Remote Plasma-Induced Synthesis of Self-Assembled MoS2/Carbon Nanowall Nanocomposites and Their Application as High-Performance Active Materials for Supercapacitors

Innovative Variation in the Morphological Characteristics of Carbon Nanowalls Grown on a Molybdenum Disulfide Interlayer

Carbon is a material with interesting properties which exists in large quantities on Earth, so many studies involving carbon have been conducted. In particular, nano-sized carbon allotropes, referred to as carbon nanomaterials, comprise the subject of various studies currently underway. The electrical, chemical, physical properties of carbon nanowalls (CNWs) are modified by parameters such as surface density, height and thickness. These characteristics have significant effects on CNWs and can be adjusted as a growth interlayer. It was confirmed that the molybdenum disulfide (MoS₂) interlayer synthesized in this paper by radio frequency (RF) magnetron sputtering altered the morphological characteristics of the CNWs, including its shaped edge, pores diameter and density. We provide interesting results through FE-SEM, EDS and Raman analysis in this paper. Based on the Raman analysis, both the D-peak of carbon and the I_D/I_G ratio decreased. Through this study, the effect of MoS₂ on the morphological characteristics of CNWs was confirmed.

Enhancing the electrochemical performance of TiO2 based material using microwave air plasma treatment with an ECR cavity

The microwave-based plasma treatment facility at the Central University of Punjab Bathinda (CUPB) based on 2.45 GHz has been used to investigate the impact on the electrochemical performance of TiO₂. This was accomplished by treating a number of pellets of TiO₂ sample material with microwave plasma at an input power of 80 W. The palette is subjected to microwave plasma treatment at 30-, 60-, 80-, and 100-s intervals. Many such characterization methods, including UV-visible spectroscopy, FTIR, XRD, and FESEM, have been applied to the study of the impact of plasma treatment on other physical and chemical properties in the context of untreated pellets. In the 80-s plasma treatment, the FTIR study showed that the (O-Ti-O) vibration band at 500-900 cm^-1 was wider than other bands. The UV results showed that an 80-s plasma treatment decreased the sample's band gap by 37% and increased the amount of disordered, amorphous material in the sample that had not been treated. XRD studies show that a sample that was treated with plasma for 80 s has low crystallinity and a high disorder (amorphous) factor. The Nyquist plot showed that the electrochemical charge transfer resistance drops from 7 (not treated) to 4 after 80 s of plasma treatment. In a study of electrochemical performance, a sample that was treated with plasma for 80 s has a capacitance that is 35% higher than a sample that was not treated.

High-Sensitivity Ammonia Sensors with Carbon Nanowall Active Material via Laser-Induced Transfer

Ammonia sensors with high sensitivity, reproducible response, and low cost are of paramount importance for medicine, i.e., being a biomarker to diagnose lung and renal conditions, and agriculture, given that fertilizer application and livestock manure account for more than 80% of NH₃ emissions. Thus, in this work, we report the fabrication of ultra-sensitive ammonia sensors by a rapid, efficient, and solvent-free laser-based procedure, i.e., laser-induced forward transfer (LIFT). LIFT has been used to transfer carbon nanowalls (CNWs) onto flexible polyimide substrates pre-patterned with metallic electrodes. The feasibility of LIFT is validated by the excellent performance of the laser-printed CNW-based sensors in detecting different concentrations of NH₃ in the air, at room temperature. The sensors prepared by LIFT show reversible responses to ammonia when exposed to 20 ppm, whilst at higher NH₃ concentrations, the responses are quasi-dosimetric. Furthermore, the laser-printed CNW-based sensors have a detection limit as low as 89 ppb and a response time below 10 min for a 20 ppm exposure. In addition, the laser-printed CNW-based sensors are very robust and can withstand more than 200 bending cycles without loss of performance. This work paves the way for the application and integration of laser-based techniques in device fabrication, overcoming the challenges associated with solvent-assisted chemical functionalization.