Breakdown Performance and Partial Discharge Development in Transformer Oil-Based Metal Carbide Nanofluids

Electric partial discharges in biodegradable oil-based ferrofluids: A study on effects of magnetic field and nanoparticle concentration

This paper presents an experimental study of partial discharge activity in ferrofluids based on biodegradable transformer oil and iron oxide nanoparticles. Three ferrofluid samples with low, medium and high nanoparticle concentrations are employed in the research. The basic ferrofluid characterization is followed by a partial discharge experiment exposing the ferrofluids to a high voltage in a needle-plate electrode configuration. The analysis confirms that the apparent charge and number of discharges decrease with increasing nanoparticle concentration. These findings are interpreted with reference to the well-recognised electro-hydrodynamic streamer model. The charge trapping by nanoparticles hinders the ionization and discharge development. The study also focuses on the partial discharge activity in the ferrofluids under the action of a static magnetic field acting perpendicularly to the electric field. A decreasing trend in the number of discharges due to the magnetic field is revealed. A qualitative explanation is provided based on the field-induced cluster formation and charge mobility reduction. The presented experiment and the discussed findings may be valuable for practical application of the ferrofluid in high voltage equipment with a special need for partial discharge suppression.

Influence of Emerging Semiconductive Nanoparticles on AC Dielectric Strength of Synthetic Ester Midel-7131 Insulating Oil

Exploring impressively effective dielectric nanofluids for transformers to improve dielectric strength and thermal stability is indispensable. It is crucial to determine the modification mechanism of dispersed nanomaterials in insulating oil for operative applications in power transformers. This paper aspires to authenticate the experimental evidence of the enhancing AC dielectric strength of synthetic ester Midel-7131 using two newly introduced semiconductive nanoparticles, CdS and Co3O4, and uncover the potential reasons for enhanced AC dielectric strength. The AC breakdown voltage (BDV) of synthetic ester and nanofluids was investigated and statistically evaluated. The mean AC breakdown voltage of SE/CdS and SE/Co3O4 was increased by 31.9% and 31.3%, respectively. The augmentation in AC breakdown strength is possibly due to the facilitated charge-scavenging ability owing to the large specific surface area and wide bandgap. Simultaneous thermogravimetric analysis, differential scanning calorimetry, and derivative thermogravimetry analyses (TGA-DSC-DTG) confirmed that the initial decomposition temperature was high and heat dissipation was low, indicating that the nanofluids were thermally stable in both air and nitrogen. Hence, emerging semiconductive CdS and Co3O4-based nanofluids of synthetic ester possess remarkable dielectric strength and thermal stability enhancement for their application in power transformers.

Effect of Conducting, Semi-Conducting and Insulating Nanoparticles on AC Breakdown Voltage and Partial Discharge Activity of Synthetic Ester: A Statistical Analysis

This paper is aimed at studying the influence of conducting (Fe3O4), semi-conductive (ZnO), and insulating (ZrO2, SiO2, and Al2O3) nanoparticles (NPs) at various concentrations on the AC dielectric strength of MIDEL 7131 synthetic ester (SE) and partial discharges activity. First, a detailed and improved procedure for preparing nanofluids (NFs) in five concentrations ranging from 0.1 g/L to 0.5 g/L is presented, including high-speed agitation and ultrasonication. Then, the long-term stability is checked based on zeta potential analysis. After preparing and characterizing the NF samples, the following step is to measure their AC breakdown voltage (BDV). Due to the limitation of the high voltage supply (Baur system), the tests are performed according to IEC 60156 standard (2.5 mm gap distance) only with ZnO, ZrO2, and SiO2 NPs, and for comparison, tests are executed for all considered NPs with an electrodes gap of 2 mm. It is shown that the addition of Fe3O4 (20 nm), ZnO (25 nm), ZrO2 (20-30 nm), SiO2 (10-20 nm), Al2O3 (20-30 nm), and Al2O3 (50 nm) NPs improves the dielectric strength of synthetic ester upon an optimal concentration which gives the highest AC BDV. SiO2 (10-20 nm) and Al2O3 (20-30 nm) manifest their best improvement at 0.3 g/L, while for the other NFs, the best improvement is observed at 0.4 g/L. Further, the Anderson-Darling goodness-of-fit test is performed on the experimental data to check their conformity with the Extreme value (EV), normal, and Weibull distributions; the normal and EV fit curves are plotted and used to evaluate the breakdown voltages at probabilities of 1%, 10%, and 50%. It is shown that the AC breakdown voltage outcomes for most investigated nanofluids mostly obey the three EV, normal, and Weibull distributions. Then, the best combinations (nature of NP and optimal concentration), namely Fe3O4 (20 nm, 0.4 g/L), Al2O3 (20-30 nm, 0.3 g/L), and Al2O3 (50 nm, 0.4 g/L) NPs, that highly enhance the AC BDV of SE are chosen for a partial discharge activity investigation and comparison with pure SE. It is shown that the addition of those NPs significantly reduces the activity of partial discharges compared to pure SE.