Durable Modification of Wood by Benzoylation-Proof of Covalent Bonding by Solution State NMR and DOSY NMR Quick-Test

Modification Mechanisms and Properties of Poplar Wood via Grafting with 2-Hydroxyethyl Methacrylate/N,N'-methylenebis(acrylamide) onto Cell Walls

As the only renewable resource among the four basic materials (steel, cement, plastic, wood), wood itself and wood products have a "low carbon" value and play an important role in storing carbon. The moisture absorption and expansion properties of wood limit its application scope and shorten its service life. To enhance the mechanical and physical properties of fast-growing poplars, an eco-friendly modification procedure has been used. This was accomplished by the in situ modification of wood cell walls by vacuum pressure impregnation with a reaction of water-soluble 2-hydroxyethyl methacrylate (HEMA) and N,N'-methylenebis(acrylamide) (MBA). The anti-swelling efficiency of HEMA/MBA-treated wood was improved (up to 61.13%), whereas HEMA/MBA-treated wood presented a lower weight-gain rate (WG) and water-absorption rate (WAR). It was observed that the modulus of elasticity, hardness, density, and other properties of modified wood had improved significantly, as indicated by XRD analysis. Modifiers diffuse primarily within cell walls and cell interstices of wood, causing crosslinks between the modifiers and the cell walls, reducing its hydroxyl content and blocking the channels for water movement, thereby enhancing its physical properties. This result can be obtained by scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDX), Nitrogen adsorption test imaging ATR-FTIR (Attenuated total reflection-Fourier-Transform Infrared) Spectroscopy, and nuclear magnetic resonance (NMR) and Nitrogen adsorption test. Overall, this straightforward, high-performance modification method is crucial for maximizing wood's efficiency and the sustainable development of human society.

Reactivity of Waterlogged Archeological Elm Wood with Organosilicon Compounds Applied as Wood Consolidants: 2D 1H-13C Solution-State NMR Studies

Some organosilicon compounds, including alkoxysilanes and siloxanes, proved effective in stabilizing the dimensions of waterlogged archaeological wood during drying, which is essential in the conservation process of ancient artifacts. However, it was difficult to determine a strong correlation between the wood stabilizing effect and the properties of organosilicon compounds, such as molecular weight and size, weight percent gain, and the presence of other potentially reactive groups. Therefore, to better understand the mechanism behind the stabilization effectiveness, the reactivity of organosilicons with wood polymers was studied using a 2D ¹H–¹³C solution-state NMR technique. The results showed an extensive modification of lignin through its demethoxylation and decarbonylation and also the absence of the native cellulose anomeric peak in siloxane-treated wood. The most substantial reactivity between wood polymers and organosilicon was observed with the (3-mercaptopropyl)trimethoxysilane treatment, showing complete removal of lignin side chains, the lowest syringyl/guaiacyl ratio, depolymerization of cellulose and xylan, and reactivity with the C6 primary hydroxyls in cellulose. This may explain the outstanding stabilizing effectiveness of this silane and supports the conclusion that extensive chemical interactions are essential in this process. It also indicates the vital role of a mercapto group in wood stabilization by organosilicons. This 2D NMR technique sheds new light on the chemical mechanisms involved in organosilicon consolidation of wood and reveals what chemical characteristics are essential in developing future conservation treatments.

Surface Tuning of Wood via Covalent Modification of Its Lignocellulosic Biopolymers with Substituted Benzoates-A Study on Reactivity, Efficiency, and Durability

Chemical modification of wood applying benzotriazolyl-activated carboxylic acids has proven to be a versatile method for the durable functionalization of its lignocellulosic biopolymers. Through this process, the material properties of wood can be influenced and specifically optimized. To check the scope and limitations of this modification method, various benzamide derivatives with electron-withdrawing (EWG) or electron-donating (EDG) functional groups in different positions of the aromatic ring were synthesized and applied for covalent modification of Scots pine (Pinus sylvestris L.) sapwood in this study. The bonded amounts of substances (up to 2.20 mmol) were compared with the reactivity constants of the Hammett equation, revealing a significant correlation between the modification efficiency and the theoretical reactivity constants of the corresponding aromatic substitution pattern. The successful covalent attachment of the respective substituted benzamides was proven by attenuated total reflection infrared (ATR-IR) spectroscopy, while the stability of the newly formed ester bond was proven in a standardized leaching test.