Effect of Carbon Nanofiber Clustering on the Micromechanical Properties of a Cement Paste

Study of the Structure and Properties of Electrical Sand Concrete under Prolonged Exposure to Sulfate Environment

Destructive processes accompanying sulfate corrosion of concrete significantly affect the durability of products and structures based on Portland cement. In the presented study, the long-term effect of sulfate corrosion on the electrical properties of electrically conductive sand concrete was studied. In the course of the study, the following were tested: an electrically conductive composition and a control composition based on plain Portland cement. The analysis of changes in the mineral composition of the samples over the course of time in an aggressive solution was carried out. The results show that during the exposure period of the samples from 28 to 224 days, the absorption of sulfate ions slows down and averages 26% for the control composition and 29% for the electrically conductive composition, of the total volume of absorbed sulfates. At the same time, the course of sulfate corrosion was accompanied by a 6% increase in the density of samples of both compositions, as well as a cyclic change in mechanical strength within 15%. In its turn, the key indicator of the electrical characteristics of the compositions-electrical resistivity-tended to increase throughout the experiment. These results can be recommended for assessing the durability and the nature of the operating conditions of electrical concretes used in aggressive environments.

Influence of Different Surfactants on Carbon Fiber Dispersion and the Mechanical Performance of Smart Piezoresistive Cementitious Composites

This experimental study presents the effect of different surfactants on micro-scale carbon fiber (CFs) distribution into carbon fiber reinforced cement-based composites (CFRC) in terms of flexural and compressive strength, stiffness, flexural toughness, and strain-sensing ability. Conducting a narrative review of the literature focusing on the fibers’ separation, this paper follows a methodology introducing a combination of mechanical and chemical carbon fibers dispersion, as well as the different mixing processes (wet or dry). Three types of surfactants: Carboxymethyl cellulose (CMC), cellulose nanocrystal (CNC), and superplasticizer (SP), were applied to evaluate the CFs distribution in the cement paste matrix. Compressive and flexural strength, modulus of elasticity, and ductility of the cement-based composites (CFRC) reinforced with 0.5 wt.% CFs were investigated by three-point bending and compressive tests; flexure tests were also conducted on notched 20 × 20 × 80 mm specimens using the Linear Elastic Fracture Mechanics (L.E.F.M.) theory. Moreover, the electrical conductivity and the piezoresistive response were determined by conducting electrical resistance measurements and applying compressive loading simultaneously. The results clearly reveal that the CFs/SP solution or the CFs’ dry incorporation led to a significant enhancement of flexural strength by 32% and 23.7%, modulus of elasticity by 30% and 20%, and stress-sensing ability by 20.2% and 18.2%, respectively. Although the wet mixing method exhibits improved mechanical and electrical conductivity performance, constituting an adequate strain and crack sensor, the authors propose dry mixing as the most economical method, in addition to the enhanced mechanical and electrical responses. The authors recommend an effective method for structural health monitoring systems combining an economical CFs insertion in cementitious smart sensors with great mechanical and self-sensing responses.