared at 100, 130, 160, 190, and 220 °C and compared with a commercial control, Bio-Oss®. Osteoclast attachment and activity were significantly higher on lower temperature processed bone and were not present ≥190 °C. The highest osteoblast proliferation and differentiation were obtained from treatments at 130 and 160 °C. Similarly, qRT2-PCR assays highlighted osteoblasts attached to bone processed at 130 and 160 °C as demonstrating the highest osteogenic gene expression. This study demonstrated the significant effects of small-scale processing changes on bone graft materials in vitro, which may translate to a tailored approach of cellular response in vivo.
Collapse
|
16
|
Probing the Structure, Cytocompatibility, and Antimicrobial Efficacy of Silver-, Strontium-, and Zinc-Doped Monetite. ACS APPLIED BIO MATERIALS 2022; 5:1648-1657. [PMID: 35324139 PMCID: PMC9019811 DOI: 10.1021/acsabm.2c00047] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/28/2022]
Abstract
![]()
Calcium phosphate
phases are among the most widely accepted compounds
for biomaterial applications, of which the resorbable phases have
gained particular attention in recent years. Brushite and its anhydrous
form monetite are among the most interesting resorbable calcium phosphate
phases that can be applied as cements and for in situ fabrication of three-dimensional (3D) implants. Of these two dicalcium
phosphate compounds, monetite is more stable and undergoes slower
degradation than brushite. The purpose of the current study is to
synthesize and dope monetite with the antimicrobial elements silver
and zinc and the osteoinductive element strontium and investigate
the possible structural variations as well as their biocompatibility
and antimicrobial effectiveness. For this, powder X-ray diffraction
(PXRD), energy-dispersive X-ray spectroscopy (EDX), scanning electron
microscopy (SEM), and cryo-transmission electron microscopy (cryo-TEM)
were used to thoroughly study the synthesized structures. Moreover,
the ASTM E-2149-01 protocol and a cell proliferation assay were used
to determine the minimum inhibitory concentration (MIC) and minimum
bactericidal concentration (MBC) and the cytocompatibility of the
different phases with the Soas-2 cell line, respectively. The results
confirm the successful synthesis and doping procedures, such that
zinc was the most incorporated element into the monetite phase and
strontium was the least incorporated element. The microbiological
studies revealed that silver is a very effective antimicrobial agent
at low concentrations but unsuitable at high concentrations because
its cytotoxicity would prevail. On the other hand, doping the compounds
with zinc led to a reasonable antimicrobial activity without compromising
the biocompatibility to obviously high concentrations. The study also
highlights that strontium, widely known for its osteoinductivity,
bears an antimicrobial effect at high concentrations. The generated
doped compounds could be beneficial for prospective studies as bone
cements or for scaffold biomaterial applications.
Collapse
|
17
|
A New Anorganic Equine Bone Substitute for Oral Surgery: Structural Characterization and Regenerative Potential. MATERIALS 2022; 15:ma15031031. [PMID: 35160976 PMCID: PMC8840601 DOI: 10.3390/ma15031031] [Citation(s) in RCA: 4] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 11/26/2021] [Revised: 01/20/2022] [Accepted: 01/26/2022] [Indexed: 12/22/2022]
Abstract
Different xenogeneic inorganic bone substitutes are currently used as bone grafting materials in oral and maxillo-facial surgery. The aim of the present study was to determine the physicochemical properties and the in vivo performance of an anorganic equine bone (AEB) substitute. AEB is manufactured by applying a process involving heating at >300 °C with the aim of removing all the antigens and the organic components. AEB was structurally characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray fluorescence (XRF), and Fourier-transformed infrared (FT-IR) spectroscopy and compared to the anorganic bovine bone (ABB). In order to provide a preliminary evaluation of the in vivo performance of AEB, 18 bone defects were prepared and grafted with AEB (nine sites), or ABB (nine sites) used as a control, in nine Yucatan Minipigs. De novo bone formation, residual bone substitute, as well as local inflammatory and tissue effects were histologically evaluated at 30 and 90 days after implantation. The structural characterization showed that the surface morphology, particle size, chemical composition, and crystalline structure of AEB were similar to cancellous human bone. The histological examination of AEB showed a comparable pattern of newly formed bone and residual biomaterial to that of ABB. Overall, the structural data and pre-clinical evidence reported in the present study suggests that AEB can be effectively used as bone grafting material in oral surgery procedures.
Collapse
|
18
|
Novel Nano-Engineered Biomaterials for Bone Tissue Engineering. NANOMATERIALS 2022; 12:nano12030333. [PMID: 35159677 PMCID: PMC8839239 DOI: 10.3390/nano12030333] [Citation(s) in RCA: 3] [Impact Index Per Article: 1.5] [Reference Citation Analysis] [Track Full Text] [Download PDF] [Subscribe] [Scholar Register] [Received: 01/18/2022] [Accepted: 01/19/2022] [Indexed: 01/25/2023]
|
19
|
Biocompatibility Studies on a Collagen-Hydroxyapatite Biomaterial. CURRENT HEALTH SCIENCES JOURNAL 2022; 48:217-225. [PMID: 36320879 PMCID: PMC9590366 DOI: 10.12865/chsj.48.02.12] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Subscribe] [Scholar Register] [Received: 02/02/2022] [Accepted: 05/24/2022] [Indexed: 01/25/2023]
Abstract
The current treatment of osteomyelitis includes systemic antibiotic therapy and a debridement procedure of the formed biofilm and necrotic tissue. Moreover, cements and three-dimensional scaffolds are used both for the delivery of therapeutic agents and as fillers for bone defects. The aim of our research was to test, on cellular cultures, the biocompatibility of a previously synthesized microporous biocomposite containing hydroxyapatite and a collagen matrix including a therapeutic agent (ciprofloxacin and gentamicin). The scaffold was obtained by direct mineralization namely co-precipitation of hydroxyapatite on a collagen matrix.
Collapse
|
20
|
Three-Dimensional Porous Scaffolds Derived from Bovine Cancellous Bone Matrix Promote Osteoinduction, Osteoconduction, and Osteogenesis. Polymers (Basel) 2021; 13:4390. [PMID: 34960941 PMCID: PMC8705055 DOI: 10.3390/polym13244390] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/26/2021] [Revised: 11/28/2021] [Accepted: 12/01/2021] [Indexed: 11/30/2022] Open
Abstract
The use of three-dimensional porous scaffolds derived from decellularized extracellular matrix (ECM) is increasing for functional repair and regeneration of injured bone tissue. Because these scaffolds retain their native structures and bioactive molecules, in addition to showing low immunogenicity and good biodegradability, they can promote tissue repair and regeneration. Nonetheless, imitating these features in synthetic materials represents a challenging task. Furthermore, due to the complexity of bone tissue, different processes are necessary to maintain these characteristics. We present a novel approach using decellularized ECM material derived from bovine cancellous bone by demineralization, decellularization, and hydrolysis of collagen to obtain a three-dimensional porous scaffold. This study demonstrates that the three-dimensional porous scaffold obtained from bovine bone retained its osteoconductive and osteoinductive properties and presented osteogenic potential when seeded with human Wharton's jelly mesenchymal stromal cells (hWJ-MSCs). Based on its characteristics, the scaffold described in this work potentially represents a therapeutic strategy for bone repair.
Collapse
|
21
|
Bioactive Coatings Loaded with Osteogenic Protein for Metallic Implants. Polymers (Basel) 2021; 13:4303. [PMID: 34960852 PMCID: PMC8703935 DOI: 10.3390/polym13244303] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/20/2021] [Revised: 12/03/2021] [Accepted: 12/06/2021] [Indexed: 12/27/2022] Open
Abstract
Osteoconductive and osteoinductive coatings represent attractive and tunable strategies towards the enhanced biomechanics and osseointegration of metallic implants, providing accurate local modulation of bone-to-implant interface. Composite materials based on polylactide (PLA) and hydroxyapatite (HAp) are proved beneficial substrates for the modulation of bone cells' development, being suitable mechanical supports for the repair and regeneration of bone tissue. Moreover, the addition of osteogenic proteins represents the next step towards the fabrication of advanced biomaterials for hard tissue engineering applications, as their regulatory mechanisms beneficially contribute to the new bone formation. In this respect, laser-processed composites, based on PLA, Hap, and bone morphogenetic protein 4(BMP4), are herein proposed as bioactive coatings for metallic implants. The nanostructured coatings proved superior ability to promote the adhesion, viability, and proliferation of osteoprogenitor cells, without affecting their normal development and further sustaining the osteogenic differentiation of the cells. Our results are complementary to previous studies regarding the successful use of chemically BMP-modified biomaterials in orthopedic and orthodontic applications.